Search

Hot compression experiments of a Ti55511 titanium alloy are conducted to study the phase transformation characteristics and dynamic recrystallization (DRX) behavior. It is found that the fraction of α phase decreases with increasing the strain rate or deformation amount. Meanwhile, the original lamellar α phases easily transform into the spheroidal and bulk α phases at larger deformation amounts or higher strain rates. Most of α phases disappear and the final microstructures are mainly β phases when the temperature is over 800 °C. The DRX degree rises with raising the deformation amount or decreasing the strain rate. However, the DRX behavior becomes weaken with raising the deformation temperature. α phases are evenly distributed around β phases during hot compressive deformation, which not only restrains the growth of β phases but also promotes the DRX process of β phases. In addition, the geometric DRX takes place within α phases, while the continuous DRX occurs within β phases during the hot compression. Image 1 • Phase transformation and dynamic recrystallization (DRX) behavior of a Ti55511 titanium alloy are studied. • The volume fraction of α phase decreases with increasing the strain rate or deformation degree. • Initial lamellar α phases easily transforms into bulk/spheroidal α phases at the larger strains or higher strain rates. • The α phases not only restrains the growth of β phase, but also promotes the DRX process of β phase. • The geometric DRX takes place within α phases, while the continuous DRX occurs within β phases. [ABSTRACT FROM AUTHOR]

Spheroidization and dynamic recrystallization (DRX) mechanisms of a Ti-55511 alloy during hot compression in α+β region is investigated. It is found that the spheroidization of lamellar α phases and DRX of β phases, which are obviously influenced by deformation conditions, are the main softening mechanisms. The spheroidization fraction of lamellar α phases first increases with the raised temperature or strain rate. However, the spheroidization fraction of lamellar α phases begins to drop at about 700 °C as the strain rate is higher than 0.01 s−1, and the maximum spheroidization fraction of lamellar α phase is about 2.3%. This phenomenon is attributed to the Implanting-Mechanism, which is induced by the common or close orientation relationships of the spheroidized and equiaxed α phases, as well as few dislocations between the spheroidized and equiaxed α phases. Contrarily, the lamellar α phases are obstructed from equiaxed α phases by a mass of dislocations. Additionally, the DRX degree of β phases increases with the reduced temperature or the raised strain rate. • Spheroidization and DRX mechanisms of a Ti-55511 alloy during hot compression in α+β region is investigated. • Spheroidization fraction of lamellar α phase first increases then drops with the raised strain rate. • The maximum spheroidization fraction of lamellar α phase is about 2.3% near 700 °C and 0.01 s−1. • Implanting-Mechanism, induced by the close orientation relationships of spheroidized and equiaxed α phases, is proposed. • The DRX extent of β phases increases with the reduced temperature and raised strain rate. [ABSTRACT FROM AUTHOR]

The hot deformation behavior and microstructural evolution of a Ti-55511 alloy in α+β region are investigated by uniaxial compressive tests at elevated temperatures. Transmission Electron Microscope (TEM) and Electron Backscattered Diffraction (EBSD) are employed to observe the microstructures. The spheroidization of lamellate α phases and the dynamic recrystallization (DRX) of β grains are analyzed. It is observed that the flow characteristics are prominently affected by deformation parameters, i.e., the flow stress, peak stress and flow softening stress decrease with the reduced strain rate or the increased deformation temperature. When the deformation temperature is slightly raised or the strain rate is properly reduced, the fraction of spheroidized α phase greatly increases. The substructures are formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. Then, the lamellate α phase is fragmentized and spheroidized. The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. Additionally, the higher dislocation density and obvious dislocation pile-ups can be noticed at the α/β interface, which induces the DRX nucleation of β grains at the α/β interface. • Hot deformation behavior and microstructure evolution of a Ti-55511 alloy in α+β region are investigated. • The fraction of spheroidized α phase increases with increasing deformation temperature or reducing strain rate. • The substructures are easily formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. • The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. • The obvious DRX of β grains easily nucleate at the α/β interface. [ABSTRACT FROM AUTHOR]