Abstract A Bio composite comprising Prosopis Juliflora Fiber (PJF) and Poly Lactic Acid (PLA) was processed considering two particulate sized reinforcements, coarse PJF (avg. 15 µm) and fine PJF (10-50 nm). They were added individually at ratios of 10, 15, 20 and 25 wt% into PLA matrix. The composites were extruded and tested for mechanical properties. The addition of PJF resulted with an increase in the tensile, flexural and impact strengths of the polymer. Adding PJF to PLA showed a decrease in the hardness of the polymer. Water Absorption test showed an increase in water uptake with increasing fiber content. The most optimum ratio of PLA to PJF was found to be 80:20. The fine PJF reinforced composites proved to be superior over the coarse PJF reinforced composites at all stages of the research. FESEM and TGA were used to study morphology and thermal characteristics respectively.

Abstract The blending of nanoclay in polymers has potential prospects in the recent development of composite technology. In this present research work, Nanoclay was added to Glass fiber and Abaca fiber reinforced hybrid epoxy composites to enhance the wear resistance of the material. Nanoclay at weight ratios of 2%, 4%, 6%, and 8% was reinforced and the composite was fabricated into laminates using compression moulding. Nanoclay reinforced composites were tested for mechanical characteristics and wear rate in comparison to the non nanoclay reinforced hybrid composites. Water absorption character and morphology were also studied. It was observed that the 4% nanoclay reinforced composites showed the optimum results, with an increase in tensile strength, flexural strength and impact strengths of 6.6%, 19.6%, and 22.6% respectively when compared with EGA composite. Similarly the wear rate of the 4% nanoclay reinforced composite also was better than the EGA composite, showing an increase of 22.1% improved resistance.