Mixed transition-metals oxide electrocatalysts have shown huge potential for electrochemical water oxidation due to their earth abundance, low cost and excellent electrocatalytic activity. Here we present Co–Fe–B–O coatings as oxygen evolution catalyst synthesized by Pulsed Laser Deposition (PLD) which provided flexibility to investigate the effect of morphology and structural transformation on the catalytic activity. As an unusual behaviour, nanomorphology of 3D-urchin-like particles assembled with crystallized CoFe2O4 nanowires, acquiring high surface area, displayed inferior performance as compared to core–shell particles with partially crystalline shell containing boron. The best electrochemical activity towards water oxidation in alkaline medium with an overpotential of 315 mV at 10 mA/cm2 along with a Tafel slope of 31.5 mV/dec was recorded with core–shell particle morphology. Systematic comparison with control samples highlighted the role of all the elements, with Co being the active element, boron prevents the complete oxidation of Co to form Co3+ active species (CoOOH), while Fe assists in reducing Co3+ to Co2+ so that these species are regenerated in the successive cycles. Thorough observation of results also indicates that the activity of the active sites play a dominating role in determining the performance of the electrocatalyst over the number of adsorption sites. The synthesized Co–Fe–B–O coatings displayed good stability and recyclability thereby showcasing potential for industrial applications. [ABSTRACT FROM AUTHOR]

A porous coating assembled with hierarchical 3D Co 3 O 4 urchin-like particles was synthesized by Pulsed Laser Deposition (PLD) and thermal oxidation. Laser ablation of Co B powder, used as the target material, in oxygen atmosphere formed core–shell particles on the coating surface with mainly a metallic Co core and a mixture of Co, B and O accommodating the shell. The thermal oxidation of these core–shell particles in air at 600 °C induces the morphological transformation to urchin-like particles consisting of nanowires (NWs) (diameter: 30–60 nm and length 1–3 μm) grown radially from the core surface. The extrusion marks on the surface of NWs indicate that the stress induced growth process is caused by difference in the thermal expansion coefficient. XRD, Raman, EXAFS and HRTEM analysis confirmed that the NWs are polycrystalline consisting of pure Co 3 O 4 phase. A wet-chemistry hydrothermal procedure was also employed to synthesize nanostructured urchin-like particles which are hollow and the structure is held together by the radially oriented nanorods (diameter: 40–150 nm). During photocatalysis, urchin-like particles synthesized by PLD displayed significantly higher (∼5 times) degradation rates when compared to chemical urchins for degradation of methylene blue dye via a photo-Fenton reaction in presence of H 2 O 2 and visible light. This is mainly attributed to poor stability of the nanorods in the chemical urchin structure. Features such as high surface area, enhanced stability against agglomeration, polycrystalline nature of the NWs, porous surface and superior adhesion, are responsible for the enhanced photocatalytic activity of Co 3 O 4 urchin-like particles assembled in a porous coating synthesized by PLD and thermal oxidation. Reusability tests also demonstrate the robust nature of the catalyst coating. [ABSTRACT FROM AUTHOR]

Ruthenium nanoparticles (NPs) supported over carbon thin films (Ru/C thin films) catalysts were synthesized by pulsed laser deposition and used as catalysts for hydrolysis of ammonia borane (AB). Highly irregular and porous carbon films with high surface area were deposited by varying Ar gas pressures during the deposition. By taking the advantage of phase explosion phenomena, occurring at high laser fluence, the surface of the carbon films were decorated with crystalline Ru NPs with size below ∼10 nm. Ru/C thin film catalyst produced H 2 with 6 times higher H 2 generation rate as compared to unsupported Ru NPs assembled film, and with a high turnover frequency value of 70.5 mol H 2 mol −1 Ru min −1 . A combination of morphological features and high content of sp 2 bonded C atoms provides good dispersion of Ru NPs over a large surface area. Both these features contribute in generating large number of active sites leading to the increase in catalytic efficiency. A possibility of using the present form of catalyst as an ON/OFF switch for H 2 production was also tested. Although the catalytic activity decreased with the number of hydrolysis cycles, Ru/C thin film catalyst was able to generate the expected amount of H 2 gas in each cycle when it was reused several times. The observed low activation energy (∼28 kJ mol −1 ) and high H 2 generation rate (15.5 L H 2 min −1 g −1 of Ru) by hydrolysis of AB suggest that Ru/C thin film catalyst is highly efficient. [ABSTRACT FROM AUTHOR]

Highlights: [•] Co3O4 NPs assembled coatings were synthesized using pulsed laser deposition. [•] Co3O4 coating, synthesized at 3J/cm2, exhibited the best catalytic activity to degrade Methylene blue dye. [•] Co3O4 nanocatalyst showed above 90% conversion efficiency of CO to CO2 at 250°C with very high specific rate. [ABSTRACT FROM AUTHOR]

Abstract: Nano-particle (NP) catalysts are under intense investigation in the nanotechnology community because of their large surface-to-volume atomic ratio, size- and shape-dependent properties, and high concentration of low-coordinated active surface sites. However, there is no general strategy to synthesize NPs, possibly in one step, of various materials with tailored properties and desired morphologies. In this work, cobalt oxide NPs assembled coatings have been prepared by reactive pulsed laser deposition of Co in O2 atmosphere. Three different deposition parameters have been varied to investigate their relevance in tailoring composition and structure of the synthesized NPs: 1) the target–substrate distance, 2) the oxygen pressure in deposition chamber, and 3) post oxidation of NPs deposited in vacuum condition. It is proved that by appropriate selection of the deposition parameters, several NP types may be obtained in one single step, namely: Co3O4 or CoO NPs, Co–Co3O4 or Co–CoO core shell NPs, with size ranging from a few nm to several tens of nm. Transmission and Scanning Electron Microscopy as well as Raman Spectroscopy have been utilized to carefully investigate the compositional and structural features of the NPs. A correlation is made between final NP properties and laser-induced processes mainly related to phase explosion generating liquid droplets that cool during flight or on the substrate. Photocatalytic properties of this heterogeneous Co3O4 NPs-assembled coating catalyst for degradation of methylene blue solution under light irradiation are assessed and compared to that of homogenous catalyst producing Co2+ ions in methylene blue solution. [Copyright &y& Elsevier]

Abstract: Nanoparticles (NPs) catalysts are under intense investigation in the catalysis community due to their exceptional activity and selective nature in catalytic processes as compared to the corresponding bulk counterpart, especially because of their large surface-to-volume atomic ratio, size- and shape-dependent properties, and high concentration of low-coordinated active surface sites. However, there is no general strategy to synthesize NPs of various materials with narrow size distribution, tailored properties, and desired morphologies. The development of a technique able to prepare NPs is thus a goal of great importance to avoid present trial and error approaches. Here we report on selected examples where pulsed laser deposition (PLD) technique greatly contributes toward NPs synthesis. Co NPs embedded in B matrix films have been synthesized by PLD technique by taking advantage of the phase explosion process of superheated liquid where a mixture of vapor and liquid droplets leave the irradiated target surface and get deposited on the substrate. The deposited NPs exhibit catalytic properties comparable to that of precious metals in hydrogen production by hydrolysis of NaBH4 and NH3BH3. These NPs, when supported on rough carbon film prepared by PLD, show about 30% increase in catalytic activity for H2 production as compared to unsupported NPs. Co3O4 NPs assembled coating has been produced by reactive PLD in oxygen atmosphere at various substrate temperatures from room temperature to 250°C. It was proved that the Co3O4 NPs can be obtained in a single step at low temperatures with mixed disordered-nanocrystalline phase that is a relevant feature for catalysis. The Co3O4 NPs assembled thin coating, employed in degradation of methylene blue solution, in water, via photo Fenton reaction in presence of H2O2, exhibits significantly higher activity as compared to the corresponding homogeneous catalyst. [Copyright &y& Elsevier]

Abstract: Co3O4 nanoparticles assembled coatings have been synthesized by physical (pulsed laser deposition (PLD) and electron beam deposition) and chemical (sol–gel and electroless) techniques. The morphological, structural, and optical properties of all the coatings were analyzed by SEM, XRD, Raman spectroscopy, XPS, and UV–vis spectroscopy. The catalytic activities of the several Co3O4 heterogeneous catalyst coatings have been compared by looking at their efficiency on degradation of methylene blue dye that occurs via photo Fenton reaction in presence of H2O2 or oxone oxidants. The coating synthesized by PLD exhibits the best photo-degradation rate of dye in presence of H2O2 (4h) or oxone (8min). The NPs produced by PLD process exhibit smaller average size (18nm), narrow size distribution (σ =3nm), perfect spherical shape, low degree of agglomeration, and mixed amorphous-nanocrystalline phase. These special features of NPs, along with better visible light absorption, are the main factors responsible for the enhanced photocatalytic activity of the PLD Co3O4 NPs assembled coating. It is also observed that although the concentration of oxone (0.5mM) was very small as compared to H2O2 (100mM) the photo-degradation of MB dye solution is much faster for oxone. [Copyright &y& Elsevier]

Ba[(Mg0.32Co0.02)Nb0.66]O3 [BMCN] thin films prepared on Pt-Si, MgO, Silicon and ITO coated glass substrates by Pulsed Laser Deposition Technique are investigated. Relative growth parameters suggest that ITO coated glass substrate has good potential for growing films with near Nano size columnar grains. In comparison to bulk, dielectric constant and dielectric loss increases in BMCN films. This undesirable rise in dielectric loss can be drastically reduced by a factor of more than 1/100th times through Ag15+ ion irradiation at 1 × 1012 ions/cm2 dose. [ABSTRACT FROM AUTHOR]

Abstract: Cobalt oxide (Co3O4) nanoparticles (NPs) assembled coating have been prepared by reactive pulsed laser deposition of Co, in O2 atmosphere, on Si or glass substrate ranging from room temperature to 250°C. The NPs, having narrow size distribution with average values of around 25–50nm, were characterized by Raman, X-ray diffraction, X-ray photoelectron spectroscopy, and scanning electron microscopy. The Co3O4 NPs synthesized at 150°C comprise a mixed amorphous–nanocrystalline phase (that is unique property for catalysis) while complete crystallization of Co3O4 occurs at 250°C with formation of spinel structure. Photocatalytic properties of Co3O4 NPs assembled coating for degradation of methylene blue solution under visible light irradiation are reported. The effect of H2O2 concentration and effect of pH variation on dye degradation rate has been reported. The reusability of the Co3O4 NPs assembled thin coating catalyst was further evaluated in several recycling runs. The activity of heterogeneous Co3O4 NPs assembled thin coating catalyst was compared with homogenous catalyst producing Co+2 ions in methylene blue solution. [Copyright &y& Elsevier]

Abstract: Thin films of Carbon-supported Co–B nanoparticles were synthesized by using Pulsed Laser Deposition (PLD) and used as catalysts in the hydrolysis of Ammonia Borane (AB) to produce molecular hydrogen. Amorphous Co–B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for nanoparticles-assembled Co–B film catalysts preparation through PLD. Various Ar pressures (10–50 Pa) were used during deposition of carbon films to obtain extremely irregular and porous carbon support with high surface area prior to Co–B film deposition. Surface morphology of the catalyst films was studied using Scanning Electron Microscopy, while structural characterization was carried out using X-Ray diffraction. The hydrogen generation rate attained by carbon-supported Co–B catalyst film is significantly higher as compared to unsupported Co–B film and conventional Co–B powder. Almost complete conversion (95%) of AB was obtained at room temperature by using present film catalyst. Morphological analysis showed that the Co–B nanoparticles produced after the laser ablation process act as active catalytic centers for hydrolysis while the carbon support provides high initial surface area for the Co–B nanoparticles with better dispersion and tolerance against aggregation. The efficient nature of our carbon-supported Co–B film is well supported by the obtained very low activation energy (∼29 kJ (mol)−1) and exceptionally high H2 generation rate (13.5 L H2 min−1 (g of Co)−1) by the hydrolysis of AB. [Copyright &y& Elsevier]

Abstract: Co-B nanoparticles supported over carbon films were synthesized by using pulsed laser deposition (PLD) and used as catalysts in the hydrolysis of sodium borohydride (NaBH4) to produce molecular hydrogen. Amorphous Co-B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for nanoparticles-assembled Co-B film catalysts preparation through PLD. Various Ar pressures (10–50Pa) were used during deposition of carbon films to obtain extremely irregular and porous-carbon support with high surface area prior to Co-B film deposition. Surface morphology of the catalyst films was studied using scanning and transmission electron microscopy, while structural characterizations were carried out using X-ray diffraction. The hydrogen generation rate attained by carbon-supported Co-B catalyst film is significantly higher as compared to unsupported Co-B film and to conventional Co-B powder. Morphological analysis along with NaBH4 hydrolysis tests showed that the Co-B nanoparticles produced with PLD act as active catalytic centers for hydrolysis while the carbon support provides high initial surface area for the Co-B nanoparticles with better dispersion and tolerance against aggregation. The hydrogen generation rate obtained by the present catalyst film was also investigated as a function of Co-B loading, carbon morphology, and solution temperature. The high performance of our carbon-supported Co-B film is well supported by the obtained very low activation energy (∼31kJ (mol)−1) and exceptionally high H2 generation rate (8.1LH2 min−1 (gofcatalyst)−1) in the hydrolysis of NaBH4. [Copyright &y& Elsevier]

Abstract: Co–P–B catalyst thin films have been synthesized on Ni-foam and glass substrate by using electroless deposition (ED) and pulsed laser deposition (PLD) respectively. The efficiency of these catalyst films was tested by catalytic hydrolysis of NaBH4 for H2 generation. While the chemically produced Co–P–B film on Ni-foam shows similar activity as that of their corresponding powder, the Co–P–B film deposited by PLD exhibits much superior H2 generation rate as compared to Co–P–B powder. We attribute this increased efficiency to the special features of the Co–P–B films which are in the form of nanoparticle-assembled films, a peculiar characteristic of PLD films for appropriate choice of the pulse laser parameters. The surface nanoparticle-configuration increases the active surface area and also favors electronic exchange mechanisms to promote hydrolysis process for H2 gas generation. The films deposited by using laser energy density of 3J/cm2 show the highest activity in connection to the best configuration of the ablated nanoparticles. Different numbers of Co–P–B layers were deposited on Ni-foam by ED and it was found that at least four layers are required for complete coverage of the foam to have the best activity. [Copyright &y& Elsevier]

Abstract: Nanoparticle-assembled Co-B thin films were synthesized by Pulsed Laser Deposition (PLD) and used as catalysts for the hydrolysis of NH3BH3 (ammonia borane, AB) to produce molecular hydrogen. Amorphous Co-B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for Co-B thin film catalysts preparation through PLD. Surface morphology of Co-B powder and film catalyst was studied using Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Compositional and structural characterizations were carried out using X-photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) techniques, respectively. The efficiency of both powder and film catalysts was tested by comparative kinetic analysis of the AB hydrolysis for hydrogen production. It was observed that nanoparticles produced during the laser ablation process act as active catalytic centers to produce significantly higher rate (about 6 times) of H2 than the same amount of the corresponding Co-B powders. Almost complete conversion (95%) of AB was obtained, as confirmed by 11B NMR, by using Co-B films at room temperature. Active Co-B nanoparticles on the surface of the PLD-deposited films is able to decrease the activation energy, for hydrolysis of AB, to the very low value of 34kJmol−1. We also found that by adding small amount of NaBH4 to the NH3BH3 solution increases the efficiency of the Co-B catalyst films, thus generating H2 with higher rate. Maximum H2 generation rate of about ∼8.2LH2 min−1 (g of Co)−1 and ∼13LH2 min−1 (g of Co)−1 was measured by hydrolysis of AB and mixture of (AB+NaBH4) solutions, respectively. [Copyright &y& Elsevier]

Abstract: Carbon-supported palladium thin films were synthesized at room temperature by KrF excimer pulsed laser deposition by using oriented pyrolytic graphite and Pd target. By changing the experimental conditions, a range of structures, from smooth to porous cluster-assembled carbon films were obtained prior to deposition of the Pd films. High amount of sp2 coordinated graphitic carbon embedded with large degree of disorder is observed in these carbon films. Surface morphology was studied by using scanning electron microscopy, while compositional analysis was performed by using energy dispersive spectroscopy. Structural analysis was performed using Raman spectroscopy and Fourier transform infrared spectroscopy. The importance of morphology and chemical structure of carbon films on their catalytic activity was investigated by using the hydrolysis of aqueous NaBH4 as a reference process. Pd/C film produced by pulsed laser deposition are here demonstrated to be a better catalyst than Pd/C powder because of the high content of sp2 bonding carbon atoms arranged into the porous and irregular surface of the carbon film. [Copyright &y& Elsevier]

Abstract: Hydrogen generation by catalytic hydrolysis of sodium borohydride (NaBH4) is studied by using Co–B-based thin film catalyst synthesized by pulsed laser deposition (PLD) technique. Co–B nanoparticles, produced in the catalyst film after the laser ablation process, act as active centers producing significantly higher H2 generation rate than Co–B bulk powder. Surface morphology was studied by using scanning electron microscopy and compositional analysis was established by using X-photoelectron and infrared spectroscopies. Films were deposited at different PLD set-up parameters in order to understand the possible role of size and density of the nanoparticles in the catalytic process. Cobalt has been found here to act as an efficient catalyst only when alloyed with boron which partially prevents cobalt oxidation. In particular we report that when used as suitable thin films, Co–B produces H2 with a maximum generation rate of about 3300ml/min per gram of catalyst. [Copyright &y& Elsevier]

The ablation of a target, composed of a homogeneous mixture of Fe & Co metal with H 3 BO 3 powder, produces core-shell type particles on the as-deposited coating surface. Annealing at 600 °C in air transforms the core-shell into urchin-like particles having nanowires of 10–30 nm in diameter and 0.5–1 μm in length, grown radially from the particle surface as a result of the stress created between core and shell. Microstructural and analytical characterization confirms that nanowires are composed of CoFe 2 O 4 and CoO phases forming a heterojunction, which showed outstanding performance as a photocatalyst, requiring half the time for an organic water pollutant degradation reaction in comparison to similarly nanostructured single-metal oxide counterparts (Co 3 O 4 and Fe 2 O 3). Degradation reactions conducted in controlled conditions demonstrate that the urchin-like mixed oxide coatings are highly efficient both in direct photocatalysis and in photo-Fenton reaction. This overall enhancement in activity is due to a synergistic effect created at the heterojunction of CoFe 2 O 4 /CoO that allows the formation of a Z -scheme mechanism to facilitate the spatial separation of photoinduced electron-hole pairs. Moreover, the hierarchical urchin-like nanostructures provide a large number of active sites for photocatalytic reactions, while the lower band gap of CoFe 2 O 4 permits better visible light absorption to effectively degrade organic pollutants even under visible light. Based on all the results, a plausible reaction mechanism is proposed related to Z -scheme heterojunction formed with CoFe 2 O 4 /CoO. Unlabelled Image • A coating of urchin-like nanostructured CoFe 2 O 4 /CoO heterojunction is synthesized by PLD. • Implementation of a Z-scheme design greatly improves charge separation. • Hierarchical nanostructuring provides large number of active sites for photocatalytic reactions. • The coating shows outstanding photocatalytic activity towards a model pollutant. [ABSTRACT FROM AUTHOR]

Nanoparticles assembled Co-B-O thin film catalysts were synthesized by pulsed laser deposition (PLD) technique for hydrolysis of Sodium Borohydride (SBH). Surface morphology of the deposited films was investigated using SEM and TEM, while compositional analysis was studied using XPS. Structural properties of Co-B-O films were examined using XRD and HRTEM. Laser process is able to produce well separated and immobilized Co-B-O NPs on the film surface which act as active centers leading to superior catalytic activity producing hydrogen at a significantly higher rate as compared to bulk powder. Co-B-O thin film catalyst produces hydrogen at a maximum rate of ∼4400 ml min −1 g −1 of catalyst, which is four times higher than powder catalyst. PLD parameters such as laser fluence and substrate-target distance were varied during deposition in order to understand the role of size and density of the immobilized Co-B-O NPs in the catalytic process. Films deposited at 3–5 cm substrate-target distance showed better performance than that deposited at 6 cm, mainly on account of the higher density of active Co-B-O NPs on the films surface. Features such as high particle density, polycrystalline nature of Co NPs and good stability against agglomeration mainly contribute towards the superior catalytic activity of Co-B-O films deposited by PLD. [ABSTRACT FROM AUTHOR]

Nanocatalysts, in the form of nanoparticles assembled coatings (NPACs) of Co 3 O 4 , were synthesized by pulsed laser deposition (PLD) with optimized parameters. Phase explosion phenomena occurring at high laser fluences produce nanoparticles (NPs) with an average size of ∼5 nm having narrow size distribution (3–10 nm) and low degree of agglomeration, which are randomly arranged in the form of coating on the substrate surface. In comparison with chemically synthesized Co 3 O 4 crystalline powder, the NPACs deposited by PLD showed significantly higher catalytic activity for H 2 generation by hydrolysis of NaBH 4 . Maximum H 2 generation rate obtained by NPACs (5010 ml min −1 g cat −1 ) is about 5 times higher than that produced by Co 3 O 4 powder (1000 ml min −1 g cat −1 ), which is mainly attributed to high surface area and large number of active sites provided by the Co 3 O 4 NPs in the coating owing to their size and shape. By varying the O 2 pressure during PLD, two different cobalt oxide phases, namely Co 3 O 4 and CoO, were formed in NPACs and found that Co 3 O 4 phase is more active for hydrolysis than CoO phase with lower oxidation number. The morphology and crystallinity of Co 3 O 4 NPACs were tuned by varying the laser fluence and substrate temperature respectively, and their effect on H 2 generation rate was studied. The results showed that the NPs with mixed amorphous-nanocrystalline phase on the surface act as active sites for favorable interaction and NaBH 4 conversion. [ABSTRACT FROM AUTHOR]

Abstract: The influence of substrate temperature, process gas, deposition pressure, and substrate type on the phase selection, orientation/epitaxy, and growth morphology of thin films in the SrNbO y (y≈3.0 or 3.5) family was investigated. Pulsed laser deposited films (from a Sr2Nb2O7 target) obtained in both oxygen and nitrogen atmospheres upon various substrates were characterized with X-ray diffraction, energy dispersive spectroscopy, atomic force microscopy, and transmission electron microscopy. In oxygen atmospheres, films adopted the (110)-layered perovskite structure of the target. Higher temperatures, lower pressures of oxygen, and use of (110)-oriented SrTiO3 substrates lead to highly crystalline, epitaxial films of Sr2Nb2O7. The use of nitrogen atmospheres resulted in cubic perovskite SrNbO3 formation: epitaxial, textured, or polycrystalline films were obtained depending on the substrate; no nitrogen incorporation could be observed on the anion sublattice. On SrTiO3, the cubic perovskite films followed a cube-on-cube epitaxy and planar defects were observed to occur on the (110) perovskite planes. [Copyright &y& Elsevier]