Search

The ability of TiO2 to generate reactive oxygen species under UV radiation makes it an efficient candidate in antimicrobial studies. In this context, the preparation of TiO2 microparticles coated with Ca- and Cu-based composite layers over which Cu(II), Cu(I), and Cu(0) species were identified is presented here. The obtained materials were characterized by a wide range of analytical methods, such as X-ray diffraction, electron microscopy (TEM, SEM), X-ray photoelectron (XPS), and UV-VIS spectroscopy. The antimicrobial efficiency was evaluated using qualitative and quantitative standard methods and standard clinical microbial strains. A significant aspect of this composite is that the antimicrobial properties were evidenced both in the presence and absence of the light, as result of competition between photo and electrical effects. However, the antibacterial effect was similar in darkness and light for all samples. Because no photocatalytic properties were found in the absence of copper, the results sustain the antibacterial effect of the electric field (generated by the electrostatic potential of the composite layer) both under the dark and in light conditions. In this way, the composite layers supported on the TiO2 microparticles’ surface can offer continuous antibacterial protection and do not require the presence of a permanent light source for activation. However, the antimicrobial effect in the dark is more significant and is considered to be the result of the electric field effect generated on the composite layer.

Ferromagnetic FexGe1−x with x = 2%–9% are obtained by Fe deposition onto Ge(001) at high temperatures (500 °C). Low energy electron diffraction (LEED) investigation evidenced the preservation of the (1 × 1) surface structure of Ge(001) with Fe deposition. X-ray photoelectron spectroscopy (XPS) at Ge 3d and Fe 2p core levels evidenced strong Fe diffusion into the Ge substrate and formation of Ge-rich compounds, from FeGe3 to approximately FeGe2, depending on the amount of Fe deposited. Room temperature magneto-optical Kerr effect (MOKE) evidenced ferromagnetic ordering at room temperature, with about 0.1 Bohr magnetons per Fe atom, and also a clear uniaxial magnetic anisotropy with the in-plane easy magnetization axis. This compound is a good candidate for promising applications in the field of semiconductor spintronics.

The effect of illumination on the hydrofluoric acid etching of AlAs sacrificial layers with systematically varied thicknesses in order to release and roll up InGaAs/GaAs bilayers was studied. For thicknesses of AlAs below 10 nm, there were two etching regimes for the area under illumination: one at low illumination intensities, in which the etching and releasing proceeds as expected and one at higher intensities in which the etching and any releasing are completely suppressed. The “etch suppression” area is well defined by the illumination spot, a feature that can be used to create heterogeneously etched regions with a high degree of control, shown here on patterned samples. Together with the studied self-limitation effect, the technique offers a way to determine the position of rolled-up micro- and nanotubes independently from the predefined lithographic pattern.

Applied surface science 267, 106 - 111 (2013). doi:10.1016/j.apsusc.2012.08.016, The surface structure, interface reactivity, electron configuration and magnetic properties of Sm layers deposited on Si(0 0 1) at various temperatures are investigated by low-energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS) and magneto-optical Kerr effect (MOKE). It is found that metal Sm is present on samples prepared at low temperature, with an interface layer containing SmSi2 and Sm4Si3. When samples are prepared at high temperature, much less metal Sm is found, with an increasing amount of SmSi2. Room temperature ferromagnetism is observed for all prepared layers, with a decrease of the saturation magnetization when samples are prepared at high temperature. It is found that ferromagnetism implies mostly a compound with approximate stoichiometry Sm4Si3. Also, the decrease in the intensity of the XAS 2p3/2 → 3d white lines with the corresponding increasing amount of SmSi2 may be explained by assuming a higher occupancy of Sm 5d orbitals (5d2 configuration), most probably due to hybridation effects., Published by North-Holland, Amsterdam