Multilayer coatings provide an effective measure to control and optimise of residual stresses, enhance coating adhesion, fracture toughness, wear and corrosion resistance of coating system. In this study, we designed and produced bi-layer and four-layer titanium/titanium nitride magnetron sputtered coating configurations by altering the position of the interlayer. The in-plane residual stresses in different coating configurations are measured by multiple peak grazing incidence X-ray diffraction techniques. Subsequently, the effect of different compressive residual stresses on adhesion, mechanical properties, wear and corrosion resistance of coatings are investigated. Results show that the position of interlayer in multilayer coating configuration has a great impact on relaxation of residual stresses. The residual stresses are relieved by 26% and 46% by lowering the position of titanium interlayer from 800 nm at the top to 1000 nm and 1200 nm, respectively. The nanoindentation hardness is decreased by 11% and 13%, respectively. The wear rate of multilayer coating having interlayer position at 800 and 1000 nm from the top is ≈ 23% lower compared to bilayer however it is increased by ≈ 50% when interlayer coatings position changed to 1200 nm from the top. The interposition of interlayer in multilayer coating configurations decreased the corrosion current density by ≈ 50%. All multilayer coatings including higher residual stresses show better adhesion to the substrate compared to bilayer coatings which shows severe delamination. [ABSTRACT FROM AUTHOR]

The effect of addition of gold (Au) on the structure and mechanical properties of (Fe0.5Co0.5)71Nb4Si5B20 BMG alloy was studied. Addition of Au formed crystals in the BMG alloy. Gradual increase in the amount of Au added to the BMG alloy resulted in an increase in the amount of crystallinity and hardness of the alloy. Hardness values in excess of 1100 HV were found in all the alloys with a maximum value of 1245 HV. The thermal transition temperatures were also found to increase with an increasing amount of Au. Corner cracks were produced in the alloy with 1.5 at.-% Au content showing a low indentation fracture toughness value of 2.98 MPa-m0.5. [ABSTRACT FROM AUTHOR]