Search

The work presented in this paper aims to highlight and to understand the size effect of nano-reinforcements on nanocomposite properties With an experimental approach. Nanocomposites of PMMA and silica particles With different sizes (15nm, 25nm, 60nm, 150nm and 500nm) and volume fractions (20/0, 4 0/0 and 60/0) were manufactured. Multiscale analysis (MET and DRX-WAXS) have shown that the characteristic parameters of the microstructure of nanocomposites vary With the size of the nanoparticles. Indeed, the decrease in the size of nanoparticles at a given volume fraction implies a decrease of the intermolecular distance. This decrease has induced a densification of the matrix and a decrease of the matrix chain mobility. Mechanical tests (tensile, DMA) have shown that the young (E) and the conservation (E') moduli of the nanocomposites increase With the decrease in the size of the nanoparticles With a constant volume fraction. And the increase of E l is kept when temperature growing. An increase in glass transition (Tg) and degradation temperature (Td) was also observed With the DSC, DMA and ATG tests. Experimental elastic properties of the nanocomposites were used to assess the relevance of size effect micromechanical models, particularly the Hashin-Shtrikman bounds With interface effects proposed by Brisard. The modeling has shown that to reproduce the experimental elastic moduli of nanocomposites, the elastic coefficients of the interface must be dependents on particle sizes. And the state of dispersion of particles must be taken into account.; Le travail présenté dans ce document vise à mettre en évidence et à comprendre l'effet de la taille nanométrique des renforts sur les propriétés des nanocomposites avec une approche expérimentale. Des nanocomposites de PMMA et particules de silice (15nm, 25nm, 60nm, 150nm et 500nm) de fractions volumiques 2 0/0, 40/0 et 6 0/0 ont été fabriqués. Des analyses multi-échelles (MET et DRX-WAXS) ont montré que les paramètres caractéristiques de la microstructure des nanocomposites varient avec la taille des nanoparticules. En effet, la diminution de la taille des nanoparticules à fraction volumique constante a entrainé une diminution de la distance intermoléculaire. Cette diminution a induit une densification de la matrice et une réduction de la mobilité des chaînes de la matrice. Des essais mécaniques (traction, DMA) ont montré que les modules de Young (E) et de conservation (E') des nanocomposites augmentent avec la diminution de la taille des nanoparticules à fraction volumique constante. Et que l'augmentation de E' est conservée avec l'augmentation de la température. Une augmentation des températures de transition vitreuse (Tg) et de dégradation (Td) a également été observée avec les essais DSC, DMA et ATG. Le modèle de la borne inférieure d'Hashin-Shtrikman étendue aux nanocomposites à renforts sphériques proposé par Brisard a été utilisé. La modélisation des modules élastiques des nanocomposites a montré que pour reproduire les données expérimentales, il faut que d'une part que les modules surfaciques caractérisant l'interface soient dépendants de la taille des nanoparticules. Et d'autre part, tenir compte de l'état de dispersion des nanoparticules.

The work presented in this paper aims to highlight and to understand the size effect of nano-reinforcements on nanocomposite properties With an experimental approach. Nanocomposites of PMMA and silica particles With different sizes (15nm, 25nm, 60nm, 150nm and 500nm) and volume fractions (20/0, 4 0/0 and 60/0) were manufactured. Multiscale analysis (MET and DRX-WAXS) have shown that the characteristic parameters of the microstructure of nanocomposites vary With the size of the nanoparticles. Indeed, the decrease in the size of nanoparticles at a given volume fraction implies a decrease of the intermolecular distance. This decrease has induced a densification of the matrix and a decrease of the matrix chain mobility. Mechanical tests (tensile, DMA) have shown that the young (E) and the conservation (E') moduli of the nanocomposites increase With the decrease in the size of the nanoparticles With a constant volume fraction. And the increase of E l is kept when temperature growing. An increase in glass transition (Tg) and degradation temperature (Td) was also observed With the DSC, DMA and ATG tests. Experimental elastic properties of the nanocomposites were used to assess the relevance of size effect micromechanical models, particularly the Hashin-Shtrikman bounds With interface effects proposed by Brisard. The modeling has shown that to reproduce the experimental elastic moduli of nanocomposites, the elastic coefficients of the interface must be dependents on particle sizes. And the state of dispersion of particles must be taken into account., Le travail présenté dans ce document vise à mettre en évidence et à comprendre l'effet de la taille nanométrique des renforts sur les propriétés des nanocomposites avec une approche expérimentale. Des nanocomposites de PMMA et particules de silice (15nm, 25nm, 60nm, 150nm et 500nm) de fractions volumiques 2 0/0, 40/0 et 6 0/0 ont été fabriqués. Des analyses multi-échelles (MET et DRX-WAXS) ont montré que les paramètres caractéristiques de la microstructure des nanocomposites varient avec la taille des nanoparticules. En effet, la diminution de la taille des nanoparticules à fraction volumique constante a entrainé une diminution de la distance intermoléculaire. Cette diminution a induit une densification de la matrice et une réduction de la mobilité des chaînes de la matrice. Des essais mécaniques (traction, DMA) ont montré que les modules de Young (E) et de conservation (E') des nanocomposites augmentent avec la diminution de la taille des nanoparticules à fraction volumique constante. Et que l'augmentation de E' est conservée avec l'augmentation de la température. Une augmentation des températures de transition vitreuse (Tg) et de dégradation (Td) a également été observée avec les essais DSC, DMA et ATG. Le modèle de la borne inférieure d'Hashin-Shtrikman étendue aux nanocomposites à renforts sphériques proposé par Brisard a été utilisé. La modélisation des modules élastiques des nanocomposites a montré que pour reproduire les données expérimentales, il faut que d'une part que les modules surfaciques caractérisant l'interface soient dépendants de la taille des nanoparticules. Et d'autre part, tenir compte de l'état de dispersion des nanoparticules.