Search

This study aimed to develop resin coatings containing monocalcium phosphate monohydrate (MCPM), Sr/F-doped bioactive glass (Sr/F-BAGs), and pre-reacted glass ionomer fillers (SPG) that enhance ion release without detrimentally affecting the mechanical properties of GIC. The objective of this study was to evaluate the degree of monomer conversion (DC), biaxial flexural strength, surface microhardness, and ion release of the GICs coated with experimental coating materials compared to a commercial product (EQUIA Coat, EC). Four experimental resin coating materials containing 10–20 wt% of MCPM with Sr/F-BAGs and 5–10 wt% SPG were prepared. The DC of the coating material was determined using ATR-FTIR. The flexural strength and surface microhardness of the coated GICs were assessed. Fluoride and elemental (Ca,P,Sr,Si,Al) release were measured using fluoride-specific electrodes and ICP-OES. The DC of the experimental coating material (60–69 %) was higher than that of EC (55 %). The strength of GICs coated with experimental materials (35–40 MPa) was comparable to EC (37 MPa). However, their surface microhardness (13–24 VHN) was lower than EC (44 VHN). The experimental coating materials reduced fluoride release by ∼43 %, similar to EC (∼40 %). However, experimental coating materials promoted higher P and Sr release than EC. In conclusion, GICs coated with the experimental resin coating containing ion-releasing additives exhibited mechanical properties similar to those of the commercial product. The new coating materials promoted a higher level of ion release for GICs. These properties could potentially enhance remineralizing actions for the coated GICs.

Abstract Objective This study aimed to develop enamel substitute material using a mechanochemical technique. Materials and Methods Hydroxyapatite was synthesized with and without tricalcium phosphate under uniaxial pressing of 10 and 17 MPa (HA10, HA17, BCP10, and BCP17), followed by sintering at 1250 °C for 2 h. Human enamel and dentin blocks were used as control groups. The mechanical properties were determined by compressive strength test and Vickers microhardness. The data were analyzed with one-way ANOVA and LSD post-hoc test (α = 0.05). The phase formation and morphology of the specimens were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Results HA17 and HA10 had compressive strength values comparable to enamel and dentin, respectively (p > 0.05). The microhardness of all synthesized groups was significantly higher than that of tooth structures (p

Abstract Background Polymeric sponge technique is recommended for developing the desired porosity of Biphasic calcium phosphate (BCP) which may favor bone regeneration. Purpose To investigate the healing of BCP with ratio of HA30/β‐TCP70 (HA30) and HA70/β‐TCP30 (HA70) polymeric sponge preparation, compare to commercial BCP (MBCP+TM). Materials and Methods Materials were tested X‐ray diffraction (XRD) pattern and scanning electron microscope (SEM) analysis. In eight male pigs, six calvarial defects were created in each subject. The defects were the filled with 1 cc of autogenous bone, MBCP+TM (MBCP), HA30, HA70, and left empty (negative group). The new bone formations, residual material particles and bone‐to‐graft contacts were analyzed at 4, 8, 12 and 16 weeks. Results Fabricated BCP showed well‐distributed porosity. At 16 weeks, new bone formations were 45.26% (autogenous), 33.52% (MBCP), 24.34% (HA30), 19.43% (HA70) and 3.37% (negative). Residual material particles were 1.88% (autogenous), 17.58% (MBCP), 26.74% (HA30) and 37.03% (HA70). These values were not significant differences (Bonferroni correction

Bone tissue engineering is a complicated field requiring concerted participation of cells, scaffolds, and osteoactive molecules to replace damaged bone. This study synthesized a chitosan-based (CS) scaffold incorporated with trichostatin A (TSA), an epigenetic modifier molecule, to achieve promising bone regeneration potential. The scaffolds with various biphasic calcium phosphate (BCP) proportions: 0%, 10%, 20%, and 40% were fabricated. The addition of BCP improved the scaffolds’ mechanical properties and delayed the degradation rate, whereas 20% BCP scaffold matched the appropriate scaffold requirements. The proper concentration of TSA was also validated. Our developed scaffold released TSA and sustained them for up to three days. The scaffold with 800 nM of TSA showed excellent biocompatibility and induced robust osteoblast-related gene expression in the primary human periodontal ligament cells (hPDLCs). To evaluate in vivo bone regeneration potential, the scaffolds were implanted in the mice calvarial defect model. The excellent bone regeneration ability was further demonstrated in the micro-CT and histology sections compared to both negative control and commercial bone graft product. New bone formed in the CS/BCP/TSA group revealed a trabeculae-liked characteristic of the mature bone as early as six weeks. The CS/BCP/TSA scaffold is an up-and-coming candidate for the bone tissue engineering scaffold.

The aim of this study was to prepare experimental resin-modified glass ionomer cements (RMGICs) containing low levels of hydroxyethyl methacrylate (HEMA) for pulp protection. Liquid and powder phases of the experimental RMGICs were polyacid functionalized with methacrylate groups and spherical pre-reacted glass fillers (SPG). Two types of liquid phase containing 0 wt. % HEMA (CM liquid) or 5 wt. % HEMA (CMH liquid) were formulated. The experimental RMGICs were prepared by mixing SPG fillers with CM liquid (F1) or CMH liquid (F2). Rheological properties were examined using a strain-controlled rheometer (n = 5). The Vickers microhardness (n = 5) and dentin shear bond strength (SBS) (n = 10) of the materials were tested. Commercial pulp protection materials (Vitrebond and TheraCal LC) were used as comparisons. The viscosity and surface microhardness of F1 (22 m Pa·s, 18 VHN) and F2 (18 m Pa·s, 16 VHN) were significantly higher than those of Vitrebond (6 mPa·s, 6 VHN) and TheraCal (0.1 mPa·s, 7 VHN). The SBS of F1 (10.7 MPa) and F2 (11.9 MPa) was comparable to that of Vitrebond (15.4 MPa) but higher than that of TheraCal LC (5.6 MPa). The addition of 5 wt. % HEMA showed no significant effect on viscosity, surface microhardness, or SBS of the experimental RMGICs. The experimental materials showed higher viscosity and microhardness but similar SBS when compared with the commercial RMGIC.

Poly(alkenoic acid)s based on copolymers of acrylic acid and itaconic acid were synthesized and further modifiedwith glutamic acid (Glu) and glycidyl methacrylate (GMA). The resultant polymers were characterized by means of protonnuclear magnetic resonance, gel permeation chromatography, and elemental analysis. Specimens of resin modified glassionomer cement (RMGIC) prepared from the cement-forming reactions between the synthesized polymers and a commerciallyreactive glass were fabricated and investigated for flexural strength using three-point bending test. The effects of differentamounts of Glu and GMA on the flexural strength were evaluated. The results showed significantly improved cement strengthdue to the incorporation of Glu into the copolymer with an optimal feed of Glu and GMA at 0.1-0.2 and 0.4 per mole ofcopolymer, respectively. The addition of 2-hydroxyethyl methacrylate (HEMA) to the RMGIC formulations tremendouslyincreased the cement strength. In this study, a formulation containing 20%-wt. of HEMA and 45%-wt. of polymer concentration gave the highest flexural strength with 62.7±3.4 MPa.

Glass ionomer cements (GICs), widely used as restorative materials in dentistry, are principally composed of fluoroaluminosilicateglass powder combined with a water-soluble polyacid. The investigation of new glass compositions and polyacid components are very important to improve the mechanical properties of these cements. The objective of this work was to prepare glass ionomers and polyacids for the use as GICs. The effects of spherical bodies, Al2O3:SiO2 ratios, replacing CaO by SrO, and ZrO2 adding in glass powder in combination with the variation of acidic copolymer concentration on the compressive strength were investigated and discussed.

This work proposes four different glass formulas derived from the SiO2-Li2O-K2O-Al2O3 system to investigate the effect of glass composition on their crystal formations and properties. Glass LD1 was SiO2-Li2O-K2O-Al2O3 system with the addition of P2O5 and CaF2 as nucleating agents. In Glass LD2, a slight amount of MgO was mixed in order to increase the viscosity of the melting glass. Finally, the important factor of Si : Li ratio was increased in Glasses LD3 and LD4 with compositions otherwise the same as LD1 and LD2. The results found that P2O5 and CaF2 served as a nucleating site for lithium phosphate and fluorapatite to encourage heterogenous nucleation and produce a fine-grained interlocking microstructure of lithium disilicate glass ceramics. MgO content in this system seemed to increase the viscosity of the melting glass and thermal expansion coefficient including the chemical solubility. Increasing the Si : Li ratio in glass compositions resulted in the change of the microstructure of Li2Si2O5 crystals.

Purpose: This study aimed to evaluate the effect of biphasic calcium phosphate (BCP) with high hydroxyapatite/tricalcium phosphate (HA/TCP) ratios on bone formation in rabbit calvarial defects. Materials and Methods: Sixteen New Zealand white rabbits were randomly divided into two groups, a control group and an experimental group. In each animal, bilateral circular defects (10-mm diameter) were created on the calvarium. In the control group (three rabbits per time frame), defects were grafted with autogenous bone chips in one side and left empty in the other side. In the experimental group (five rabbits per time frame), defects were grafted with BCP1 (HA:TCP, 8:2) in one side and BCP2 (HA:TCP, 9:1) in the contralateral side. The animals were sacrificed at 2 and 8 weeks as designated. Bone formation and residual grafting material were assessed by radiographic densitometry, microcomputed tomography (micro-CT), and histomorphometric analysis. Results: Histologic observation revealed that BCP1, BCP2, and the autogenous bone group preserved good contours of the defect, while the unfilled defect group showed connective tissue healing. Micro-CT analysis at 8 weeks showed the comparable percentages of bone volume fraction (% BV/TV) of BCPI (20.70% ± 2.76%) and BCP2 (20.72% ± 3.97%) and two times higher than that of 2 weeks (9.90% ± 0.75%, 10.57%> ± 0.85%). The autogenous group had a significantly (P < .005) greater % BV/TV (34.58%o ± 8.85%) than other groups. The percentage of the material volume fraction of BCP1 and BCP2 was not different. The histomorphometry demonstrated a higher increase in newly formed bone from 2 to 8 weeks in all groups, and all were comparable (autogenous: 4.30% ± 0.76%, 12.83% ± 7.74%; unfilled: 2.82% ± 1.19%, 8.14% ± 6.35%; BCP1: 3.01% ± 2.57%, 8.81% ± 3.86%; BCP2: 3.24% ± 1.09%, 10.27% ± 3.98%). Conclusion: BCP with a high ratio of HA presented good osteoconductive properties and space-maintaining capacity and would be beneficial for long-term preservation or when stable graft volume is essential. [ABSTRACT FROM AUTHOR]

This study was to evaluate the acid-buffering capacity and antibacterial properties of orthodontic adhesives containing bioactive glasses (BAGs) (45S5, 45S5F, S53P4), Hydroxyapatite, beta-tricalcium phosphate, and Canasite. Fillers comprising 15 wt% bioactive glasses, HAp, β-TCP, and Canasite incorporated with 55 wt% silanated glass were added to a mixture of UDMA/TEGDMA. Acidbuffering capacity was tested by exposing disc-shaped samples of each adhesive to medium of bacteria-produced acids, and pH changes were recorded at 24 and 48 h. Antibacterial properties were assessed by indirect testing by exposing polymerized adhesive samples to a medium and direct testing by immersing the specimens in solutions containing S. mutans and S. sanguinis. A significant buffering capacity was shown by the 45S5, 45S5F and S53P4 BAG adhesives. The antibacterial properties were not significant in all experimental adhesives. Therefore, the experimental orthodontic adhesives containing BAGs demonstrated a significant buffering capacity but did not show significant antibacterial properties against S. mutans and S. sanguinis [ABSTRACT FROM AUTHOR]