This study deals with combustion behavior of B 2 O 3 /Mg/NH 4 Cl/C complex systems for the synthesis of amorphous boron (B), boron carbide (B 4 C), and boron nitride (BN) nanostructures. The raw mixtures used in the experiments were prepared on the base of a B 2 O 3 –Mg precursor mixture, which is sufficiently exothermic to maintain a self-propagating regime of the combustion reaction. Thermodynamic analysis of the combustion temperatures and experimental validation indicate that the 1000–1500 °C temperature range is very effective for synthesizing the nanostructures of B, B 4 C, and BN. It was found that B-containing functional nanostructures are mainly spherical nanoparticles (B) or nanosheets (B 4 C, BN). The phase composition and microstructural characteristics of the final products were evaluated based on the combustion temperature and solid/liquid phase changes. [ABSTRACT FROM AUTHOR]

We have investigated a thermally induced combustion route for preparing 2D hexagonal BN nanoplates from B 2 O 3 +(3+0.5 k )Mg+ k NH 4 Cl solid system, for k =1–4 interval. Temperature–time profiles recorded by thermocouples indicated the existence of two sequential exothermic processes in the combustion wave leading to the BN nanoplates formation. The resulting BN nanoplates were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy, PL spectrometry, and Brunauer–Emmett–Teller surface area analysis. It was found that B 2 O 3 was converted into BN completely (by XRD) at 1450–1930 °C within tens of seconds in a single-step synthesis process. The BN prepared at a k =1–4 interval comprised well-shaped nanoplates with an average edge length ranging from 50 nm to several micrometer and thickness from 5 to 100 nm. The specific surface area of BN nanoplates was 13.7 g/m 2 for k =2 and 28.4 m 2 /g for k =4. [ABSTRACT FROM AUTHOR]