Search

The subject of this paper is the analysis of the influence of laser cutting of oak wood on its drying process. The subject of the research was the comparison of the drying process and the quality of the dried wood in samples cut by classical technology (sawing) and samples cut with the use of laser. The research was carried out on two sets of samples which were subjected to an identical drying process. Continuous moisture loss and final moisture attained, moisture gradients before and after drying, and internal tensions before and after drying were monitored by means of the fork test and the cut-test. The final moisture content at the end of drying was 8.09% for the saw-cut samples and 8.22% for the laser-cut samples, a difference of only 0.13%. The analysis of the individual characteristics observed showed that the influence of the cutting technology did not have a significant effect on the drying process or the quality of the dried oak sawn timber. [ABSTRACT FROM AUTHOR]

The mechanical properties of wood have remarkable influence on its use in buildings. The improvement of the mechanical properties enables the reduction in the cross-sections of structural elements, particularly the increase in their load. The paper deals with the change in the mechanical properties of beech wood through the process of contact drying. Plate pressures of 1.0, 1.4, and 1.6 MPa at a temperature of 160 °C were used. It was found that contact drying increased the bending strength by more than 30% compared to convection drying. The value of Brinell's hardness measured on the surface of the samples increased by 80 to 98% after contact drying, and the measured values of impact toughness were higher, about 31.1% compared to the samples dried by the convection drying method. As a result of contact drying, the density in the absolutely dry state increased for radial samples by 102.3 kg·m−3 and for tangential samples by 83.1 kg·m−3. The pressure of the plates also had an effect on the change in density. [ABSTRACT FROM AUTHOR]

In wood processing, wood is exposed to an environmental temperature of less than 0 °C for some time, which mainly occurs during the air drying of wood in the winter months, or when lumber is stored in wood piles outdoors before the kiln drying process. In these cases, the wood freezing process increases the degree of freezing of the wood, subsequently significantly affecting the process of its heating during further processing (for example, in the cutting process). The most common method is heating by humid air, during the hot air drying of wood. We analyzed the temperature profiles on a cross-section of wood and moisture losses due to the freezing process and the size of moisture gradients. We compared theoretical calculations of the time required for defrosting and heating of wood with the experimentally measured values. The results show that the moisture content (MC) of wood has a remarkable effect on the wood freezing process. In samples with an average MC of 35.47%, the temperature drop was faster. After 10 h, the temperatures on the entire cross-section of the samples reached the lowest value of −13.2 °C. In samples with an average initial MC of 81.38%, three stages of temperature reduction in the wood were observed. The temperature dropped and the lowest temperature of −20.11 °C was reached after 24 h. The defrosting and heating process of samples with lower MC was significantly easier. The desired temperature of 65 °C in the middle of the samples was reached in 2 h and 20 min. The total time to defrost and heat the second group of samples (MC > FSP) was 3 h 30 min. [ABSTRACT FROM AUTHOR]

Beech wood has a high frequency of defects such as red heartwood, reaction wood (tension wood). For the experimental measurements four logs without visible defects like red heartwood, which can noticeably affects the measurements' results were qualified. The drying medium temperature in the first phase of the process before the moisture content of the specimens fell below the FSP was maintained at 45 °C. Then, the temperature was gradually increased to the maximum value 65 °C. The results showed that different initial wood moisture content does not affect to final value of tension and normal wood. The colorimetric parameter L* was much higher for tension wood. After steaming, there were greater differences in the colorimetric parameters, respectively, a* and b*. After drying the difference of all colorimetric parameters between tension and normal wood was significantly less. The color changes were only noticed in the surface layers of specimens. Differences were small, and thus, the impact of the tension wood on the color changes was not confirmed. However, since the lightness of tension wood plays a key role for its visual detection, it may be adequate to only measure the lightness parameter (L*). [ABSTRACT FROM AUTHOR]

This study examined the changes in the properties of beech wood (Fagus sylvatica L.) after intense drying. Beech wood with false red heartwood was selected as the test specimen. The test samples had dimensions of 50 mm thickness, 180 mm width, and 350 mm length. The specimens were divided into two groups, false red heartwood and sapwood. These specimens were selected with different angles of the growth rings (radial and tangential). The results showed that samples with red heartwood, in comparison to samples with sapwood content, had a remarkable effect in covering. Observation of specimens with false red heartwood and sapwood before and after drying process revealed significant differences in color changes and measured values during the covering-slicing test, but not between samples with different growth ring angles. [ABSTRACT FROM AUTHOR]