Search

• The model can account for the non-linear lifting of the flange groove and the effects of wheelset traverse and side roll. • The wheel tread and flange are alternately loaded with two wheel load transition areas in the frog area. • Wear in the flange bearing area is significantly higher than in the tread bearing area, with an increase of 59.7%. • RCF damage dominates in the wing rail and the two wheelload transition areas. • Reducing the speed to 15 km/h significantly improves the service performance of the fixed frog. The tram No. 3 turnout fixed frog uses a variation in the depth of the flange groove so that the wheel rolls over the frog area in a continuous flange bearing. This method of travelling over the turnout requires the wheel load to transition back and forth between the tread and the flange, resulting in wheel-rail impact, which in turn affects service life. In order to investigate its service characteristics, this paper has established a transient wheel-rail rolling contact finite element model for the No. 3 turnout fixed frog. The macroscopic dynamic response and microscopic wheel-rail contact solution as the tram passes through the turnout at different axle weights and speeds are analysed in detail, and the changing patterns of wear and fatigue damage are investigated. The research shows that rail wear is particularly severe in the wheel flange bearing area, approximately 1.6 times greater than in the tread bearing area. In addition, when tram speeds are reduced to 15 km/h, there is a significant reduction in wheel-rail impact and wear, thereby improving ride smoothness and safety. The results of this study are of great significance to the operation and maintenance of the No.3 fixed frog turnout. [ABSTRACT FROM AUTHOR]

The presence of fatigue crack is a common damage pattern in railway wheel-rail system, which will reduce service life and increase the maintenance costs of railway transportation. In this study, a two-stage simulation strategy was proposed to investigate the elastic-plastic fatigue crack growth behaviour of the wheel and rail, where a three-dimensional wheel-rail rolling contact finite element model was first built to solve the elastic-plastic wheel-rail contact pressure and tangential traction modification, and then a simplified three-dimensional finite element model of the wheel and rail inserted with vertical cracks under the equivalent moving load was built to explore the fatigue crack growth. Taking the J -integral at the crack tip as an elastic-plastic crack growth parameter, the influences of crack face friction, crack depth and traction coefficient on the crack growth were elucidated. Meanwhile, the competing mechanisms of wheel/rail wear and fatigue crack growth under rolling-sliding contact condition was illuminated based on the Archard wear model. The simulation results indicate that two critical locations for crack growth appear during the contact load approaching and departing from the crack. The Mises stress near the deepest crack tip exceeds the yield stress, causing a small plastic zone with the greatest crack growth rate. The reduction in the crack face friction, and/or the increase in crack depth and traction coefficient will accelerate the propagation of fatigue crack. In the case of only normal contact load or rolling-sliding contact (μ ≤ 0.375), the crack growth on the wheel and rail is dominant compared to wear and crack will continue to grow. • Proposed a two-stage simulation strategy to study wheel-rail fatigue crack growth. • Built 3-D finite element model of the wheel and rail inserted with vertical cracks. • Elucidated influences of key parameters on wheel-rail fatigue crack growth. • Illuminated competing mechanisms of wheel/rail wear and fatigue crack growth. [ABSTRACT FROM AUTHOR]