Objective: To explore and characterize the effect of the discrepancy between crestal bone height (CB) and pulp chamber floor (PCF) in the fatigue performance of endodontically-treated teeth rehabilitated with an endocrown restoration. Materials and methods: A total of 75 human molars free of defects, caries history or cracks were selected, then endodontically treated and randomly allocated into 5 groups (N = 15) according to the difference between PCF and CB, as follows: PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below. Endocrown restorations were made with composite resin (Tetric N-Ceram, shade B3, Ivoclar) in 1.5 mm thickness and luted with a resin cement (Multilink N, Ivoclar) onto the dental elements. Monotonic testing was performed to define the fatigue parameters, and a cyclic fatigue test was used until failure of the assembly. The collected data were submitted to statistical survival analysis (Kaplan-Meier followed by Mantel-Cox and Weibull), fractographic analysis and finite element analysis (FEA) were performed as complementary analyzes. Results: The PCF 2 mm below and PCF 1 mm below groups presented the best results regarding fatigue failure load (FFL) and number of cycles for failure (CFF) (p < 0.05), but presented no difference between each other (p > 0.05). The PCF leveled and PCF 1 mm above groups presented no statistical difference between them (p > 0.05), but performed better than the PCF 2 mm above group (p < 0.05). The rate of favorable failures of PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below groups were 91.7%, 100%, 75%, 66.7% and 41.7%, respectively. FEA showed different stress magnitudes according to the pulp-chamber design. Conclusion: The insertion level of the dental element to be rehabilitated with an endocrown interferes in the mechanical fatigue performance of the set. The discrepancy between the CB height and the PCF has a direct effect, where the higher the PCF in relation to the CB, the greater the risk of mechanical failure of the restored dental element.

The present study aimed to determine the influence of adhesive luting on the fatigue mechanical properties of simplified lithium disilicate crowns luted to dentin analogues preparations, and to compare two different approaches of simulation of a non-adhesive luting procedure. To this end, 30 prosthetic preparations of glass fiber-filled epoxy resin used as dentin analogues were milled and lithium disilicate crowns were pressed (1.5 mm thickness), which were allocated into three different groups: resin cement (RC), resin cement isolated by paraffin oil (RCI) and zinc phosphate cement (ZP). For luting procedures, the ceramic crowns of the RC and RCI groups had their internal surface treated with 5% hydrofluoric acid and universal primer. Afterwards, a thin layer of paraffin oil was applied onto the ceramic crown intaglio surface in the RCI group. The dentin analogues were treated with 10% hydrofluoric acid, followed by primer application and luting as recommended by the manufacturer. No previous surface treatments were performed for the ZP group, and the cement was applied as recommended. The fatigue test was run under cyclic fatigue (load 400–2000 N, step-size 100 N, 15,000 cycles/step, frequency 20 Hz) until failure detection (radial crack) by transillumination. The fatigue failure load (FFL), number of cycles until failure (CFF), and survival rate in each testing step were recorded. The RC group presented a higher FFL, CFF and survival rate compared to the other groups (p < 0.001), which were statistically equal to each other (p > 0.05). Weibull analysis detected no difference between groups for the Weibull module. Therefore, loss of adhesion between the evaluated substrates induces a significant reduction in load-bearing capacity under fatigue of the lithium disilicate crowns, strengthening the strong-importance of long-lasting adhesion for crown's survival. In addition, different methods for the simulation of non-adhesive conditions induce the same performance in the explored outcomes, confirming that both are valid approaches for laboratory studies.

Objectives: To evaluate the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4YSZ simplified restorations. Methods: Ceramic discs (Ø = 10 mm, thickness = 1 mm) were randomly allocated into 6 groups considering: “In-lab simulation of CAD/CAM grinding” (ground or polished) and “intaglio surface treatments”: Ctrl (without surface treatment), AlOx (aluminum oxide air abrasion) or GLZ (glaze spray application). The surface roughness of all samples was measured, the treated discs received a ceramic primer, were luted with resin cement onto a dentin analogue material (woven glass-reinforced epoxy resin) and tested under a cyclic fatigue test (step-stress approach, n = 15; 1.4 Hz, 10,000 cycles/step, step-size of 100N starting at 200N until failure). A complementary analysis was performed to corroborate the findings in the fatigue test that the glaze fill defects increase the mechanical properties of the ceramic. To do so, bars (n= 10; 1.0 × 1.0 × 12 mm; considering the groups: N-ID: non-indented; ID: indented; ID-GLZ: indented plus glaze spray application) were indented in a vickers hardness tester to produce a crack pattern, treated with glaze or not, and then submitted to flexural strength tests (FS). Fractographic and topographic analysis were performed. Results: In-lab simulation of CAD/CAM grinding decreased the fatigue failure load of the 4YSZ ceramic when comparing polished and ground groups, regardless of surface treatment. GLZ induced better fatigue performance compared to the air abrasion, regardless of the grinding condition (ground or polished surface). The results of the flexural strength test corroborated the findings in the fatigue test, as the ID-GLZ group presented superior FS than the ID group, however both had inferior FS than N-ID. There is an inverse association between roughness and fatigue failure load, as the higher the surface roughness, the lower the fatigue failure load. Failures in the fatigue and flexural strength tests started from the face subjected to tensile stresses. Conclusion: In-lab simulation of CAD/CAM grinding had a detrimental effect on the fatigue behavior of 4YSZ and glaze spray induced better 4YSZ performance compared to the air abrasion. The intaglio surface treatments differently influenced the 4YSZ fatigue performance, however, only glaze spray can reverse the damage caused by the grinding.

This study aimed to investigate the effect of surface roughness (polished vs. CAD/CAM milling simulation) on impact strength of five dental ceramics for manufacturing CAD/CAM monolithic restorations. Specimens of five ceramics (FC- feldspathic glass-ceramic; PICN- polymer-infiltrated ceramic-network; ZLS- zirconia-reinforced lithium silicate glass-ceramic; LD- lithium disilicate glass-ceramic; YZ- yttria-stabilized tetragonal zirconia polycrystal ceramic) to be tested under impact (15×10×2mm3; n= 15) were divided into two groups, according to surface treatment: polishing (pol) and grinding (gri) as CAD/CAM milling simulation. Impact strength was tested using the Dynstat method. Roughness, topographic, fractographic and finite element analyses were performed. The impact strength data were analyzed by Weibull, and Pearson correlation was used to correlate roughness and impact strength data. The CAD/CAM milling simulation led to significantly (p

© 2021 Wiley Periodicals LLC.Objective: To evaluate the effect of surface treatments on optical, colorimetric, and surface characteristics of lithium disilicate glass–ceramic. Materials and Methods: Specimens (n = 5, IPS e.max CAD) were randomly allocated to the following treatments: mirror-polished: SiC papers; as-cut: mimicking CAD-CAM milling; ground: 90-120 μm-grit diamond bur; ground polished: ground, finished (46-30 μm-grit diamond bur), polished (diamond cups, brush and diamond paste); ground glazed: ground, glazed; ground polished glazed: association of methods. CIELAB color coordinates were obtained by a spectrophotometer. CIEDE2000 color differences (ΔE00) and the translucency parameter (TP00) were calculated. Light transmittance was assessed with a colorimeter. Surface characteristics (topography and roughness) were analyzed. Statistical differences for each condition and outcome were detected using one-way ANOVA with Tukey's post-hoc test (α = 0.05). Results: TP00 data show statistical reduction after grinding (p < 0.05), which was only restored with polishing (solely or with glazing). ΔE00 shows that grinding results in perceptible variations in color (above 0.81), which were restored after all post-processing protocols (exception to only glaze application in contact with a black background). Light transmittance data corroborated such performance. Polishing and glazing reduced roughness and improved surface topography. Conclusion: Grinding statistically increased roughness, reduced translucency, light transmittance through the ceramic, and resulted on color differences. On contrary, polishing (followed or not by glazing) reduced roughness and enhanced ceramic translucency and light transmittance. Glaze also reduced roughness, but it still presented reduced translucency. The positioning (facing up or down) of the ceramic treated surface influenced the considered outcomes. Clinical Significance: Grinding with diamond burs results in a deleterious impact to the optical, colorimetric and surface characteristics of lithium disilicate ceramic. Thus, polishing (followed or not by glazing) is recommended for optical and topographical enhancements when lithium disilicate monolithic restorations require occlusal adjustments.

It aims on evaluate the effect of the test environment on static fatigue behavior of lithium disilicate-based (LD), and yttrium oxide-stabilized zirconia (YSZ) ceramics. Specimens of LD (IPS e.max CAD, Ivoclar Vivadent) and YSZ (IPS e.max ZirCAD MO, 3 mol% Y2O3, Ivoclar Vivadent) were randomly allocated into three groups: tested in air, inert (paraffin oil, Sigma Aldrich) or distilled water. The static fatigue test (n=15) was performed using a piston-on-three ball assembly, adapted from ISO 6872, as follows: starting load 100 N for LD and 300 N for YSZ; loading application time set to 1 hour for each loading step; step size of 50 N for LD and 100 N for YSZ, applied successively until fracture. Data from static fatigue strength (MPa) and time to fracture (hours) were recorded. Fractographic analysis was executed. Survival analysis corroborates absence of influence of environment on static fatigue outcomes (fatigue strength, time to fracture and survival rates) for YSZ. For LD, specimens tested in air presented statistically superior survival rate and static fatigue strength (p= 0.025). In regards of time to fracture, LD tested in air were superior than when tested in distilled water (p=0.019) or inert (p=0.017) environments. No statistical differences for Weibull modulus were observed. Failures started on the tensile stress surface. Thus, the test environment did not affect slow crack growth (SCG) mechanisms during static fatigue test of YSZ ceramics, but it plays a significant role for the static fatigue behavior of lithium disilicate-based glass ceramics, indicating a high susceptibility to SCG. Resumo O presente estudo objetivou investigar a influência do ambiente de teste no comportamento a fadiga estática (resistência à fratura e tempo para falha) de cerâmicas à base de dissilicato de lítio (LD) e zircônia estabilizada com ítria (YSZ). Espécimes de LD (IPS e.max CAD, Ivoclar Vivadent) e YSZ (IPS e.max ZirCAD MO, 3mol% Y2O3, Ivoclar Vivadent) foram obtidos e alocados aleatoriamente em três grupos: testado em ar, em líquido inerte (óleo de parafina) ou em água destilada. O teste de fadiga estática (n= 15) foi realizado usando o teste pistão sobre três esferas, ISO 6872, da seguinte forma: carga inicial 100 N para LD e 300 N para YSZ; tempo de aplicação de carregamento definido para 1 hora para cada etapa de carregamento; tamanho do passo de 50 N para LD e 100 N para YSZ, aplicados sucessivamente até a fratura. Dados de resistência à fadiga estática (MPa) e tempo até a fratura (horas) foram registrados. A análise fractográfica foi executada. A análise de sobrevivência corrobora a ausência de influência do ambiente de teste nos resultados de fadiga estática (resistência à fadiga, tempo de fratura e taxas de sobrevivência) para a YSZ. Para LD, os corpos de prova testados em ar apresentaram taxa de sobrevivência e resistência à fadiga estática estatisticamente superiores (p= 0,025). Em relação ao tempo de fratura, os espécimes LD testados em ar foram superiores aos testados em água destilada (p= 0,019) ou em ambiente inerte (p= 0,017). Não foram observadas diferenças estatísticas para o módulo de Weibull. Todas as falhas começaram no lado onde se concentra a tensão de tração (lado de baixo) durante o teste. Com base nisso, observa-se que o ambiente de teste não afetou os mecanismos de crescimento lento de trinca durante o teste de fadiga estática da cerâmica YSZ, mas desempenha um papel significativo na resistência à fadiga estática da cerâmica de vidro à base de dissilicato de lítio, indicando alta susceptibilidade ao crescimento lento e subcrítico de trincas.

Objective: To evaluate the fatigue failure load, number of cycles until failure, and survival probability of adhesively cemented materials with different microstructures (glass-, hybrid- and resin-ceramic) used to manufacture CAD/CAM monolithic restorations. Methods: Disc-shaped specimens (n = 15; Ø = 10 mm; thickness = 1.0 mm) were produced from CAD/CAM blocks as follows: feldspathic (FEL); leucite (LEU); lithium disilicate (LD); zirconia-reinforced lithium silicate (ZRLS); polymer-infiltrated ceramic network (PICN); and resin nanoceramic (RNC). Adhesive cementation was performed onto epoxy discs (dentin analogue- Ø = 10 mm; thickness = 2.5 mm). The cemented assemblies were subjected to fatigue testing using a step–stress approach (400 N–2200 N; step-size of 200 N; 10,000 cycles per step; 1.4 Hz). Fatigue data were analyzed using Kaplan–Meier and Mantel–Cox (log-rank) tests (p < 0.05) and Weibull statistical analysis. Fractographic analysis was also performed. Results: All RNC specimens survived the fatigue test (100% probability of survival at 2200 N; 100,000 cycles) and presented occlusal deformation in response to loading, while all other tested materials failed in distinct loading steps with radial cracks starting from the bonding surface. LD (1146.7 N; 47,333) and ZRLS (1013.3 N; 40,666) materials obtained the highest fatigue failure loads and cycles until failure, meanwhile all PICN specimens failed during the first step (0% probability of survival at 400 N; 10,000). FEL had similar Weibull modulus to LD and ZRLS and higher than LEU for both load and number of cycles outcomes. Significance: The microstructure of adhesively cemented glass-, hybrid- and resin-ceramic CAD/CAM restorative materials influence their response during fatigue testing, which aids in suggesting the best clinical indications.

The purpose of this study was to investigate whether different surface treatments, executed before and after the sintering process, affect the surface characteristics (roughness and morphology) and shear bond strength of computer-aided design–computer-aided manufacturing (CAD–CAM) milled zirconia luted with self-adhesive resin cement onto human dentin. Sixty-four rectangular zirconia slabs (6 × 8.5 × 2.3 mm thickness) were prepared using the CAD–CAM system and randomly distributed into two groups according to the moment of treatment, before and after sintering, and four subgroups according to the surface treatment (n = 8): C (untreated; control), AO (aluminum oxide air abrasion), GB (glass beads air abrasion), and HA (etching with hydrofluoric acid). The samples were evaluated using a confocal laser microscope to assess the surface roughness and morphology. For the shear bond strength test, the milled zirconia was cemented onto dentin slabs using self-adhesive resin cement and submitted to the test in a universal testing machine. Data were submitted to a two-way ANOVA and Tukey test (p

The aim of the study was to evaluate the effect of a ceramic primer and its increased passive application on the fatigue performance of adhesively cemented lithium disilicate simplified restorations. Ceramic discs (Ø = 10 mm; thickness = 1.0 mm) were submitted to an in-lab simulation of CAD/CAM milling and allocated into 8 groups (n = 15), considering 2 factors: “surface treatment”– PRIMER, only coupling agent application (Monobond N); HF5+PRIMER, 5% hydrofluoric acid and coupling agent; E&P 20s + 40s and E&P 20s+5min, ceramic etching/priming (Monobond Etch & Prime, E&P) for 20 s of active application followed by 40 s or 5 min of passive application, respectively; and “aging condition”– baseline, storage for 24 h to 5 days; aged, storage for 90 days +12,000 thermal cycles. Adhesive cementation (Multilink N) was performed onto epoxy discs (Ø = 10 mm; thickness = 2 mm) and the cemented assemblies were subjected to step-stress fatigue tests (initial load of 200 N; step-size of 50 N; 10,000 cycles per step; 20 Hz). The results showed that the groups had similar fatigue performance in the baseline condition (except for E&P 20s+5min: 940.0 N; 123,000 cycles > PRIMER: 786.7 N; 92,333 cycles). When aged, the PRIMER group presented the worst fatigue performance (480.8 N; 31,154 cycles) compared to the other groups (810.0–840.0 N; 97,000–103,000 cycles). In addition, only the PRIMER treatment showed unstable fatigue performance (baseline > aged). Therefore, ceramic surface treatment promoting micromechanical interlocking and chemical bonds is mandatory for stable fatigue performance of adhesively cemented lithium disilicate restorations. The one-step ceramic primer/conditioner promoted similar fatigue performance to the 5% hydrofluoric acid + coupling agent, but increased E&P etching time did not improve the fatigue behavior.

Background The aims of this study were to assess whether the previous registration of a systematic review (SR) is associated with the improvement of the quality of the report of SRs and whether SR registration reduced outcome reporting bias. Methods We performed a search in PubMed for SRs in dentistry indexed in 2017. Data related to SR registration and reporting characteristics were extracted. We analyzed if the reporting of 21 characteristics of included SRs was associated with the prospective registration of protocols or reporting of a previously established protocol. The association between prospective registering of protocols, reporting of funding and number of included studies versus outcome reporting bias was tested via multivariable logistic regression. Results We included 495 SRs. One hundred and 62 (32.7%) SRs reported registering the SR protocol or working from a previously established protocol. Thirteen reporting characteristics were described statistically significant in SRs registered versus SRs that were not. Publication bias assessment and Report the number of participants showed the highest effects favoring the register (RR 1.59, CI 95% 1.19–2.12; RR 1.58, CI 95% 1.31–1.92 respectively). Moreover, Registration was not significantly linked with the articles’ reporting statistical significance (OR 0.96, CI 95% 0.49–1.90). Conclusion There is a positive influence of previously registering a protocol in the final report quality of SRs in dentistry. However, we did not observe an association between protocol registration and reduction in outcome reporting bias.

This study investigated the effect of zirconia surface treatment (air-abrasion with aluminum oxide or tribochemical silica coating) and aging on the fatigue behavior of thin monolithic Y-TZP (yttria-stabilized tetragonal zirconia polycrystal) restorations cemented with 2 types of resin cements, containing or not containing MDP, to a dentin-like substrate. Y-TZP ceramic (Zenostar T, diameter (O) 10 mm, 0.7 mm thick) and dentin-like discs (O 10 mm, 2.8 mm thick) were assigned into eight groups according to three factors: ‘zirconia surface treatment’ (aluminum oxide particles air-abrasion ‘AO’; or tribochemical silica coating via silica-coated aluminum trioxide particles air-abrasion + silanization ‘SC’); ‘MDP-containing resin cement’ (with: Panavia F2.0, ‘MDP’; or without: Multilink Automix, ‘nMDP’); and ‘aging’ (baseline; or aged - 'AG':12,000 thermal cycles + 60 days water storage). Y-TZP intaglio surface was conditioned and dentin-like substrate was etched with hydrofluoric acid prior to bonding. Aging was performed in half of the specimens before the fatigue testing (Staircase, 20 Hz; 250,000 cycles). Fractographic and topographic characteristics were analyzed by stereomicroscope and SEM. Prior to aging, no significant difference was found between the two surface treatments, irrespective to the cement. Samples bonded with resin cement containing MDP had a significant reduction in their fatigue failure load when Y-TZP was air-abraded with aluminum oxide particles and subjected to aging (MDP-AO = 2050.71A; MDP-AO/AG = 1756.67B). Other studied conditions were not affected by aging. Topographic images revealed a rougher surface for aluminum oxide air-abrasion. Fractography supports all failures as a radial crack starting at the Y-TZP intaglio surface. Bonded thin simplified Y-TZP restorations had a high load-bearing capacity, regardless of the studied factors. The MDP-containing resin cement applied on aluminum oxide air-abraded zirconia surface was not enough to maintain the fatigue performance after aging, while higher stability to aging was achieved by treating with the tribochemical silica coating method. When using MDP-free resin cement, the surface treatment and the aging did not impact the fatigue performance.

Made available in DSpace on 2019-08-28T18:55:35Z (GMT). No. of bitstreams: 0 Previous issue date: 2019 This study evaluated the effect of the CAD/CAM burs experience (newer vs older as consequence of the milling sequence) on fatigue failure load (FFL), number of cycles for failure (CFF), and survival rates of lithium disilicate glass-ceramic simplified restorations adhesively cemented to a dentin analogue substrate. Three sets of CAD/CAM burs were used to mill disc-shaped ceramic specimens (1 bur set - 18 milled discs with 10 mm diameter and 1.5 mm thickness), considering the bur experience as a result of the milling sequence to compose the study groups: G1-6 - discs obtained from the 1st to 6th milling of each bur set; G7-12 - specimens from the 7th to 12th milling; G13-18 - discs from the 13th to 18th. Discs of dentin analogue (G10, 10 mm diameter and 2.0 mm thickness) were made to serve as substrate (base material) and randomly assigned into pairs with the respective ceramic discs. Then, the ceramic discs were adhesively cemented onto the dentin analogue substrate, composing a three-layer specimen that mimics a monolithic restoration of a posterior tooth. Specimens were tested under stepwise fatigue approach: frequency = 20 Hz, 5000 cycles at maximum load of 400 N to accommodate the testing assembly, followed by incremental steps of 200 N with initial load ranging from 10 to 1000 N, to a maximum of 20,000 cycles/each step, until the occurrence of failure (radial crack). FFL and CFF were recorded at the end of the testing and subjected to statistical analysis. Supplementary roughness analysis of the milled surface was performed (n = 18) using a contact profilometer. Residual stress after milling and acid etching were accessed via X-ray Diffractometry analysis. FFL and CFF were not affected by increase on bur experience (no statistical differences among groups), despite that, it affected both Ra and Rz parameters (G1-6 had the smoothest surface). The residual stress concentration was negligible (milling did not induce residual stress concentration). It is concluded that the fatigue behavior of adhesively cemented lithium-disilicate glass-ceramic restorations was not influenced by CAD/CAM bur experience (newer vs older as consequence of the milling sequence), and so the residual stress concentration induced by milling was negligible. [de Andrade, Guilherme Schmitt; Diniz, Vandeberg; Datte, Carlos Eduardo; Bottino, Marco Antonio; de Melo, Renata Marques] Sao Paulo State Univ Unesp, Inst Sci & Technol, Dept Dent Mat & Prosthodont, Sao Jose Dos Campos, Brazil [Venturini, Andressa Bonin; Valandro, Luiz Felipe] Fed Univ Santa Maria UFSM, Fac Odontol, Prosthodont Unit, Oral Sci, Floriano Peixoto 1184, BR-97015372 Santa Maria, RS, Brazil [Rocha Pereira, Gabriel Kalil] Merid Fac IMED, Sch Dent, Passo Fundo, RS, Brazil [Amaral, Marina] Universidade de Taubaté (Unitau) , Dept Dent Prosthet Dent [Bastos Campos, Tiago Moreira] Aeronaut Technol Inst ITA, Dept Phys, Sao Jose Dos Campos, Brazil

This study evaluated the effect of different protocols of low-temperature degradation simulation on the mechanical behavior (structural reliability and flexural strength), the surface topography (roughness), and phase transformation of a Y-TZP ceramic. Disc-shaped specimens (1.2 mm×12 mm, Lava Frame, 3M ESPE, Seefeld, Germany) were manufactured according to ISO:6872-2008 and divided (n=30) according to the aging protocol executed: “Ctrl” – as-sintered – without any treatment; “Dist Water” – stored at distilled water at 37 °C for 365 days; “MC” mechanical cycling into two steps: First – 200 N, 2.2 Hz for 2.000.000 cycles, Second – 450 N, 10 Hz for 1.000.000 cycles; “Aut” – steam autoclave at 134 °C, 2 bar (200 kPa) for 20 h; “Aut+MC”– Aut and MC methods. Roughness analysis (μm) showed, for Ra parameter, higher statistically significant values for Ctrl 0.68 (0.27), while for Rz parameter, the highest values were observed for Ctrl 4.43(1.53) and Aut 2.24 (0.62). Surface topography analysis showed that none aging method promoted surface alterations when compared to control group. Phase transformation analysis showed that all aging methods promoted an increase in m-phase content (Ctrl: 0.94%, Dist Water: 20.73%, MC: 9.47%, Aut: 53.33% and Aut+MC: 61.91%). Weibull Analysis showed higher statistical characteristic strength values for Aut (1033.36 MPa) and Dist Water (1053.76 MPa). No aging method promoted deleterious impact either on the biaxial flexural strengths or on the structural reliabilities (Weibull moduli). Also, none of the aging methods promoted reduction of Y-TZP mechanical properties; thus the development of new methodologies and the association between mechanical stimuli and hydrothermal degradation should be considered to better understand the mechanism of low-temperature degradation.

Considering the interest of the research community in the fatigue behavior of all-ceramic restorations and the time consumed in low-frequency cyclic fatigue tests, this study aimed to investigate the influence of the loading frequency on the zirconia fatigue strength. The biaxial flexural fatigue strength of Y-TZP discs was determined by the staircase approach after 500,000 cycles. The investigated frequencies were 2 Hz (control-simulation of the chewing activity; n=20), 10 Hz (n=20), 20 Hz (n=20), and 40 Hz (n=21). The fatigue strength data were analyzed using one-way ANOVA and post-hoc Tukey׳s test (α=0.05). Pearson coefficient (r) was calculated to assess the existence of a correlation between fatigue strength and loading frequency. X-ray diffraction analysis was used to determine the relative amount of monoclinic phase under each fatigue test condition. The fatigue strength was significantly higher for 40 Hz group (630.7±62.1 MPa) and did not differ among the groups 2 Hz (550.3±89.7 MPa), 10 Hz (574.0±47 MPa) and 20 Hz (605.1±30.7 MPa). Pearson correlation coefficient indicated a significantly moderate correlation (r=0.57) between fatigue strength and loading frequency. The percentage of monoclinic phase was similar among the groups. Therefore, the use of loading frequencies up to 20 Hz seems a good alternative to expedite the cycling strength fatigue tests in polycrystalline ceramics without significantly changing the fatigue behavior showed by zirconia in tests employing the frequency of the masticatory cycle.

This study characterized the mechanical properties (static and under fatigue), the crystalline microstructure (monoclinic - m, tetragonal - t and cubic - c phase contents) and the surface topography of three yttrium-stabilized zirconia (YSZ) materials with different translucent properties, before and after aging in an autoclave (low temperature degradation). Disc-shaped specimens were produced from second generation (Katana ML/HT – high-translucent) and third generations (Katana STML – super-translucent and UTML – ultra-translucent) YSZ ceramics (Kuraray Noritake Dental Inc.), following ISO 6872–2015 guidelines for biaxial flexural strength testing (final dimensions: 15 mm in diameter and 1.2 ± 0.2 mm in thickness), and then subjected to the respective tests and analyses. ML was mainly composed of tetragonal crystals, while STML and UTML presented cubic content. Aging increased the monoclinic content for ML and did not affect STML and UTML. Topographical analysis highlights different grain sizes on the ceramic surface (UTML > STML > ML) and aging had no effect on this outcome. Weibull analysis showed the highest characteristic strength for ML both before and after aging, and statistically similar Weibull moduli for all groups. ML material also obtained the highest survival rates (ML > STML > UTML) for both fatigue strength and number of cycles to failure. All fractures originated from surface defects on the tensile side. Third generation zirconia (Katana STML and UTML) are fully stabilized materials (with tetragonal and cubic crystals), being totally inert to the autoclave aging, and presented lower mechanical properties than the second-generation zirconia (Katana ML - metastable zirconia).

Objective To evaluate the effect of restorative strategy (fiber post vs cast post and core), coronal height (0 mm vs 2 mm) and thickness (higher than 1 mm vs lower than 1 mm) on survival rate, fracture resistance and stress distribution. Material and Methods Seventy-two bovine teeth were cleaned and allocated in six groups (n = 12). Twenty-four teeth were sectioned at 13 mm length (no remaining coronal structure) and forty-eight were sectioned at 15 mm (2 mm remaining coronal structure). Half of the forty-eight had remaining coronal thickness lower than 1 mm and the other half had thickness higher than 1 mm. All root canals were prepared at 10 mm (luting length), fiber posts were cemented in thirty-six specimens and cast post and core in other thirty-six. All teeth were restored with metallic crowns. Specimens were submitted to 1.5 million cycles (100 N, 45°, 10 Hz at 2 mm below incisal edge) and evaluated at each 500,000 cycles to detect failures. Specimens that survived were submitted to load to fracture test. Bidimensional (Rhinoceros® 4.0) models were obteined survival data submitted to Kaplan-Meier (α=0.05) analysis and load to fracture values submitted to ANOVA and Tukey tests (α=0.05). Results Groups without remaining coronal structure showed survival rates lower than other groups (p=0.001). ANOVA showed higher values of load to fracture for groups with coronal thickness higher than 1 mm (p=0.0043). Finite element analysis showed better stress distribution in groups with remaining coronal structure and restored with fiber post. Conclusion Specimens without remaining coronal structure have lower survival rates. Specimens with remaining structure lower than 1 mm and without coronal structure support the same load to fracture value independently of the restorative strategy.

This study aimed to investigate the effect of grinding and multi-stimuli aging on the fatigue strength, surface topography and the phase transformation of Y-TZP ceramic. Discs were manufactured according to ISO-6872:2008 for biaxial flexure testing (diameter: 15 mm; thickness: 1.2 mm) and randomly assigned considering two factors “grinding” and “aging”: C- control (as-sintered); CA- control + aging; G- ground; GA- ground + aging. Grinding was carried out with coarse diamond burs under water-cooling. Aging protocols consisted of: autoclave (134°C, 2 bars pressure, 20 hours), followed by storage for 365 days (samples were kept untouched at room temperature), and by mechanical cycling (106 cycles by 20 Hz under a load of 50% from the biaxial flexure monotonic tests). Flexural fatigue strengths (20,000 cycles; 6 Hz) were determined under sinusoidal cyclic loading using staircase approach. Additionally, surface topography analysis by FE-SEM and phase transformation analysis by X-ray Diffractometry were performed. Dixon and Mood methodology was used to analyze the fatigue strength data. Grinding promotes alterations of topographical pattern, while aging apparently did not alter it. Grinding triggered t-m phase transformation without impacting the fatigue strength of the Y-TZP ceramic; and aging promoted an intense t-m transformation that resulted in a toughening mechanism leading to higher fatigue strength for as-sintered condition, and a tendency of increase for ground condition (C < CA; G = GA). It concludes that grinding and aging procedures did not affect deleteriously the fatigue strength of the evaluated Y-TZP ceramic, although, it promotes surface topography alterations, except to aging, and t-m phase transformation. Resumo Este estudo objetivou investigar o efeito do desgaste e envelhecimento (estímulos combinados) na resistência à fadiga, topografia superficial e transformação de fase de uma cerâmica Y-TZP. Discos para teste de flexão biaxial foram confeccionados segundo as normas da ISO-6872:2008 (15 mm Ø; 1,2 mm espessura) e randomicamente distribuídos de acordo com os fatores “desgaste” e “envelhecimento”: C- controle (sinterizado); CA- controle envelhecido; G- desgaste; GA- desgaste envelhecido. O desgaste foi feito com pontas diamantadas de granulação grossa sob irrigação com água. Os protocolos de envelhecimento consistiram em: autoclave (134°C, 2 bar de pressão, 20 horas), 365 dias armazenados em temperatura ambiente, e ciclagem mecânica (106 ciclos a 20 Hz em um intervalo de carga de até 50% da carga monotônica observada em testes estáticos). A resistência à fadiga foi determinada para 20.000 ciclos à 6 Hz sob carregamento sinusoidal através do método de escada. Adicionalmente, análises de topografia superficial em microscopia eletrônica de varredura e de transformação de fase por difração de raios-X foram executadas. A metodologia de Dixon e Mood foi usada para analisar os dados de resistência à fadiga. Foi observado que o desgaste promove uma alteração de padrão topográfico superficial; enquanto o envelhecimento aparentemente não demonstra influência. Em relação à transformação de fase e resistência à fadiga, o desgaste desencadeou um aumento de fase m sem impactar na resistência à fadiga da cerâmica Y-TZP; já o envelhecimento promoveu uma intensa transformação de fase, resultando no mecanismo de tenacificação, que gerou um aumento na resistência à fadiga para a condição sinterizada e uma tendência a aumento na condição desgaste (C < CA; G = GA). Os dados elucidam que o desgaste e o envelhecimento não impactaram negativamente na resistência à fadiga da cerâmica Y-TZP, apesar de promoverem alterações de topografia superficial e intensa transformação de fase de t-m respectivamente.

Objective This study investigated the influence of hydrofluoric acid (HF) etching at different concentrations on the fatigue failure load of adhesively cemented feldspathic ceramic discs (Vita Mark II). Besides, their effect on the micromorphology of ceramic surface was investigated. Methods Eighty ceramic discs (ϕ = 10 mm; thickness = 1.5 mm) were cemented to epoxy supporting discs (ϕ = 10 mm; thickness = 2.0 mm) using different surface conditioning methods (n = 20): nonetched control (CTRL), or etched for 60 s with different HF concentrations: 1% (HF1), 5% (HF5), or 10% (HF10). All the ceramic discs received a silane application (Monobond Plus). The epoxy discs were etched with 10% HF for 60 s and received a primer coating (Multilink Primer A + B). Adhesively cementation was performed (Multilink Automix), and the assemblies (ceramic discs/epoxy discs) were subjected to cyclic loads in water by a staircase approach (500,000 cycles; 20 Hz; initial load = 290 N; step size = 30 N). Fatigue failure load data were analyzed using 1-way ANOVA and post-hoc Tukey’s tests (α = .05). Results Mean failure load of the HF5 group (255.0 ± 23.0 N) was significantly lower; HF1 group (301.7 ± 71.0 N) presented intermediate values, and the highest values were achieved in CTRL (351.7 ± 13.4 N) and HF10 (341.7 ± 20.6 N) groups. All the failures were radial cracks starting from the bonding surface. Significance In terms of fatigue failure load, etching with 1% and 5% HF had a deleterious effect on the fatigue behavior of an adhesively cemented feldspathic ceramic, while 10% HF had no negative influence.

This study investigated the effect of etching with distinct hydrofluoric (HF) acid concentrations on the cyclic load-to-failure (CLf) of simplified lithium disilicate glass-ceramic restorations adhesively cemented to a dentin analogue (n = 20): non-etched/control (CTRL), or etched for 20 s with HF acid at 3% (HF3), 5% (HF5), or 10% (HF10). A silane coating was then applied onto the ceramic surfaces. Fatigue tests followed the staircase approach (initial load= 720 N; step-size= 70 N; 500,000 cycles per sample; 20 Hz) using a hemispheric stainless-steel piston (O= 40 mm) under water. The CLf data were analyzed using Dixon and Mood method. Topographic and fractographic analyses were conducted. CLf (in N) of HF3 (1355 ± 32.0) and HF5 (1335 ± 58.8) groups were the highest and statistically similar; HF10 presented intermediate CLf (1175 ± 132.9), while the non-etched group had the lowest one (965 ± 145.0). Topographical analysis showed that the higher the HF acid concentration, the more pronounced the topographical changes. All failures (radial cracks) started from the inner surface of the ceramic discs. Topographical changes promoted by intermediate HF acid concentrations (3% and 5%) may improve fatigue performance for adhesively-cemented lithium disilicate restorations.

Objectives To evaluate the effects of the etching with different hydrofluoric acid (HF) concentrations on the cyclic load-to-failure ( C L f ) of machined lithium disilicate crowns cemented to dentin analogue material. Methods Pairs of dentin analogue prosthetic preparations and lithium disilicate ceramic crowns with simplified and standardized designs were machined (n = 18). The preparations were etched with 10% HF (60 s), followed by primer application. The intaglio surface of the ceramic crowns was treated as follows: non-etched (control, CTRL); or etched for 20 s with different HF concentrations — 3% (HF3), or 5% (HF5), or 10% (HF10). A silane coating was then applied onto the treated ceramic surfaces, and they were adhesively cemented to the preparations. To perform the fatigue tests (staircase approach), a hemispheric stainless-steel piston (O = 40 mm) applied cyclic loads in the center of the crowns under water (initial load: 720 N; step-size: 70 N; cycles: 500,000; frequency: 20 Hz). Additionally, topographic, fractographic, and fractal analyses were carried out. The fatigue data were analyzed using the Dixon and Mood method. Results Although the topographic and fractal analyses depicted the action of HF etching altering the superficial complexity and topography, the preponderant topography pattern was established by machining on CAD/CAM. All groups showed similar CLf (in N) (CTRL = 805.00 ± 91.23; HF3 = 781.25 ± 29.87; HF5 = 755.00 ± 154.49; HF10 = 833.75 ± 100.74). Significance Etching with different HF acid concentrations did not promote a deleterious effect on the cyclic load-to-failure of machined lithium disilicate crowns.

Objective. To evaluate the effect of internal roughness and bonding on the load to failure and structural reliability (Weibull analysis) of a lithium disilicate-based glass ceramic under different testing scenarios.Methods. IPS e.max CAD blocks (Ivoclar Vivadent AG) were shaped into cylinders (N = 100), crystalized according to the manufacturer’s instructions, and randomly assigned into two surface conditions: (1) polished surface (600-grit SiC polish papers), and (2) a roughened surface (air-abrasion with 50 μm Al2O3). Two assemblies were investigated: a ceramic disc isolated (to isolate the effect of roughness); and a simplified tri-layer setup simulating the restoration of a posterior tooth (ceramic + cement + epoxy resin) to evaluated the influence of bonding isolated and the associated effect of both factors. Four different scenarios were tested: (1) isolated disc under static load (n = 10); (2) disc bonded to an epoxy resin substrate and tested under a static load (n = 10); (3) disc bonded and tested under fatigue (n = 20); and (4) simulated-bonding tested statically (n = 10). The data of load to failure were submitted to One-way ANOVA and Weibull analysis.Results. At a non-bonded scenario (isolated disc and simulated-bonding) a polished internal surface presented a higher characteristic strength. However, when bonding was present this difference became inexistent. No difference was found in terms of structural reliability (Weibull moduli) among the groups. FEA analysis shows that with bonding the tensile stress is better distributed, while in a non-bonded scenario higher tensile stresses occur at the bonding interface.Significance. A rough internal surface impacted deleteriously the mechanical properties of lithium disilicate ceramic when it was not properly bonded to the substrate. However, bonding to the substrate appeared to play a more significant role in the fracture resistance than internal roughness.

Made available in DSpace on 2018-12-11T17:23:42Z (GMT). No. of bitstreams: 0 Previous issue date: 2017-11-06. Added 1 bitstream(s) on 2019-10-09T18:32:04Z : No. of bitstreams: 1 S1806-83242017000100268.pdf: 897134 bytes, checksum: aa9f6ef096c103a85927936c96121b2d (MD5) Monolithic restorations of Y-TZP have been recommended as a restorative alternative on prosthetic dentistry as it allows a substantial reduction of ceramic thickness, which means a greater preservation of tooth structure. However, the influence of grinding and aging when using a thinner layer of the material is unclear. This investigation aimed to evaluate and compare the effects of ceramic thickness (0.5 mm and 1.0 mm), grinding and aging (low-temperature degradation) on the mechanical behavior and surface characteristics of a full-contour Y-TZP ceramic. Y-TZP disc-shaped specimens (15 mm diameter) were manufactured with both thicknesses and randomly assigned into 4 groups considering the factors 'grinding with diamond bur' and 'aging in autoclave'. Surface topography (roughness, 3D profilometry and SEM), phase transformation, flexural strength and structural reliability (Weibull) analyses were executed. Grinding affected the surface topography, while aging did not promote any effect. An increase in m-phase content was observed after grinding and aging, although different susceptibilities were observed. Regardless of zirconia's thickness, no deleterious effect of grinding or aging on the mechanical properties was observed. Thus, in our testing assembly, reducing the thickness of the Y-TZP ceramic did not alter its response to grinding and low temperature degradation and did not impair its mechanical performance. Universidade Estadual Paulista - Unesp, Dental School, Prosthodontics Units, São José dos Campos, SP, Brazil Universidade Federal de Santa Maria - UFSM, Faculty of Odontology, Prosthodontics Units, Santa Maria, RS, Brazil

Made available in DSpace on 2018-11-26T17:20:59Z (GMT). No. of bitstreams: 0 Previous issue date: 2017-04-01 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) United States National Institute of Dental & Craniofacial Research, National Institutes of Health Objective. This study evaluated the effects of two grading techniques of zirconia material on the fatigue limit of full-contour 3-unit fixed dental prostheses (FDPs). Methods. Presintered blocks of 3Y-TZP were milled to obtain sixty-nine 3-unit FDPs, which were divided into three groups (n = 23). The control group (CTL) was sintered and glazed following manufacturer's instructions. In the two experimental groups presintered FDPs received a surface silica/glass infiltration treatment before the sintering process. Silica sol-gel group (SSG) was graded by the sol-gel processing route, while the glass-zirconiaglass group (GZG) was graded by an enameling technique. Graded groups did not receive a glaze layer after sintering. All FDPs were then luted with a dual-curing resin cement on composite abutments, embedded in polyurethane and stored in water for five days. The initial load of the fatigue test was calculated based on the results of the monotonic testing applied on three specimens of each group. To determine the fatigue limit, 20 samples of each group were subjected to staircase testing (100,000 cycles/5 Hz). Results. The fatigue limits (in Newtons) were CTL= 1607.27, SSG = 1824.31, and GZG= 2006.57, and the Dixon and Mood test indicated statistically significant differences among groups (95% confidence interval) (GZG > SSG > CTL). Significance. The infiltration of silica and glass on bulk zirconia, by two different grading methods, increased the fatigue limits of monolithic zirconia FDPs. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved. Sao Paulo State Univ, Sch Dent, Restorat Dent, Prosthet Dent Unit, Av Eng Franscisco Jose Longo,777, BR-12245 Sao Jose Dos Campos, SP, Brazil Univ Fed Santa Maria, Oral Sci, Prosthet Dent Unit, R Floriano Peixoto,1184, BR-97015 Santa Maria, RS, Brazil Technol Inst Aeronaut, Dept Phys, Sao Jose Dos Campos, SP, Brazil New York Univ Coll Dent, Dept Biomat & Biomimet, New York, NY 10010 USA Univ Fed Santa Maria, Fac Odontol, MDS PhD Grad Program Oral Sci, Prosthodont Unit, R Floriano Peixoto,1184, BR-97015 Santa Maria, RS, Brazil Sao Paulo State Univ, Sch Dent, Restorat Dent, Prosthet Dent Unit, Av Eng Franscisco Jose Longo,777, BR-12245 Sao Jose Dos Campos, SP, Brazil United States National Institute of Dental & Craniofacial Research, National Institutes of Health: 2R01 DE017925

The aim of this study was to systematically review the literature to assess the effect of grinding on the mechanical properties, structural stability and superficial characteristics of Y-TZP ceramics. The MEDLINE via PubMed and Web of Science (ISI – Web of Knowledge) electronic databases were searched with included peer-reviewed publications in English language and with no publication year limit. From 342 potentially eligible studies, 73 were selected for full-text analysis, 30 were included in the systematic review with 20 considered in the meta-analysis. Two reviewers independently selected the studies, extracted the data, and assessed the risk of bias. Statistical analyses were performed using RevMan 5.1, with random effects model, at a significance level of 0.05. A descriptive analysis considering phase transformation, Y-TZP grain size, Vickers hardness, residual stress and aging of all included studies were executed. Four outcomes were considered in the meta-analyses (factor: grinding x as-sintered) in global and subgroups analyses (grinding tool, grit-size and cooling) for flexural strength and roughness (Ra) data. A significant difference (p

Made available in DSpace on 2019-09-12T16:53:37Z (GMT). No. of bitstreams: 0 Previous issue date: 2016 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) NUFFIC (Netherlands Organization for International Cooperation in Higher Education, The Netherlands) agency (Grants CAPES/NUFFIC) [056/14] The following study aimed to evaluate the effect of grinding and low-temperature aging on the fatigue limit of Y-TZP ceramics for frameworks and monolithic restorations. Disc specimens from each ceramic material, Lava Frame (3M ESPE) and Zirlux FC (Ivoclar Vivadent) were manufactured according to ISO:6872-2008 and assigned in accordance with two factors: (1) "surface treatment"-without treatment (as-sintered, Ctrl), grinding with coarse diamond bur (181 mu m; Grinding); and (2) "low-temperature aging (LTD)" - presence and absence. Grinding was performed using a contra-angle handpiece under constant water-cooling. LTD was simulated in an autoclave at 134 degrees C under 2-bar pressure for 20 h. Mean flexural fatigue limits (20,000 cycles) were determined under sinusoidal loading using stair case approach. For Lava ceramic, it was observed a statistical increase after grinding procedure and different behavior after LTD stimuli (Ctrl

Several rotary instruments have been daily employed on clinic to promote cut aiming to adjust the length of fiber posts to the radicular conduct, but there is no information on the literature about the effects of the different rotary instruments and its impact on the micromorphology of surface and mechanical properties of the glass fiber post. This study aimed the impact of rotary instruments upon fiber-matrix integrity, micromorphology and flexural-strength of glass-fiber posts (GFP). GFP (N=110) were divided into 5 groups: Ctrl: as-received posts, DBc: coarse diamond-bur, DBff: extra-fine diamond-bur, CB: carbide-bur, DD: diamond-disc. Cutting procedures were performed under abundant irrigation. Posts exposed to rotary instruments were then subjected to 2-point inclined loading test (compression 45°) (n=10/group) and 3-point flexural-strength test (n=10/group). Fiber-matrix integrity and micromorphology at the cut surface were analyzed using a SEM (n=2/group). Cutting procedures did not significantly affect the 2-point (51.7±4.3-56.7±5.1 MPa) (p=0.0233) and 3-point flexural-strength (671.5±35.3-709.1±33.1 MPa) (p=0.0968) of the posts (One-way ANOVA and Tukey׳s test). Fiber detachment was observed only at the end point of the cut at the margins of the post. Cut surfaces of the CB group were smoother than those of the other groups. After 3-point flexural strength test, fiber-matrix separation was evident at the tensile side of the post. Rotary instruments tested with simultaneous water-cooling did not affect the resistance of the tested fiber posts but caused disintegration of the fibers from the matrix at the end of the cut, located at the margins.

Made available in DSpace on 2015-10-22T06:28:45Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-05-01 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) This study evaluated the effects of low-temperature aging on the surface topography, phase transformation, biaxial flexural strength, and structural reliability of a ground Y-TZP ceramic. Disc-shaped specimens were manufactured and divided according to two factors: "grinding" - without grinding (as-sintered, Ctrl), grinding with an extra-fine diamond bur (25 mu m Xfine) and coarse diamond bur (181 mu m Coarse); and "low-temperature-aging" (absence or presence). Grinding was performed using a contra-angle handpiece under water-cooling. Aging was performed in an autoclave at 134 degrees C, under 2 bar, over a period of 20 h. Surface topography analysis showed an increase in roughness based on grit-size (Coarse>Xfine>Ctrl), and aging promoted different effects on roughness (Ctrl AgCoarse). Grinding and aging promoted an increase in the amount of m-phase, although different susceptibilities to degradation were observed. Weibull analysis showed an increase in characteristic strength after grinding (Coarse=Xfine>Ctrl); however, distinct effects were observed for aging (CtrlCoarse Ag). Weibull moduli were statistically similar. Grinding promoted an increase in characteristic strength as a result of an increase in m-phase content; when the Y-TZP surface was ground by coarse diamond burs followed by aging, characteristic strength was reduced, meaning the low-temperature degradation appeared to intensify for rougher Y-TZP surfaces. Copyright (C) 2014 Elsevier Ltd. All rights reserved. Univ Fed Santa Maria, Fac Odontol, PhD Grad Program Oral Sci, Prosthodont Unit, BR-97119900 Santa Maria, RS, Brazil Sao Paulo State Univ UNESP, Inst Sci &Technol, Fac Odontol, Sao Jose Dos Campos, Brazil Univ Sao Paulo, Fac Odontol, Dept Biomat &Oral Biol, BR-09500900 Sao Paulo, Brazil Indiana Univ, Sch Dent, Dept Restorat Dent, Div Dent Biomat, Indianapolis, IN USA Univ Amsterdam, Dept Dent Mat Sci ACTA, Amsterdam, Netherlands Vrije Univ Amsterdam, Amsterdam, Netherlands Univ Fed Santa Maria, Fac Odontol, MSD PhD Grad Programs Oral Sci, Prosthodont Unit, BR-97119900 Santa Maria, RS, Brazil Sao Paulo State Univ UNESP, Inst Sci &Technol, Fac Odontol, Sao Jose Dos Campos, Brazil