Search

Both softwood (southern yellow pine) and hardwood (red oak) can be completely dissolved in the ionic liquid 1-ethyl-3-methylimidazolium acetate ([C2mim]OAc) after mild grinding. Complete dissolution was achieved by heating the sample in an oil bath, although wood dissolution can be accelerated by microwave pulses or ultrasound irradiation. It has been shown that [C2mim]OAc is a better solvent for wood than 1-butyl-3-methylimidazolium chloride ([C4mim]Cl) and that variables such as type of wood, initial wood load, particle size, etc.affect dissolution and dissolution rates; for example, red oak dissolves better and faster than southern yellow pine. Carbohydrate-free lignin and cellulose-rich materials can be obtained by using the proper reconstitution solvents (e.g., acetone/water 1 : 1 v/v) and approximately 26.1% and 34.9% reductions of lignin content in the reconstituted cellulose-rich materials (from pine and oak, respectively) have been achieved in one dissolution/reconstitution cycle. The regenerated cellulose-rich materials and lignin fractions were characterized and compared with the original wood samples and biopolymer standards. For pine, 59% of the holocellulose (i.e., the sum of cellulose and hemicellulose) in the original wood can be recovered in the cellulose-rich reconstituted material; whereas 31% and 38% of the original lignin is recovered, respectively, as carbohydrate-free lignin and as carbohydrate-bonded lignin in the cellulose-rich material. [ABSTRACT FROM AUTHOR]

Experiments were conducted to study the effects of reaction conditions on the hydrolysis of miscanthus dissolved in 1-ethyl-3-methylimidazolium chloride ([Emim][Cl]) catalyzed by H2SO4. It was determined that while there is a small co-inhibition effect associated with the simultaneous hydrolysis of the cellulosic and hemicellulosic portions of miscanthus, the largest rate decreases were observed for the hydrolysis of the hemicellulosic portion. This rate decrease was attributed to the chemical linkage between hemicellulose and lignin in miscanthus, which could be broken with chemical pretreatment. While chemical pretreatment increased the rate of the hydrolysis of the hemicellulosic component, delignification showed no further benefit. The rate of hydrolysis was determined to be first order in concentrations of β-1,4 glycosidic linkage and acid, and zero order in water concentration. The activation energy for the hydrolysis of the glycosidic linkages in the cellulosic and hemicellulosic components were determined to be 95 kJ mol−1 and 114 kJ mol−1 respectively. Progressive addition of water during the first hour of the reaction increased conversion and selectivity to saccharine products, while limiting dehydration of the sugars formed. The conversion of the cellulosic portion of miscanthus could be increased after the first hour of the reaction by increasing the reactor temperature. While miscanthus is only partially soluble in [Emim][Cl], it was found that the initial miscanthus loading could be increased to 9 wt% before significant yield decreases attributed to solubility limitations of the cellulosic component were observed. By proper adjustment of reaction conditions, it was possible to achieve yields of sugars approaching 84% from the cellulosic and hemicellulosic components of miscanthus, with minimal dehydration of the sugars to furans. [ABSTRACT FROM AUTHOR]

Lignocellulosic biomass composite fibers (southern yellow pine and bagasse) were successfully prepared directly from the ionic liquid, 1-ethyl-3-methylimidazolium acetate ([C2mim]OAc) with a dry-jet wet spinning process using short dissolution times (10–30 min) and temperatures above the glass transition temperature of lignin. Fibers could not be spun at all from solutions of pine dissolved using previously reported dissolution methods (110 °C, 16 h), while bagasse fibers spun using the higher temperature/shorter time method were stronger than those obtained using the lower temperature/longer time method. [ABSTRACT FROM AUTHOR]