Search

The service life of rolling contacts is dependent on many factors. The choice of materials in particular has a major influence on when, for example, a ball bearing may fail. Within an exemplary process chain for the production of hybrid high-performance components through tailored forming, hybrid solid components made of at least two different steel alloys are investigated. The aim is to create parts that have improved properties compared to monolithic parts of the same geometry. In order to achieve this, several materials are joined prior to a forming operation. In this work, hybrid shafts created by either plasma (PTA) or laser metal deposition (LMD-W) welding are formed via cross-wedge rolling (CWR) to investigate the resulting thickness of the material deposited in the area of the bearing seat. Additionally, finite element analysis (FEA) simulations of the CWR process are compared with experimental CWR results to validate the coating thickness estimation done via simulation. This allows for more accurate predictions of the cladding material geometry after CWR, and the desired welding seam geometry can be selected by calculating the cladding thickness via CWR simulation. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.

The Collaborative Research Centre 1153 (CRC 1153) &ldquo, Process chain for the production of hybrid high-performance components through tailored forming&rdquo, aims to develop new process chains for the production of hybrid bulk components using joined semi-finished workpieces. The subproject B1 investigates the formability of hybrid parts using cross-wedge rolling. This study investigates the reduction of the coating thickness of coaxially arranged semi-finished hybrid parts through cross-wedge rolling. The investigated parts are made of two steels (1.0460 and 1.4718) via laser cladding with hot-wire. The rolling process is designed by finite element (FE)-simulations and later experimentally investigated. Research priorities include investigations of the difference in the coating thickness of the laser cladded 1.4718 before and after cross-wedge rolling depending on the wedge angle &beta, cross-section reduction ∆A, and the forming speed &nu, Also, the simulations and the experimental trials are compared to verify the possibility of predicting the thickness via finite element analysis (FEA). The main finding was the ability to describe the forming behavior of coaxially arranged hybrid parts at a cross-section reduction of 20% using FEA. For a cross-section reduction of 70% the results showed a larger deviation between simulation and experimental trials. The deviations were between 0.8% and 26.2%.

The present paper describes a new method concerning the production of hybrid bevel gears using the Tailored Forming technology. The main idea of the Tailored Forming involves the creation of bi-metal workpieces using a joining process prior to the forming step and targeted treatment of the resulting joint by thermo-mechanical processing during the subsequent forming at elevated temperatures. This improves the mechanical and geometrical properties of the joining zone. The aim is to produce components with a hybrid material system, where the high-quality and expensive material is located in highly stressed areas only. When used appropriately, it is possible to reduce costs by using fewer high-performance materials than in a component made of a single material. There is also the opportunity to significantly increase performance by combining special load-tailored high-performance materials. The core of the technology consists in the material-locking coating of semi-finished parts by means of plasma-transferred-arc welding (PTA) and subsequent forming. In the presented investigations, steel cylinders made of C22.8 are first coated with the higher-quality heat-treatable steel 41Cr4 using PTA-welding and then hot-formed in a forging process. It could be shown that the applied coating can be formed successfully by hot forging processes without suffering any damage or defects and that the previous weld structure is completely transformed into a homogeneous forming-typical structure. Thus, negative thermal influences of the welding process on the microstructure are completely neutralized.