Search

(1) Background: currently, the advantages of bulk-fill resin composite and high-viscosity glass ionomer materials have increased their use in dentistry; accordingly, their mechanical, surface, and optical properties have become more important. This study aimed to evaluate the mechanical, surface, and optical properties of three different restorative materials (a high-viscosity bulk-fill resin composite (TNC), a flowable bulk-fill resin composite (EBF), and a high-viscosity glass ionomer (FIX)) after application using different techniques (control, heat application, and ultrasonic activation). (2) Methods: specimens were prepared to assess the color stability and surface roughness (n = 12). The specimens were immersed in two different solutions for 14 days. For the compressive strength test, specimens were prepared using a Teflon mold (n = 12). (3) Results: among the specimens applied according to the manufacturer's instructions and immersed in distilled water, it was observed that the surface roughness values of FIX on the 7th day were statistically significantly higher than the other materials (p < 0.05). The compressive strength values of EBF applied using ultrasonic activation were significantly lower than those of EBF applied using the other techniques (p < 0.05). (4) Conclusions: coffee can negatively affect the color stability of restorative materials, but discoloration may vary depending on differences in the content of the material. All materials evaluated in this study exhibited clinically acceptable surface roughness values. It can be concluded that flowable bulk-fill resin composite is the most durable material in terms of compressive strength, so it can be used in the restoration of posterior teeth, especially those exposed to intensive stress. [ABSTRACT FROM AUTHOR]

The aim of this study is to evaluate the effectiveness of in-office bleaching in esthetic dentistry on the roughness and color stability of the enamel surface, using different concentrations of hydrogen peroxide (HP). Fifty human incisors were randomly divided into 5 groups (n = 10). No bleaching was performed in the control group. For these groups, concentrations of 40% HP with fluoride (F), 35% HP with calcium (Ca), 25% HP with nano-hydroxyapatite (nHA) and 18% HP with nHA were used for bleaching in the test groups. Surface roughness was assessed at baseline after bleaching occurred. Color measurements were first obtained at baseline, then after the first and second sessions of bleaching, and, finally, after the staining protocol. Scanning electron microscopy and atomic force microscopy were performed. Statistical analysis was conducted with a one-way ANOVA, followed by a post hoc Tukey's test and a paired-samples t-test (p < 0.05). All the bleaching gels used exhibited a similar color change (p > 0.05). Bleaching gels containing 18% HP with nHA and that containing 35% HP with Ca caused less surface roughness of the enamel. Of these concentrations, 25% HP with nHA caused the most surface roughness and no significant difference was observed, compared with 40% HP with F. The highest coloration after bleaching was observed in 40% HP with F and 25% HP with nHA. The lowest coloration was obtained in 35% HP with Ca and 18% HP with nHA but no significant difference was observed between them and the control group. A concentration above 18% HP does not increase the bleaching effectiveness. The results show that 18% HP with nHA and 35% HP with Ca resulted in the least increase in enamel surface roughness when compared to high-concentrate HP; however, it also prevented recoloration after bleaching. [ABSTRACT FROM AUTHOR]

Background: The various advantages of crown materials produced using three-dimensional (3D) printers have increased their use in restorative and prosthetic dentistry in recent years. Accordingly, their optical and mechanical properties have become more important., Objectives: To evaluate the mechanical, surface and optical properties of crown materials produced with 3D printing and computer-aided design (CAD)/computer-aided manufacturing (CAM), which has recently been used frequently in the clinic., Material and Methods: The 3-point bending test was used to evaluate the mechanical properties of 2 different crown materials produced with 3D printing (Permanent Crown and VarseoSmile Crown Plus) and a crown material produced using CAD/CAM (Vita Enamic). After the initial color and surface roughness measurements were made, the specimens were immersed in 4 different solutions., Results: The most translucent material was VarseoSmile Crown Plus (p < 0.05). In all specimens, coffee caused the most discoloration (p < 0.05). The effects of the solutions on the roughness were mostly observed in Permanent Crown specimens (p < 0.05). Vita Enamic showed the highest statistically significant values in terms of flexural strength (p < 0.05)., Conclusions: The stereolithographic technique among the materials produced by 3D printing can be recommended for use in restorations due to its higher flexural strength.