Abstract: This report presents an atmospheric-pressure nitrogen-plasma jet generated from microdischarges in a porous dielectric. A plasma jet with a length of 42 mm was produced by feeding nitrogen gas through a porous alumina installed between an outer electrode and a hollow inner electrode and by applying 60 Hz sinusoidal voltage wave to the electrodes. Microdischarges in the porous alumina are ejected as a plasma jet from the outer electrode through a 1 mm hole by increasing the applied voltage, showing that the temperature of the jet decreases to a value close to room temperature. Even at a frequency as low as 60 Hz, the plasma that evolves from a large amount of microdischarge inside a porous dielectric can have characteristics that are similar to those generated at several hundreds of kilohertz. From the electrical measurements, it is expected that not only the steady generation but also the frequency of the pulses resulting from the microdischarges in the porous dielectric play an important role in obtaining a stable plasma jet. We also identified the various excited plasma species produced from the plasma jet by an optical emission spectroscopy. [Copyright &y& Elsevier]

The adhesion of copper coatings to carbon substrates is very poor, because of lack of diffusion or reaction between the constituents. Because there is technological interest in enhancing the adhesion and improving the interface between copper and carbon, plasma treatment of the carbon substrate was employed in this study. For modification of the carbon surface a nitrogen plasma was used. It was confirmed by pull-off tests that the strength of adhesion of the copper coating can be improved by a factor of more than 10 by plasma pretreatment, even after treatment for a very short time (1 min). To obtain more information about the mechanisms of the processes occurring at the interface SIMS investigations were performed on samples which had been treated for different times (between 1 and 60 min). These measurements confirmed that nitrogen is located on the interface. With increasing pretreatment time the amount of nitrogen detected on the interface increased. Besides characterisation of as-deposited samples, another focus was to study the mechanisms of diffusion of nitrogen if the samples are heat treated at 500°C. [ABSTRACT FROM AUTHOR]