Search

Abstract: Two types of mesoporous Co–B nanocatalysts were prepared by the reduction of cobalt chloride with Sodium Borohydride (SBH) in the presence of cationic and non-ionic surfactant templates, namely n-cetyl-trimethyl-ammonium bromide (CTAB) and Pluronic (P123) respectively. Nitrogen adsorption–desorption isotherms revealed the presence of slit-like pores on the catalyst surface which provide high effective surface area. These surface enhanced catalysts were tested for hydrogen production by hydrolysis of sodium borohydride. The mesoporous Co–B catalysts showed much higher activity (4 times) in comparison to the non-porous Co–B, which can be attributed to the higher surface area of the mesoporous structures. Co–B/P123 catalyst showed the highest hydrogen generation rate owing to the presence of wide uniform pores which facilitated easier interaction of the reactants to release hydrogen. The lack of stability in the pore structure is observed at elevated temperatures for both the mesoporous Co–B catalyst. [Copyright &y& Elsevier]

Abstract: Catalyst in the form of Co-B nanoparticles supported on mesoporous silica particles (MSP) was synthesized by chemical impregnation–reduction method. This catalyst powder was used for hydrogen production by hydrolysis of Ammonia Borane (AB) and was compared with Co-B catalyst supported on non-porous silica particles (NSP) and unsupported Co-B powder. It was found that the MSPs synthesized in the present studies have average pore size of about 3.1nm which were efficient to anchor the Co-B particles with average size of ~8nm on the surface to provide high active surface area and improved degree of dispersion. MSP-supported Co-B catalyst was able to produce expected amount of H2 gas from hydrolysis of AB with significantly superior generation rate, about 3 times higher than that produced by unsupported and NSP-supported Co-B catalyst. Availability of a large number of under-coordinated Co active atoms owing to the size of nanoparticles, better dispersion, high surface area and good stability against agglomeration during the reaction are the main features acquired by the Co-B nanoparticles supported on MSP that exhibit high catalytic efficiency. [Copyright &y& Elsevier]

Abstract: Thin films of Carbon-supported Co–B nanoparticles were synthesized by using Pulsed Laser Deposition (PLD) and used as catalysts in the hydrolysis of Ammonia Borane (AB) to produce molecular hydrogen. Amorphous Co–B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for nanoparticles-assembled Co–B film catalysts preparation through PLD. Various Ar pressures (10–50 Pa) were used during deposition of carbon films to obtain extremely irregular and porous carbon support with high surface area prior to Co–B film deposition. Surface morphology of the catalyst films was studied using Scanning Electron Microscopy, while structural characterization was carried out using X-Ray diffraction. The hydrogen generation rate attained by carbon-supported Co–B catalyst film is significantly higher as compared to unsupported Co–B film and conventional Co–B powder. Almost complete conversion (95%) of AB was obtained at room temperature by using present film catalyst. Morphological analysis showed that the Co–B nanoparticles produced after the laser ablation process act as active catalytic centers for hydrolysis while the carbon support provides high initial surface area for the Co–B nanoparticles with better dispersion and tolerance against aggregation. The efficient nature of our carbon-supported Co–B film is well supported by the obtained very low activation energy (∼29 kJ (mol)−1) and exceptionally high H2 generation rate (13.5 L H2 min−1 (g of Co)−1) by the hydrolysis of AB. [Copyright &y& Elsevier]

Abstract: Co-B nanoparticles supported over carbon films were synthesized by using pulsed laser deposition (PLD) and used as catalysts in the hydrolysis of sodium borohydride (NaBH4) to produce molecular hydrogen. Amorphous Co-B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for nanoparticles-assembled Co-B film catalysts preparation through PLD. Various Ar pressures (10–50Pa) were used during deposition of carbon films to obtain extremely irregular and porous-carbon support with high surface area prior to Co-B film deposition. Surface morphology of the catalyst films was studied using scanning and transmission electron microscopy, while structural characterizations were carried out using X-ray diffraction. The hydrogen generation rate attained by carbon-supported Co-B catalyst film is significantly higher as compared to unsupported Co-B film and to conventional Co-B powder. Morphological analysis along with NaBH4 hydrolysis tests showed that the Co-B nanoparticles produced with PLD act as active catalytic centers for hydrolysis while the carbon support provides high initial surface area for the Co-B nanoparticles with better dispersion and tolerance against aggregation. The hydrogen generation rate obtained by the present catalyst film was also investigated as a function of Co-B loading, carbon morphology, and solution temperature. The high performance of our carbon-supported Co-B film is well supported by the obtained very low activation energy (∼31kJ (mol)−1) and exceptionally high H2 generation rate (8.1LH2 min−1 (gofcatalyst)−1) in the hydrolysis of NaBH4. [Copyright &y& Elsevier]

Abstract: Nanoparticle-assembled Co-B thin films were synthesized by Pulsed Laser Deposition (PLD) and used as catalysts for the hydrolysis of NH3BH3 (ammonia borane, AB) to produce molecular hydrogen. Amorphous Co-B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for Co-B thin film catalysts preparation through PLD. Surface morphology of Co-B powder and film catalyst was studied using Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Compositional and structural characterizations were carried out using X-photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) techniques, respectively. The efficiency of both powder and film catalysts was tested by comparative kinetic analysis of the AB hydrolysis for hydrogen production. It was observed that nanoparticles produced during the laser ablation process act as active catalytic centers to produce significantly higher rate (about 6 times) of H2 than the same amount of the corresponding Co-B powders. Almost complete conversion (95%) of AB was obtained, as confirmed by 11B NMR, by using Co-B films at room temperature. Active Co-B nanoparticles on the surface of the PLD-deposited films is able to decrease the activation energy, for hydrolysis of AB, to the very low value of 34kJmol−1. We also found that by adding small amount of NaBH4 to the NH3BH3 solution increases the efficiency of the Co-B catalyst films, thus generating H2 with higher rate. Maximum H2 generation rate of about ∼8.2LH2 min−1 (g of Co)−1 and ∼13LH2 min−1 (g of Co)−1 was measured by hydrolysis of AB and mixture of (AB+NaBH4) solutions, respectively. [Copyright &y& Elsevier]

Abstract: Hydrogen generation by catalytic hydrolysis of sodium borohydride (NaBH4) is studied by using Co–B-based thin film catalyst synthesized by pulsed laser deposition (PLD) technique. Co–B nanoparticles, produced in the catalyst film after the laser ablation process, act as active centers producing significantly higher H2 generation rate than Co–B bulk powder. Surface morphology was studied by using scanning electron microscopy and compositional analysis was established by using X-photoelectron and infrared spectroscopies. Films were deposited at different PLD set-up parameters in order to understand the possible role of size and density of the nanoparticles in the catalytic process. Cobalt has been found here to act as an efficient catalyst only when alloyed with boron which partially prevents cobalt oxidation. In particular we report that when used as suitable thin films, Co–B produces H2 with a maximum generation rate of about 3300ml/min per gram of catalyst. [Copyright &y& Elsevier]