Search

Abstract: Catalyst in the form of Co-B nanoparticles supported on mesoporous silica particles (MSP) was synthesized by chemical impregnation–reduction method. This catalyst powder was used for hydrogen production by hydrolysis of Ammonia Borane (AB) and was compared with Co-B catalyst supported on non-porous silica particles (NSP) and unsupported Co-B powder. It was found that the MSPs synthesized in the present studies have average pore size of about 3.1nm which were efficient to anchor the Co-B particles with average size of ~8nm on the surface to provide high active surface area and improved degree of dispersion. MSP-supported Co-B catalyst was able to produce expected amount of H2 gas from hydrolysis of AB with significantly superior generation rate, about 3 times higher than that produced by unsupported and NSP-supported Co-B catalyst. Availability of a large number of under-coordinated Co active atoms owing to the size of nanoparticles, better dispersion, high surface area and good stability against agglomeration during the reaction are the main features acquired by the Co-B nanoparticles supported on MSP that exhibit high catalytic efficiency. [Copyright &y& Elsevier]

Abstract: Co-P-B catalyst coatings have been synthesized on Ni-foam by using electroless deposition (ED) and their catalytic activity was investigated by catalytic dehydrogenation of ammonia borane (AB, NH3BH3) for H2 generation. Co-P-B catalyst (both in form of powder and coating) showed superior catalytic activity in hydrolysis reaction of AB than that of Co-B powder, with complete evolution of H2 (97%) at very high rate (2l/min/gcatalyst). This was mainly attributed to synergic effect caused by B and P over Co active sites to lower the activation energy of the process. For thermolysis reaction, it was observed that AB loaded on Co-P-B/Ni catalyst releases first mole of H2 at considerably low temperature starting at 50°C and with desorption peak centered at 80°C. To our knowledge this value is the lowest reported for solid state catalyst. Moreover, the catalytic thermolysis did not present any induction time and minimizes the formation of undesirable byproduct like borazine and ammonia. The present result suggests that Co-P-B coated on Ni is a highly efficient and low cost catalyst and can be used for both hydrolysis as well as thermolysis reaction of NH3BH3 with the important advantage that it can be easily recovered and repeatedly reused. [Copyright &y& Elsevier]

Abstract: Nanoparticle-assembled Co-B thin films were synthesized by Pulsed Laser Deposition (PLD) and used as catalysts for the hydrolysis of NH3BH3 (ammonia borane, AB) to produce molecular hydrogen. Amorphous Co-B-based catalyst powders, produced by chemical reduction of cobalt salts, were used as target material for Co-B thin film catalysts preparation through PLD. Surface morphology of Co-B powder and film catalyst was studied using Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Compositional and structural characterizations were carried out using X-photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) techniques, respectively. The efficiency of both powder and film catalysts was tested by comparative kinetic analysis of the AB hydrolysis for hydrogen production. It was observed that nanoparticles produced during the laser ablation process act as active catalytic centers to produce significantly higher rate (about 6 times) of H2 than the same amount of the corresponding Co-B powders. Almost complete conversion (95%) of AB was obtained, as confirmed by 11B NMR, by using Co-B films at room temperature. Active Co-B nanoparticles on the surface of the PLD-deposited films is able to decrease the activation energy, for hydrolysis of AB, to the very low value of 34kJmol−1. We also found that by adding small amount of NaBH4 to the NH3BH3 solution increases the efficiency of the Co-B catalyst films, thus generating H2 with higher rate. Maximum H2 generation rate of about ∼8.2LH2 min−1 (g of Co)−1 and ∼13LH2 min−1 (g of Co)−1 was measured by hydrolysis of AB and mixture of (AB+NaBH4) solutions, respectively. [Copyright &y& Elsevier]

Abstract: Hydrogen generation by catalytic hydrolysis of sodium borohydride (NaBH4) is studied by using Co–B-based thin film catalyst synthesized by pulsed laser deposition (PLD) technique. Co–B nanoparticles, produced in the catalyst film after the laser ablation process, act as active centers producing significantly higher H2 generation rate than Co–B bulk powder. Surface morphology was studied by using scanning electron microscopy and compositional analysis was established by using X-photoelectron and infrared spectroscopies. Films were deposited at different PLD set-up parameters in order to understand the possible role of size and density of the nanoparticles in the catalytic process. Cobalt has been found here to act as an efficient catalyst only when alloyed with boron which partially prevents cobalt oxidation. In particular we report that when used as suitable thin films, Co–B produces H2 with a maximum generation rate of about 3300ml/min per gram of catalyst. [Copyright &y& Elsevier]