In this research work, we reported the synthesis of a spherical-shaped bismuth vanadate (BiVO4) photocatalyst using a cost-effective, simple, chemical hydrothermal method and studied the effect of deposition temperatures on the structural, morphological, optical properties, etc. The XRD result confirmed the monoclinic scheelite phase of BiVO4. An XPS study confirmed the occurrence of Bi, V, and O elements and also found that Bi and V exist in +3 and +5 oxidation states, respectively. SEM micrographs revealed the spherical-shaped morphology of the BiVO4 photocatalyst. Optical investigation showed that the bandgap of the BiVO4 photocatalyst varied between 2.25 and 2.32 eV. The as-synthesized BiVO4 photocatalyst was used to study the photocatalytic degradation of crystal violet (CV) dye under visible light illumination. The photocatalytic degradation experiment showed that the degradation percentage of crystal violet dye using BiVO4 reached 98.21% after 120 min. Mineralization of crystal violet dye was studied using a chemical oxygen demand analysis.

Barium titanate (BaTiO3) thin films have been prepared using the spray pyrolysis method. The films were deposited onto a glass substrate at varying substrate temperature ranging from 250 to 350 °C with the interval of 50 °C. The structural, morphological, electrical and dielectric properties of the deposited films have been studied. The X-ray diffraction pattern confirmed the polycrystalline nature of the films with a cubic crystal structure. X-ray photoelectron spectroscopy (XPS) showed a good agreement of the thin films stoichiometry with BaTiO3. A presence of Ba, Ti and O in the BaTiO3 thin films was observed by energy dispersive X-ray analysis. The scanning electron microscopy (SEM) showed the heterogeneous distribution of cubical grains all over the substrate. The grain size decreased with an increase in substrate temperature. The dielectric constant and dielectric loss showed the dispersion behaviour as a function of frequency, measured in the frequency range of 20 Hz to 1 MHz. The AC conductivity (σac) measurement showed the linear nature of obtained films, which confirms conduction mechanism due to small polarons. Impedance spectroscopy has been used to study the electrical behaviour of BaTiO3 ferroelectric thin films. The ferroelectric hysteresis loop has been recorded at room temperature.