This text describes the plasma nitriding of a ductile iron, to increase the surface hardness and improve its wear behavior. A ferritic ductile iron was used and processed with gases (N2 + H2) for 5 hours in a treatment chamber built at the UNAM Physics Institute. The treated samples were characterized using scanning electron microscopy, atomic force microscopy, microhardness and X-ray diffraction. The presence of Fe-N compounds was corroborated on the surface of the material. Modifications in surface morphology and a 30% increase in microhardness were also obtained. [ABSTRACT FROM AUTHOR]

A fotopolimerização inadequada das resinas compostas pode ocasionar falhas na restauração, como microinfiltração marginal, resistência ao desgaste e falhas na dureza do material restaurador. A microdureza das resinas compostas é de extrema importância, pois afeta a propriedade mecânica, podendo causar uma perda prematura da restauração. Diante disso, essa revisão de literatura tem como objetivo identificar os fatores que interferem na microdureza das resinas compostas durante a sua polimerização, para assim evitar a ocorrência do insucesso das restaurações. Para tanto, foi realizada uma busca bibliográfica nos bancos de dados Google Scholar, PubMed e Biblioteca Virtual em Saúde (BVS) com o emprego dos descritores: resina composta, fotopolimerizador, restauração, polimerização e microdureza. Alguns fatores importantes foram observados: aspectos como intensidade e colimação da luz usada e seu comprimento de onda, o material e a técnica escolhida, o tipo e a quantidade do fotoiniciador presente no material e as características do aparelho fotopolimerizador. Para concluir, é fundamental conhecer o aparelho de luz selecionado e as propriedades do material restaurador para otimizar seus resultados, prevenir falhas na dureza do material e assim proporcionar restaurações mais duradouras.

La mezcla de polvo de Ti+Ni3Al+Al2O3 a base de Fe se alea mecánicamente en un molino de bolas Spex. Los compuestos con adición de Ti+Ni3Al+Al2O3 a base de Fe se produjeron a una temperatura de sinterización de 1000 °C durante un tiempo de 1 h. Las propiedades de estos compuestos se examinaron mediante microscopía electrónica de barrido (SEM), microscopía óptica (OM), espectroscopía de dispersión de energía (EDS), difracción de rayos X (XRD) y análisis de microdureza. El producto final producido por aleación mecánica fue una solución sólida rica en níquel nanocristalina, el tamaño promedio del cristal era de unos pocos nanómetros. El contenido de titanio en el refuerzo aumentó los valores de microdureza del composite. Los compuestos producidos incluían las fases Fe3Al, TiAl, NiAl, Al3Ni2, Al2O3 y Fe3O.

En este trabajo se estudió el efecto del ángulo de giro del proceso de torsión y la distancia desde el centro en barras cilíndricas en el perfil de microdureza del acero AISI 1045 recocido. Los resultados mostraron que la microdureza aumenta con los parámetros evaluados y el endurecimiento se relaciona con la deformación plástica causada por el proceso más que por transformaciones microestructurales. Con base en los resultados experimentales, se realizó un análisis ANOVA-Pareto que demostró que el ángulo de giro es el factor de control más influyente (59,35%) entre los parámetros investigados. Finalmente, se presenta un modelo para predecir el perfil de microdureza del proceso de torsión.

Copyright of Bioscience Journal is the property of Bioscience Journal and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Bioscience Journal is the property of Bioscience Journal and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Los efectos de la deformación previa sobre los procesos de precipitación en una aleación de Cu-2,8 Ni-1,4 Si (at.%) fueron estudiados utilizando calorimetría diferencial de barrido (DSC), microscopía electrónica de transmisión (TEM) y medidas de microdureza. Las curvas calorimétricas muestran la presencia de una reacción exotérmica atribuido a la formación de precipitados de δ-Ni2Si en la matriz de cobre, lo cual fue confirmado mediante TEM. Además, sse puede observar que la temperatura del máximo del pico de DSC decrece con el aumento de la deformación previa a los tratamientos de envejecimiento. Las energías de activación calculadas para la precipitación de δ-Ni2Si, mediante el método de Kissinger, resultaron similares a aquellas calculadas mediante una función de Arrhenius, a partir del máximo de endurecimiento de la matriz debido al tratamiento de envejecimiento (saturación de la dureza durante el envejecimiento isotérmico). El análisis de las medidas de microdureza en conjunto con las curvas calorimétricas y las micrografías TEM permiten corroborar, por una parte que la formación de la fase δ-Ni2Si, durante los tratamientos de envejecimiento, son los responsables del endurecimiento de la matriz de cobre, y por otra que la deformación previa al tratamiento de envejecimiento inhibe parcialmente la formación de los precipitados.

Resumo Introdução Dentes artificiais têm sido empregados para a prática de ensino pré-clínico. Porém, não se sabe o comportamento dos mesmos frente aos diferentes procedimentos realizados durante um tratamento endodôntico simulado. Objetivo Avaliar a microdureza de réplicas de dentes humanos, frente a diferentes soluções irrigadoras. Material e método Quarenta e cinco incisivos centrais superiores artificiais de três marcas comerciais nacionais (dentes “A”, “B” e “C”) e 15 incisivos humanos foram utilizados. As amostras foram seccionadas a 5 mm do ápice dentário. Os fragmentos radiculares foram fixados em resina para posterior teste de microdureza. Os ensaios da microdureza Knoop foram realizados em dois momentos: momento 1 - microdureza inicial; momento 2 - microdureza final, que foi feita após o uso das soluções irrigadoras (Cloreto de Sódio a 0,9%, Hipoclorito de Sódio a 2,5% e Gluconato de Clorexidina a 2%). As endentações deixadas na superfície da amostra foram mensuradas. O valor obtido para microdureza de cada amostra foi feita com base na média de três endentações. Para análise estatística, foram utilizados os testes ANOVA e Teste t pareado, com nível de significância de 5%. Resultado Os dentes artificiais “A” e “C” apresentaram valores inferiores de microdureza quando comparados ao dente humano (P = 0,05). Não houve diferença estatística entre os dentes artificiais “B” e o dente humano (P = 0,2428). Quanto ao uso das diferentes soluções irrigadoras, também não houve diferença na microdureza das peças dentárias. Conclusão Embora a solução irrigadora não tenha influenciado a microdureza, os dentes artificiais apresentaram valores de dureza inferiores aos do dente humano.

In the Al-2.0 wt.% Fe alloy the laser surface remelting (LSR) treatment was executed to investigate the treated and untreated layers areas, at different laser beam scanning, among them, 80, 100 and 120 mm/s, to respect, was presented and discussed about microstructural characteristics using the FEG and EDS techniques, and numerical experiments of pyramidal indentations of the LSR-treated systems were conducted using the FEM method. In the sample-treated cross-sectional area, the microstructure presented a columnar growth characteristics, a lot of nano-porosities and large size of the molten pool geometry in low laser beam scanning, however, in high laser beam scanning, the microstructure consisted of a cellular arrangement or fine-grained microstructure, the nanoporosities concentration and the molten pool geometry are slightly decreased. Besides, the micro-hardness in the LSR-treated area increased slightly as a function of increase of the laser beam scanning, but, the micro-hardness was much higher than the untreated sample. Meanwhile, modeling of indentation on COMSOL of the LSR-treatment by finite element method of the microhardness was successfully calculated. Therefore, a good agreement was found between experimental and simulated data. [ABSTRACT FROM AUTHOR]

En este trabajo se ha estudiado el efecto de la microestructura y de la microdureza sobre la resistencia al desgaste de recubrimientos de circona-alúmina (ATZ), circona-itria (YSZ) y circona-ceria (CSZ) elaborados mediante proyección térmica por plasma atmosférico. La microestructura y la fractura de la sección transversal de los recubrimientos han sido evaluadas mediante microscopia electrónica de barrido (MEB), sus fases han sido analizadas a partir de espectros de difracción de rayos X (DRX), su microdureza ha sido determinada mediante microindentación Vickers y su resistencia al desgaste ha sido evaluada mediante el ensayo de bola-disco. Los resultados mostraron que el recubrimiento que presentó el mejor desempeño tribológico fue el de ATZ, a pesar de tener una cantidad importante de la fase circona monoclínica, la cual es de menor dureza que la tetragonal presente en mayores cantidades en los otros 2 recubrimientos y este comportamiento ha estado muy relacionado con su microestructura y su alta microdureza. La menor resistencia al desgaste de los recubrimientos de YSZ y CSZ ha estado relacionada con la estructura columnar presente dentro de sus lamelas, lo que puede ocasionar un mayor desprendimiento de partículas en la superficie de contacto durante el ensayo bola-disco, aumentando así su desgaste.

In this work, the effect of the torsion process angle of twist and distance from the center of cylindrical bars on the microhardness profile of annealed AISI 1045 steel was studied. The results showed that the microhardness increase with the evaluated parameters and the hardening is related to the plastic deformation caused by the process rather than by microstructural transformations. Based on the experimental results, ANOVA-Pareto analysis was conducted proving that the angle of twist is the most influential control factor (59.35 %) among the parameters investigated. Finally, a model to predict the microhardness profile from the torsion process is presented. [ABSTRACT FROM AUTHOR]

Las propiedades de los recubrimientos cerámicos, no solo se ven afectadas por los parámetros eléctricos asociados a la deposición, sino también están influenciadas por el material de alimentación. Características como: elementos constitutivos, morfología, fases y distribución granulométrica de los polvos cerámicos, influyen en la rugosidad y acabado superficial de los recubrimientos, como también en la porosidad, dureza y tenacidad de los mismos. Por lo anterior, el siguiente estudio se basa en la caracterización de polvos cerámicos de Carburo de Tungsteno (WC-12%Co), Alúmina-Titania (Al2O3–13%TiO2; sistemas empleados en la obtención de recubrimientos termorrociados. Para ello, se evaluaron sus características químicas y morfológicas empleando las técnicas de Difracción de Rayos X, Microscopía Óptica y Microscopía Electrónica de Barrido con EDX; relacionándose a su vez, la morfología y distribución granulométrica con propiedades microestructurales como la porosidad y microdureza en recubrimientos obtenidos a partir de estos sistemas cerámicos.

OBJECTIVE: The aim of the present study was to assess the influence of saliva contamination over the structural strength and integrity of conventional glass-ionomer cements used for cementing orthodontic bands in the absence and presence of a surface-protecting varnish. METHOD: 48 samples were prepared by inserting 3 types of glass-ionomer cements into standardized metallic matrixes of 10 mm of diameter and 2 mm of depth. The cements used were: Meron (VOCO), Ketac-Cem (3M ESPE) and Vidrion C (DFL), all of which comprised groups A, B and C, respectively. Subgroups A1, B1 and C1 comprised samples with no surface protection, whereas subgroups A2, B2 and C2 comprised samples of which surface was coated with Cavitine varnish (SS White), after cement manipulation and application, in order to protect the cement applied. All samples were stored in artificial saliva for 24 hours at 37ºC. A Vickers diamond micro-durometer was used to produce indentations on the non-treated group (non-varnished) and the treated group (varnished). RESULTS: Varnished materials had significantly higher microhardness values in comparison to non-varnished materials. Ketac-Cem had the highest microhardness value among the varnished materials. CONCLUSION: Varnish application is necessary to preserve the cement and avoid enamel decalcification. Glass-ionomer cements should be protected in order to fully keep their properties, thus, contributing to dental health during orthodontic treatment.

Se llevaron a cabo soldaduras sin material de aporte y empleando un electrodo convencional (ER308L) para unir un acero inoxidable ferrítico, empleando el proceso de soldadura de arco con electrodo de tungsteno (GTAW). Los parámetros de soldadura fueron ajustados para obtener tres valores diferentes de calor de aporte. La microestructura revela la presencia de una matriz ferrítica gruesa y placas de martensita en la Zona Afectada por el Calor (ZAC). La dilución entre el metal base y de aporte fue correlacionada con la presencia de austenita, martensita y ferrita en el metal de soldadura. Los ciclos térmicos de la soldadura fueron medidos para correlacionar la transformación microestrutural en la ZAC. Mediciones de microdureza (mapas y perfiles), permitieron identificar las diferentes zonas de las uniones soldadas (metal base, ZAC y metal de soldadura). Se observó un incremento de dureza en el metal de soldadura (~350 HV0,5) y en la ZAC (~310 HV0,5), en relación al metal base (~172 HV0,5), que se ha atribuido a la formación de martensita. La resistencia a la tensión de las uniones soldadas sin metal de aporte aumentó ligeramente con respecto al metal base. En cambio, la ductilidad se incrementó aproximadamente un 25% en relación al material base, lo cual mejoró la tenacidad de las uniones.

This article shows the creation of ceramic films of the SiO2-TiO2 Organic Polymer hybrid system from Tetraethyl-Orthosilicate (Si (OC2H5)4) and Titanium Tetrabutoxide (Ti(OBu)4) synthesized through the sol-gel method in several volumetric concentrations of precursors. This hybrid system was deposited on AISI 304 stainless steel substrates through the dip-coating technique. Feasibility for obtaining hybrid and homogeneous coatings on this type of substrate and evaluating the surface properties was studies. For such a purpose, the coating microhardness and adhesion were studies. Additionally, the film surface was characterized through the SEM (Scanning Electron Microscopy). The study concluded that characteristics of films change in function of the volumetric amount of precursors used for creating films.Este trabajo muestra la conformación de películas cerámicas del sistema híbrido SiO2-TiO2-Polímero Orgánico, a partir de tetraetil-ortosilicato (Si (OC2H5)4), y tetra-butoxido de titanio (Ti(OBu)4) y sintetizado por el método sol-gel en diferentes concentraciones volumétricas de los precursores. Este sistema híbrido se depositó sobre sustratos de acero inoxidable AISI 304 mediante la técnica de inmersión (dip-coating). Se estudió la viabilidad de obtener recubrimientos híbridos homogéneos sobre este tipo de sustrato y evaluar las propiedades superficiales. Para tal efecto, se estudió microdureza y adhesión del recubrimiento. Adicionalmente, se caracterizó la superficie de las películas por microscopía electrónica de barrido (MEB). Del estudio se concluye que las características de las películas cambian en función de la cantidad volumétrica de los precursores utilizados en la conformación de las mismas.

Los recubrimientos multicapa representan una clase promisoria de recubrimientos protectores, gracias a la mejora en las propiedades tribológicas, mecánicas y anticorrosivas que confieren a las superficies recubiertas. Esto ha motivado la investigación, desarrollo e implementación de estos materiales en muchas aplicaciones industriales, debido a que en la actualidad los requisitos que se tienen en la industria no se satisfacen con materiales que cumplan con una propiedad buena, sino con una combinación de buenas propiedades para la mayoría de las aplicaciones. En este trabajo se depositaron recubrimientos multicapa de CrN/TiN por pulverización catódica; la variación del número de bicapas de los recubrimientos con 4 ju,m de espesor fue de 10, 40, 80 y 100. El tamaño de grano y la rugosidad de los recubrimientos se determinaron mediante microscopía de fuerza atómica; se realizaron pruebas de microdureza y adhesión por rayado, los coeficientes de fricción se evaluaron en un tribómetro de tipo esfera sobre disco y la resistencia al desgaste abrasivo se determinó por el método Calotest. Los recubrimientos con 100 bicapas de CrN/TiN exhibieron un volumen de desgaste dos órdenes de magnitud menor que las muestras de una monocapa de TiN y de CrN. Las propiedades mecánicas fueron fuertemente influenciadas con la disminución del espesor del período de modulación de los recubrimientos, incrementándose de 23,1 GPa para la muestra con 10 bicapas a 29,8 GPa para la muestra con 100 bicapas de CrN/TiN.Os revestimentos multicamada representam uma classe promissória de revestimentos protetores, devido à melhora nas propriedades tribológicas, mecânicas e anticorrosivas que conferem às superfícies recobertas. Isto tem motivado a pesquisa, desenvolvimento e implementação destes materiais en muitas aplicações industriais, porque na atualidade os requisitos que se têm na indústria não se satisfazem com materiais que cumpram com una propriedade boa, sino com uma combinação de boas propriedades para a maioria das aplicações. Neste trabalho depositaram-se revestimentos multicamada de CrN/TiN por pulverização catódica; a variação do número de bicamadas dos revestimentos com 4 μm de espessura foi de 10, 40, 80 y 100. O tamanho de grão e a rugosidade dos revestimentos determinaram-se mediante microscopia de força atómica; realizaram-se provas de microdureza e adesão por rajado, os coeficientes de fricção avaliaram-se em um tribômetro de tipo esfera sobre disco y a resistência ao desgaste abrasivo determinou-se por o método Calotest. Os revestimentos com 100 bicamadas de CrN/TiN exibiram um volume de desgaste duas ordens de magnitude menor que as mostras de una monocapa de TiN y de CrN. As propriedades mecânicas foram fortemente influenciadas com a diminuição da espessura do período de modulação dos revestimentos, incrementando-se de 23,1 GPa para a mostra com 10 bicamadas a 29,8 GPa para a mostra com 100 bicamadas de CrN/TiN.Multilayer coatings represent a promising class of protective coatings due to the improvement in tribological, mechanical, and anticorrosive properties conferred to the coated surfaces. This has motivated the research, development and implementation of these materials in many industrial applications; nowadays the requirements of the industry are not satisfied with materials that have a good property, but a combination of good properties for most of the applications. In this work CrN/TiN multilayer coatings were deposited by magnetron sputtering; the variation of number of coating bilayers with 4 ju,m total thickness was of 10, 40, 80 and 100. The grain size and the roughness of coatings were determined by means of atomic force microscopy; micro hardness and scratch adhesion tests were performed, the friction coefficients were evaluated in a ball on disk tribometer, and the abrasive wear resistance was determined by Calotest method. The coatings with CrN/TiN 100 bilayers exhibited a wear volume two orders of magnitude lower than the single layer coatings of TiN and CrN. Mechanical properties were strongly influenced by the decrease of the modulation period thickness of the coatings, having increased from 23.1 GPa for the sample with 10 bilayers to 29.8 GPa for the sample with CrN/TiN 100 bilayers.

Titanium-Vanadium nitride (TiVN) has been prepared from carbothermal reduction of corresponding oxides and also by direct nitridation of a mix of two metals employing the ATVC method. The characterization of the final product by X-ray diffraction, scanning electron microscopy, electron energy loss (EELS), and X-ray absorption spectroscopy (XAS) is presented. The synthesis of the ternary nitride has been possible in all range of composition and the final product is obtained with nanometric particle size and a high microhardness after sintering.En el presente trabajo se aborda la síntesis del nitruro ternario de titanio y vanadio por reducción carbotérmica de una mezcla de óxidos o bien por nitruración directa de la mezcla de metales, en todo el rango de composiciones empleando el método de análisis térmico a velocidad controlada (ATVC). La caracterización de los productos obtenidos se ha llevado a cabo mediante difracción de rayos-X y microscopia electrónica. El empleo de la técnica EELS ha mostrado su capacidad para la cuantificación de este tipo de materiales, así como la utilización de la técnica espectroscópica XAS nos ha servido para corroborar los datos obtenidos a partir de los diagramas de difracción de rayos-X sobre distancias de enlace, número de coordinación y grado de desorden, esto último no detectado por las otras técnicas usadas en la caracterización de los productos. Los valores de microdureza registrados para las muestras sintetizadas se encuentran dentro del rango de valores reportados para este tipo de materiales.

El objetivo del trabajo es el estudio de los efectos de la pulverización con altas energías sobre la resistencia, estabilidad térmica y conductividad eléctrica del compuesto Cu-Al2O3. El polvo pre-aleado de cobre, obtenido a través de la atomización con gas inerte y con un contenido de 3wt. % Al, se molió durante 20 h en el molino planetario de bolas dando lugar a la oxidación in situ del aluminio con el oxígeno del aire. El compuesto compactado se ha obtenido mediante prensado en caliente en atmósfera de argón a 800 °C durante 3 h y a una presión de 35MPa. La caracterización microestructural se hizo a través de microscopia óptica, microscopia electrónica de barrido (SEM), microscopia electrónica de transmisión (TEM) y difracción de rayos X (XRD). También se realizaron medidas de micro-dureza, de conductividad eléctrica y de densidad. La micro-dureza de los compuestos compactados (102 HV) aumentó casi tres veces comparada con la de los obtenidos del polvo Cu-3 wt. % Al (102 HV). El tamaño de grano del compactado Cu-3 wt. % Al fue 75 y 45 nm después de 5 y 20 h de pulverización, respectivamente. El pequeño aumento del tamaño de grano y la pequeña caída de micro-dureza del compuesto Al2O3 indican alta estabilidad térmica durante la exposición a altas temperaturas de 800 °C.

Mediante calorimetría diferencial de barrido (DSC) se estudió la cinética de precipitación de átomos de cobalto y titanio a partir de una solución sólida de Cu-0,49Co-0,44Ti, templada desde 1.173 K. El análisis de las curvas calorimétricas muestran la presencia de una reacción exotérmica la cual se atribuye a la formación de partículas de CoTi en la matriz de cobre. La energía de activación de la reacción fue estimada a partir del método de Kissinger modificado. Los parámetros cinéticos fueron calculados mediante el formalismo de Johnson- Mehl-Avrami. Por otra parte, se efectuó un análisis estadístico del proceso de precipitación, mediante medidas de microdureza Vickers, empleando una función de distribución de probabilidad deWeibull. Se estimaron los parámetros deWeibull mediante el método de mínimos cuadrados. La bondad de ajuste se analizó considerando el test de chi-cuadrado con un nivel de confianza del 95 %. A medida que se incrementó el tiempo de envejecimiento, para igual temperatura de recocido, incrementó el valor del módulo deWeibull, lo cual puede atribuirse a la precipitación de la fase CoTi.

O propósito deste trabalho é fazer uma comparação entre resinas poliméricas dentárias, polimerizadas por aparelhos baseados em lâmpada halógena e diodo emissor de Luz (LED), utilizando-se o método do disco retificado aperfeiçoado para odontologia e os respectivos valores de microdureza. Foram realizados testes em amostras de resinas compostas de 5 diferentes marcas, polimerizadas a tempos de 10, 20 e 40 s, pelos dois aparelhos. A análise estatística dos valores de microdureza e agressividade permitiu concluir que estatisticamente não há correlação entre essas propriedades. Na análise de microdureza, a heterogeneidade característica do material implicou em resultados com valores de desvio padrão relativamente altos, de forma que não foi encontrada diferença estatística entre as amostras avaliadas. Na análise estatística dos ensaios baseados no método do disco retificado, a resina que apresentou maior desgaste nos ensaios, foi a Tetric Ceram, polimerizada pelo aparelho de LED por 10 s, cujo valor médio de agressividade obtido foi 0,170 mm³/N.m. A resina que sofreu menor desgaste foi a Charisma, polimerizada por Lâmpada Incandescente, por um tempo de 20 s, cuja média dos valores de agressividade foi 0,057 mm³/N.m.The purpose of this work was to compare polymeric dental resins cured with halogen lamp and with light emission diode (LED) devices, using the grinding disk method customized for dentistry and the corresponding microhardness values. Tests were carried out on resin samples of five brands, which were cured for 10, 20 and 40 s with the two devices. The analysis of microhardness and aggressiveness has allowed us to conclude that there is no correlation between these properties. In Microhardness tests, the material heterogeneity has produced relative high standard deviation values and has not shown statistical differences between the analyzed samples. In the statistical analysis for the results with the grinding disk method, the resin with highest wear was the Tetric Ceram, cured with LED device for 10 s (aggressiveness average 0.170 mm³/N.m ). The composite resin with least wear was Charisma, cured with halogen lamp device for 20 s (aggressiveness average 0.057 mm³/N.m ).

Mediante calorimetría diferencial de barrido (DSC), se estudió el proceso de precipitación de átomos de níquel y aluminio a partir de una solución sólida de Cu-Ni-Al. El análisis de las curvas calorimétricas muestra la presencia de dos reacciones exotérmicas (etapas 1 y 2), que se interpretan como la formación de dos tipos de precipitados. La primera etapa corresponde a la formación de la fase de equilibrio b (NiAl), en tanto que la etapa 2 corresponde a la formación del precipitado g’ de composición estequiométrica Ni3Al. Además, se observa que las curvas se desplazan a temperaturas más bajas a medida que la velocidad de calentamiento lineal decrece. Las energías de activación de las reacciones fueron evaluadas a partir de un método de Kissinger modificado. Los parámetros cinéticos se calcularon mediante el formalismo de Johnson- Mehl-Avrami. Los valores de n obtenidos son indicativos de un proceso de nucleación de partículas a partir de núcleos pre existentes. Las medidas de microdureza y las micrografías obtenidas por microscopía electrónica de transmisión ayudaron a confirmar la formación de las fases antes indicadas.

In this work hard chromium electroplating process is developed on small test specimens on AISIA36 steel. This paper includes the development of hard chrome plating process at laboratory scale and provide a simplified procedure for industrial applications. By applying a differential power over the A36 steel submerged in an electrolytic bath of chromic acid, a thin coat of 30 to 80 microns of chrome is deposited over the specimen. The hard chrome deposition is achieved by a combination of multiple variables such as: chromic acid concentration, substrate metal, anodes, current density, solution temperature and time. From the abovementioned parameters, the time and the current density are the working parameters to be manipulated while the others remain unchanged. For these experiment, a linear simplified model is theoretically and experimentally derived from Faraday’s electro-deposition law for hard chrome plating. The thickness variation, micro-hardness and cracking network of the combination of the working parameters are included and discussed in this work. The chrome deposit obtained is microscopically and gravimetrically measured. The results obtained by combining the working parameters show hardness values within the range provided of 66 to 70 HRC. This paper studies and analyzes the possible causes that influence hardness with the microstructure (number of surface cracks, density) and processing parameters such as time and current density.

En este trabajo se realizaron soldaduras de punto utilizando la técnica de fricción-agitación, SFAP, sobre láminas traslapadas de aleación de aluminio 6063-T5, de 2,8 mm de espesor y un área de traslape de 25,4 mm2. El proceso de soldadura SFAP se realizó en una fresadora universal en variadas condiciones de velocidad de rotación y tiempo de sostenimiento; se mantuvieron constantes tanto la velocidad y la profundidad de la penetración; para determinar las propiedades mecánicas óptimas de dureza y resistencia mecánica; se caracterizaron los puntos de soldadura mediante ensayos de tensión, barridos de microdureza y análisis metalográfico. Los resultados permitieron concluir que mediante este proceso de soldadura se pueden obtener soldaduras de puntos con buena apariencia, sanidad en el área transversal de la unión, resistencia mecánica y además una adecuada homogeneidad, lo que las hace una alternativa ventajosa frente a los procesos de soldadura convencionales aplicados sobre aluminio.

PURPOSE: The aim of the present study was to evaluate the alterations of surface microhardness and wear caused by the sodium bicarbonate jet on bovine enamel and the further remineralizing effect of artificial saliva. METHODS: Fifteen enamel samples (4,0mm x 4,0mm) were used, which constituted the groups: no treatment (MI); treatment with sodium bicarbonate jet (MII and DI); treatment with sodium bicarbonate jet and immersion in saliva for one hour (MIII and DII), 24 hours (MIV and DIII) and 7 days (MV and DIV). Microhardness tests were carried out using a microdurometer in groups M and wear tests by a rugosimeter in groups D. The data were assessed by the one criterion variance analysis and Tukey test. RESULTS: The mean value of microhardness, in KHN, in groups MI, MII, MIII, MIV and MV were 359,80; 335,46; 369,20; 377,73 and 341,86, respectively, whereas the mean values in µm, of wear for group DI, DII, DIII and DIV were 0,564; 0,519; 0,441 and 0,428, respectively. CONCLUSIONS: The sodium bicarbonate jet caused a wear and a reduction in microhardness on the enamel surface; saliva promoted the recovery of initial condition surface microhardness and reduced the wear; the repairing effect of saliva on the surface microhardness alterations occurred within one hour of treatment, having no significant statistical difference from the effect obtained in 24 hours; the best saliva repairing effect on the wear occurred with treatment of 24 hours.OBJETIVO: A finalidade do trabalho foi avaliar as alterações da microdureza e o desgaste provocado pelo jato de bicarbonato de sódio em esmalte bovino e o posterior efeito remineralizador da saliva artificial. MÉTODOS: Utilizaram-se 15 espécimes de esmalte (4,0mm x 4,0mm) que constituíram os grupos: sem tratamento (MI); tratamento com jato de bicarbonato de sódio (MII e DI); tratamento com jato de bicarbonato de sódio e imersão em saliva artificial por uma hora (MIII e DII), 24 horas (MIV e DIII) e sete dias (MV e DIV). Foram realizados testes de microdureza com um microdurômetro nos grupos M e testes de desgaste com um rugosímetro nos grupos D. RESULTADOS: Os dados foram avaliados pela Análise de Variância a um critério e pelo Teste de Tukey. O valor das médias da microdureza, em KHN, nos grupos MI, MII, MIII, MIV e MV foram 359,80; 335,46; 369,20; 377,73 e 341,86; respectivamente, enquanto que os valores médios, em µm, do desgaste para o grupo DI, DII, DIII e DIV foram 0,564; 0,519; 0,441 e 0,428, respectivamente. CONCLUSÕES: o jato de bicarbonato de sódio causou desgaste e diminuição da microdureza superficial; a saliva promoveu o retorno da microdureza superficial à condição inicial e reduziu o desgaste; o efeito reparador da saliva sobre as alterações na microdureza superficial já ocorreu com uma hora de tratamento, não havendo diferença estatisticamente significante do efeito obtido com 24 horas; o melhor efeito reparador da saliva sobre o desgaste ocorreu com 24 horas de tratamento.

OBJECTIVE: This study evaluated the depth of cure of five dental composites submitted to different light-curing modes. MATERIAL AND METHODS: Canal-shaped cavities with 5mm of length were prepared on the buccal surfaces of extracted third molars, and restored using P-60, A-110, Admira, Z-250 and Supreme resin composites. Materials were light-cured from the top, according to three modes (Group 1- Conventional (C): 500 mW/cm² / 40 s; Group 2 - Soft-Start (SS): 250 mW/cm²/ 20 s + 500 mW/cm²/ 20 s + 500 mW/cm²/ 10 s and Group 3 - LED: 250 mW/cm²/ 40 s). After that, cavity longitudinal surfaces were polished and marked with a millimeter scale of 4mm of length. Depth of cure was evaluated by means of Knoop hardness number (KHN), so that five indentations were performed at each millimeter. Original data were submitted to three-way ANOVA and Fisher's LSD test (alpha = 0.01). RESULTS: All materials presented a significant reduction on KHN from first to third millimeter. Regarding depth of cure, the results obtained for Conventional and Soft-Start modes were similar, but statistically superiors to those found for group 3 (LED). CONCLUSION: This performance may be related to the differences among energy densities obtained with different light-curing modes.OBJETVO: Este estudo avaliou a profundidade de polimerização de cinco compósitos fotopolimerizáveis submetidos a diferentes métodos de fotoativação. MATERIAL E MÉTODO: Cavidades em forma de canaleta com 5 mm de comprimento, preparadas nas faces vestibulares de terceiros molares, foram restauradas com os compósitos P-60, A-110, Admira, Z-250 e Supreme. Os materiais foram fotoativados pelo topo das cavidades com três técnicas (Grupo 1 - Convencional (C): 500 mW / cm² / 40 s; Grupo 2 - Soft-Start (SS): 250 mW / cm² / 20 s + 500 mW / cm² / 20 s + 500 mW / cm² / 10 s e Grupo 3 - LED: 250 mW / cm² / 40 s). Após a fotoativação, as superfícies longitudinais dos materiais foram polidas e marcadas com uma escala milimetrada com 4 mm de comprimento. A profundidade de polimerização foi avaliada através do número de dureza Knoop (NDK), com cinco indentações a cada milímetro. Os dados originais foram submetidos à Análise de Variância de três fatores e teste de Fisher para comparações entre médias (alfa = 0,01). RESULTADOS: Todos os materiais apresentaram diminuição do NDK do primeiro para o terceiro milímetro (p < 0,01). Os resultados obtidos com os Grupos Convencional e Soft-Start foram similares e superiores ao Grupo LED (p < 0,01). CONCLUSÃO: Este desempenho pode ser relacionado às diferenças nas densidades de energia obtidas com os métodos de fotoativação utilizados.

INTRODUCTION: The evolution of light curing units can be noticed by the different systems recently introduced. The technology of LED units promises longer lifetime, without heating and with production of specific light for activation of camphorquinone. However, further studies are still required to check the real curing effectiveness of these units. PURPOSE: This study evaluated the microhardness of 4 shades (B-0.5, B-1, B-2 and B-3) of composite resin Filtek Z-250 (3M ESPE) after light curing with 4 light sources, being one halogen (Ultralux - Dabi Atlante) and three LED (Ultraled - Dabi Atlante, Ultrablue - DMC and Elipar Freelight - 3M ESPE). METHODS: 192 specimens were distributed into 16 groups, and materials were inserted in a single increment in cylindrical templates measuring 4mm x 4mm and light cured as recommended by the manufacturer. Then, they were submitted to microhardness test on the top and bottom aspects of the cylinders. RESULTS: The hardness values achieved were submitted to analysis of variance and to Tukey test at 5% confidence level. It was observed that microhardness of specimens varied according to the shade of the material and light sources employed. The LED appliance emitting greater light intensity provided the highest hardness values with shade B-0.5, allowing the best curing. On the other hand, appliances with low light intensity were the least effective. It was also observed that the bottom of specimens was more sensitive to changes in shade. CONCLUSION: Light intensity of LED light curing units is fundamental for their good functioning, especially when applied in resins with darker shades.INTRODUCTION: A evolução dos aparelhos fotopolimerizadores pode ser notada nos diferentes sistemas introduzidos recentemente no mercado. A tecnologia apresentada pelos aparelhos LED promete maior tempo de vida útil, não gerar aquecimento e produzir luz específica para a ativação da canforoquinona. No entanto, ainda são necessários estudos complementares para se conhecer a real efetividade destes aparelhos na polimerização dos materiais. PROPOSTA: Neste trabalho foi verificada a microdureza de 4 cores (B-0,5, B-1, B-2 e B-3) da resina composta Filtek Z-250 (3M ESPE) quando polimerizadas com 4 fontes de luz, sendo uma halógena (Ultralux - Dabi Atlante) e três LED (Ultraled - Dabi Atlante, Ultrablue - DMC e Elipar Freelight - 3M ESPE). MÉTODOS: Os 192 corpos-de-prova foram distribuídos em 16 grupos e os materiais foram inseridos em único incremento em matrizes cilíndricas de 4mm X 4mm, sendo polimerizados pelo tempo preconizado pelo fabricante. Em seguida, foram submetidos ao teste de microdureza na superfície superior e inferior dos cilindros. RESULTADOS: Os valores de dureza obtidos foram submetidos à análise de variância e ao teste de Tukey ao nível de 5%. Foi observado que a dureza dos corpos-de-prova variou conforme a cor do material e aparelhos utilizados. O aparelho LED que emite maior intensidade luminosa proporcionou a obtenção dos maiores valores de dureza, com o croma B-0,5 possibilitando a melhor polimerização. Por outro lado aparelhos com baixa intensidade luminosa foram os menos efetivos. Também foi observado que a região do fundo dos corpos-de-prova foi mais sensível à mudança das cores. CONCLUSÕES: A intensidade de luz dos fotopolimerizadores LED é fundamental para seu bom funcionamento, principalmente quando empregadas resinas com croma mais acentuado.

The purpose of this study was to evaluate the microhardness of dental enamel around composite restorations bonded with fluoride-containing adhesive systems (FCAS), after thermo- and pH-cycling protocols. Standardized cylindrical cavities were prepared on enamel surfaces of 175 dental fragments, which were randomly assigned into seven experimental groups (n=25). Four groups used FCAS: Optibond Solo (OS); Prime&Bond 2.1 (PB); Syntac Sprint (SS) and Tenure Quick (TC). Other groups consisted of "Sandwich" technique restoration (STR) (glass ionomer liner + hydrophobic adhesive resin /restorative composite) or used Single Bond with (SB) or without (SBWC) cycling protocols. Adhesive systems were applied according to manufacturers' instructions and cavities were restored with a microfilled composite (Durafill VS). After finishing and polishing, all groups were submitted to 1,000 thermal cycles (5 ºC and 55 ºC) and to demineralization (pH 4.3) and remineralization (pH 7.0) cycling protocols, except for SBWC group. The Knoop microhardness of enamel surfaces were measured around restorations. Indentations were recorded at 150, 300 and 450-mm from the cavity wall. Data were analyzed by two-way ANOVA and Duncan's Test (a=0.05%). Means ± SD of enamel microhardness for the groups were (Kg/mm²): SBWC: 314.50 ± 55.93ª ; SB: 256.78 ± 62.66b; STR: 253.90 ± 83.6b; TQ: 243.93 ± 68.3b; OS: 227.97 ± 67.1c; PB: 213.30 ± 91.3d; SS: 208.73 ± 86.6d. Means ± SD of microhardness for the distances 150, 300, 450mm from the cavity wall were, respectively: 234.46 ± 77.81ª; 240.24 ± 85.12ª; 262.06 ± 79.46b. SBWC group, which was not submitted to thermo- and pH-cycling protocols, showed the highest enamel microhardness mean value and the FCAS resulted in lower microhardness values. At 450 mm from the cavity wall, the enamel microhardness increased significantly.O objetivo deste estudo foi avaliar a microdureza do esmalte dental ao redor de restaurações em compósito que utilizaram sistemas adesivos contendo fluoretos (FCAS), após tratamento dessas superfícies restauradas aos protocolos de ciclagem térmica e pH. Cavidades cilíndricas padronizadas foram preparadas em 175 superfícies de esmalte de fragmentos dentais, os quais foram aleatoriamente divididos em sete grupos (n=25). Quatro grupos utilizaram os FCAS: Optibond Solo (OS); Prime&Bond 2.1 (PB); Syntac Sprint (SS) e Tenure Quick (TC). Outros grupos consistiram em restaurações "Sandwich" (STR - ionômero de vidro como base + restauração em composíto) ou utilizaram Single Bond com (SB) ou sem (SBWC) ciclagens. Os sistemas adesivos foram aplicados segundo as instruções dos fabricantes e as cavidades restauradas com compósito microparticulado (Durafill VS). Após o acabamento e polimento, todos grupos foram submetidos a 1.000 ciclos térmicos (5 ºC e 55 ºC) e a um protocolo de ciclagem de pH (desmineralização-pH 4,3 e remineralização-pH 7,0), exceto para o grupo SBWC. A microdureza das superfícies de esmalte foi mensurada ao redor das restaurações. Indentações foram feitas nas distâncias de 100, 300 and 450-mm da parede cavitária. Os dados foram analisados pela ANOVA (2 fatores) and Teste de Duncan (5%). Os valores médios ± DP da microdureza do esmalte para os grupos foram (Kg/mm²): SBWC: 314,50 ± 55,93ª ; SB: 256,78 ± 62,66b; STR: 253,90 ± 83,6b; TQ: 243,93 ± 68,3b; OS: 227,97 ± 67,1c; PB: 213,30 ± 91,3d; SS: 208,73 ± 86,6d. As médias ± DP de microdureza para as distâncias 150, 300, 450 mm da parede cavitária foram, respectivamente: 234,46 ± 77,81ª; 240,24 ± 85,12ª; 262,06 ± 79,46b. O grupo SBWC que não foi submetido aos protocolos de ciclagem térmica e pH mostrou a maior média de microdureza do esmalte e os FCAS resultaram nos menores valores de microdureza. Na distância de 450 mm da parede cavitária, a microdureza apresentou aumento significativo.

One of the most important uses of HVOF thermal plasma spray coatings is for wear resistance. In this work, the characteristics of nanocristalline CCr-NiCr coating and their effect on the mechanical properties and tribological behaviour of the material have been investigated. The objective of this study is the replacement of hazardous hard chromium plating technology used today in industry for an efficient and clean HVOF technology, using micro and nanocristalline CCr-NiCr coatings. Commercially available CCr-NiCr powder was mechanically treated, in order to obtain nano powders. Later the HVOF thermal spray process was used to produce conventional and nanocrystalline CCr-NiCr coatings. The ultra-microindentation technique was applied to evaluate the grain size effect in the hardness and the elasto-plastic properties of the coating. Difference in roughness has been determined by profilometry. The coating microstructures were characterised by SEM and optical microscopy and the porosity percentage was determined by Image Analysis technique. In order to evaluate the friction and wear properties of different substrate materials a reciprocating sliding motion has been used. CrC-NiCr standard coatings shows better tribological properties than WC-CoCr coatings.Una de las características más importantes de los recubrimientos de proyección térmica HVOF es su resistencia al desgaste. En este proyecto, se han investigado las características del recubrimiento nanocristalinos de CrC-NiCr y su efecto en las propiedades mecánicas y tribológicas del material. De acuerdo con los ensayos realizados, los recubrimientos nanocristalinos CrC-NiCr proporcionan una rugosidad un 66% menor, que los recubrimientos estándar, lo que produce una importante mejora en las propiedades de fricción (reducción coeficiente de fricción del 38%) y desgaste (reducción del desgaste del 84%).

The purpose of this study was to compare the microhardness of four indirect composite resins. Forty cylindrical samples were prepared according to the manufacturer’s recommendations using a Teflon mold. Ten specimens were produced from each tested material, constituting four groups (n=10) as follows: G1 - Artglass; G2 - Sinfony; G3 - Solidex; G4 - Targis. Microhardness was determined by the Vickers indentation technique with a load of 300g for 10 seconds. Four indentations were made on each sample, determining the mean microhardness values for each specimen. Descriptive statistics data for the experimental conditions were: G1 - Artglass (mean ±standard deviation: 55.26 ± 1.15HVN; median: 52.6); G2 - Sinfony (31.22 ± 0.65HVN; 31.30); G3 - Solidex (52.25 ± 1.55HVN; 52.60); G4 - Targis (72.14 ± 2.82HVN; 73.30). An exploratory data analysis was performed to determine the most appropriate statistical test through: (I) Levene's for homogeneity of variances; (II) ANOVA on ranks (Kruskal-Wallis); (III) Dunn's multiple comparison test (0.05). Targis presented the highest microhardness values while Sinfony presented the lowest. Artglass and Solidex were found as intermediate materials. These results indicate that distinct mechanical properties may be observed at specific materials. The composition of each material as well as variations on polymerization methods are possibly responsibles for the difference found in microhardness. Therefore, indirect composite resin materials that guarantee both good esthetics and adequate mechanical properties may be considered as substitutes of natural teeth.O objetivo deste estudo foi comparar a microdureza de 4 resinas compostas indiretas. Quarenta amostras cilíndricas foram obtidas com o auxílio de uma matriz de teflon, seguindo-se as recomendações dos fabricantes. Foram obtidas 10 amostras para cada material testado, contituindo-se 4 grupos (n=10) como se segue: G1-Artglass; G2-Sinfony; G3-Solidex; G4-Targis. A microdureza foi determinada pela técnica da indentação Vickers com uma carga de 300g por 10 segundos. Quatro indentações foram realizadas em cada amostra, obtendo-se um valor médio. Os dados da análise estatística descritiva para cada condição experimental foram: G1-Artglass (média ± desvio padrão:55,26 ± 1,15HVN; mediana: 52,6); G2- Sinfony (31,22 ± 0,65HVN; 31,30); G3- Solidex (52,25 ± 1,55HVN; 52,60); G4- Targis (72,14 ± 2,82HVN; 73,30). Uma análise exploratória dos dados foi realizada para determinar o teste estatístico mais apropriado: (I) Teste de Levene para variâncias homogêneas; (II) Teste de ANOVA (Kruskal-Wallis); (III) Teste de comparação múltipla de Dunn. O Targis apresentou os maiores valores de microdureza, enquanto que o Sinfony apresentou os menores valores. O Artglass e o Solidex se comportaram como materiais intermediários. Estes resultados indicaram que propriedades mecânicas distintas podem ser observadas nos materiais. A composição de cada material, bem como as variações nos métodos de polimerização são possivelmente responsáveis pelas diferenças observadas na microdureza. Portanto, materiais resinosos indiretos que garantam estética e propriedades mecânicas satisfatórias podem ser considerados como substitutos dos dentes naturais.

O presente trabalho tem como objetivo investigar a microestrutura e a microdureza de uma alumina sinterizada a 1650o durante 2 horas.

Las aleaciones de aluminio de la serie AW7XXX de medias prestaciones se están empleando ampliamente en el sector del transporte, así como en la construcción de estructuras soldadas. La posibilidad de que estas aleaciones se empleen con mayor profusión está condicionada a un mayor conocimiento del comportamiento de la unión soldada. La evolución de la microdureza como un indicador de resistencia es ampliamente utilizado, pero no hay acuerdo sobre el efecto de la preparación de bordes previo a la soldadura y es por ello que el objetivo de este trabajo sea estudiar la influencia de la preparación de bordes sobre el perfil de microdureza y microestructura de la unión soldada de una aleación de aluminio AW7020, soldada mediante el proceso MIG, empleando como metal de aporte AW5356.

The study is associated with the effect of aspirin (Acetyl Salicylic Acid) on the microhardness of mineralized tissues of the offspring's teeth, in response to the ingestion of the drug during pregnancy. Aspirin is a widely used analgesic and antipyretic medicine, for symptomatic treatment. Misuse of this drug during pregnancy may instigate developmental defects in offspring. An experimental control study was designed, in which female rabbits were taken as representative mammalian models and treated with aspirin during pregnancy. Their offspring's teeth were used to assess the microhardness of dental tissues. The rabbits were alienated into two groups, treated and control, consisting of seven rabbits in each set (n= 7). Microhardness was evaluated in three types of the sample teeth. The total number of teethexamined were, 2×7×12= 168 samples. Vicker's Hardness degree values were measured and recorded vis-à-vis (50 g for 15 s with 3 indentations per specimen on enamel and dentine separately). The range of hardness obtained was statistically analyzed and the Student's t-tests was applied, with the aid of SPSS version 20. The P-values for bothenamel and dentine from maxillary incisors and molars were less than 0.05. The same trend was observed in the mandibular teeth. However, a teratogenicity of Acetyl Salicylic Acid was pragmatic in the recent in vivo studies. Based on the analysis, it was evident that the aspirin administration could produce negative effects leading to reduction in the microhardness of dental tissues of the offsprings. [ABSTRACT FROM AUTHOR]

There has been a great advance in the grinding process by the development of dressing, lubri-refrigeration and other methods. Nevertheless, all of these advances were gained only for continuous cutting; in other words, the ground workpiece profile remains unchanged. Hence, it becomes necessary to study grinding process using intermittent cutting (grooved workpiece - discontinuous cutting), as little or no knowledge and studies have been developed for this purpose, since there is nothing found in formal literature, except for grooved grinding wheels. During the grinding process, heat generated in the cutting zone is extremely high. Therefore, plenty of cutting fluids are essential to cool not only the workpiece but also the grinding wheel, improving the grinding process. In this paper, grinding trials were performed using a conventional aluminum oxide grinding wheel, testing samples made of AISI 4340 steel quenched and tempered with 2, 6, and 12 grooves. The cylindrical plunge grinding was performed by rotating the workpiece on the grinding wheel. This plunge movement was made at three different speeds. From the obtained results, it can be observed that roughness tended to increase for testing sample with the same number of grooves, as rotation speed increased. Roundness error also tended to increase as the speed rotation process got higher for testing the sample with the same number of grooves. Grinding wheel wear enhanced as rotation speed and number of grooves increased. Power consumed by the grinding machine was inversely proportional to the number of grooves. Subsuperficial microhardness had no significant change. Micrographs reveal an optimal machining operation as there was no significant damage on the machined surface. [ABSTRACT FROM AUTHOR]

This work gathers a comparative study of the mechanical and tribological behaviour (microhardness under load, Young modulus, elasticplastic properties, friction and wear coefficients) of TiN/CrN and TiN/AlTiN multilayers deposited by conventional industrial PVD techniques. PVD multilayers with about between 50 nm individual layer thickness were deposited on flat samples of Co-cemented WC achieving a total thickness of about 2 microns. Mechanical and Tribological tests include microhardness under load at final loads between 10 mN aand 750 mN, Young modulus calculations and friction and wear tests.El presente trabajo recoge un estudio comparativo de las propiedades mecánicas y tribológicas (microdureza, fluencia, módulo elástico, coeficientes de fricción y desgaste), de multicapas TiN/AlTiN y TiN/CrN depositadas mediante técnicas industriales de PVD. Las capas, de espesores comprendidos entre 25nm y 100nm, se depositaron secuencialmente sobre substratos de WC, hasta obtener un espesor total de unas 2 micras. El estudio mecánico y tribológico comparativo incluyó ensayos de microdureza a cargas entre 10 mN y 750 mN, módulo elástico, comportamiento frente a fluencia y coeficientes de fricción y desgaste.

Al 5083 samples have been subjected to 90º equal-channel angular extrusion (ECAE) at 270ºC. After ECAE, the microhardness was measured and the texture for the plane perpendicular to the extrusion direction was analysed by X-Rays and EBSD. The microstructure was characterized by optical microscopy and EBSD. As deformation accumulates the hardness increases until it reaches saturation at an effective strain of about ε∼4. With regard to the texture, it has been shown that a high density of {111} planes are oriented parallel to the shear plane of the last pass.Varias muestras de aluminio 5083 se han sometido a extrusiones en canal angular de 90º a 270ºC. A continuación se midieron las durezas de las muestras obtenidas y se caracterizó la textura en el plano perpendicular a la dirección de extrusión mediante Rayos-X y difracción de electrones retrodispersados (EBSD). La caracterización microestructural se hizo mediante microscopio óptico y EBSD. Se ha observado que la dureza aumenta sensiblemente con el grado de deformación y que alcanza un nivel máximo de saturación a partir de ε∼4. En cuanto a la textura, se observa que los planos {111} tienden a orientarse paralelos al plano de la última cortadura.

UNS S32205 duplex stainless steel welds were performed by friction stir welding (FSW). Advancing and retreating sides showed distinct characteristics in the welded joint. The advancing side shows the strongest grain refinement which is corroborated by microhardness measurements. The microstructure characterization was carried out by optical, scanning and transmission electron microscopy. The thermomechanically affected zone displays austenite islands deformed in a ferrite matrix. The stir zone (SZ) showed a fine recrystallized microstructure providing an outstanding increase of hardness associated with better corrosion performance. Transmission electron microscopy and corrosion tests have corroborated the absence of intermetallic phases on welded joints. [ABSTRACT FROM AUTHOR]

Copyright of Revista Odonto Ciencia is the property of EDIPUCRS - Editora Universitaria da PUCRS and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)