1. Effect of YAG content on creep resistance and mechanical properties of Al2O3-YAG composite.
- Author
-
Bučevac, Dušan, Omerašević, Mia, Egelja, Adela, Radovanović, Željko, Kljajević, Ljiljana, Nenadović, Snežana, and Krstić, Vladimir
- Subjects
- *
YTTRIUM aluminum garnet , *SELF-propagating high-temperature synthesis , *FRACTURE toughness , *FRACTURE strength , *ALUMINUM nitrate , *ELASTIC modulus - Abstract
Comprehensive study on effect of YAG amount on densification, creep resistance and room-temperature mechanical properties of Al 2 O 3 -YAG composite pressureless sintered at 1600 °C was conducted. The main goal was to optimize the amount of YAG in order to fabricate a composite with improved creep resistance and sufficiently good room-temperature mechanical properties. The composite was made by mixing a commercially available Al 2 O 3 powder with fine YAG powder obtained by glycine-nitrate combustion synthesis starting from aluminum nitrate and yttrium nitrate. Increased driving force for sintering of fine YAG powder allowed fabrication of dense Al 2 O 3 -YAG composite with up to 30 vol% YAG. The presence of YAG was found to be very effective in improving creep resistance of Al 2 O 3 -YAG composite. Large Y3+ ions blocked diffusion along Al 2 O 3 grain boundaries, reduced diffusivity and therefore enhanced creep resistance of Al 2 O 3 -YAG composite which continuously increased as the YAG amount increased. Тhe presence of YAG was also found to improve mechanical properties such as hardness and elastic modulus. The improvement of these properties was ascribed to increased density of Al 2 O 3 -YAG composites owing to high sintering activity of YAG powder. While fracture strength of the composite can be as high as that of monolithic Al 2 O 3 , fracture toughness of composite decreased continuously as the YAG content increased. The decrease was ascribed to transgranular fracture of both YAG and Al 2 O 3 grains in samples containing larger amounts of YAG. The proper balance between fracture toughness and creep resistance was found in composite containing 18 vol% YAG which had considerably improved creep resistance accompanied by a relatively small decrease in fracture toughness. [ABSTRACT FROM AUTHOR]
- Published
- 2020
- Full Text
- View/download PDF