High titanium heavy slag is one kind of solid waste that exists in large amounts in the southwest of China. In this paper, this high titanium heavy slag is used as natural pre-wetted material in concrete because of its porous structure. Three kinds of aggregates are used in this concrete. The first one is natural limestone and river sand. The second one is dry slag fine aggregate and coarse aggregate. The third one is pre-wetted coarse slag aggregate and dry slag fine aggregate. The strength, dry shrinkage, autogenous shrinkage, relative humidity, pore size distribution, stress–strain relationship, micro-hardness and chloride penetration of concrete composed of the above three aggregates are tested in this study. The results show that pre-wetted slag aggregate is a suitable internal curing material. The concrete with pre-wetted slag aggregate shows higher strength, lower shrinkage and smaller porosity. The water absorbed in the slag aggregate can be released effectively to increase the relative humidity, accelerate hydration, improve porosity and increase the interface strength. [ABSTRACT FROM AUTHOR]

Damage to concrete structures with gypsum-contaminated aggregate occurs frequently. Aggregates in much of the southern part of China are contaminated with gypsum. Therefore, in this study, the effects of using different quantities of gypsum-contaminated aggregate on the expansion and compressive strength of concrete were investigated over a period of one year. Two groups of concrete were designed with the gypsum-contaminated aggregate containing different parts of fine and coarse aggregate, respectively. The SO3 contents were 0%, 0.5%, 1%, 1.5%, 3%, 5%, and 7% by weight of aggregate. X-ray diffraction (XRD), thermogravimetry (TG), and differential scanning calorimetry (DSC) were used to analyze the change in mineral composition over time. The microstructure was also studied by scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). The results showed that significant expansion and great loss in compressive strength did not occur in concrete if the content of SO3 lay below 1.5% and 3% in fine and coarse aggregates, respectively. The concentration of sulfate ions in concrete was not enough to form new a phase of gypsum. During the process of internal sulfate attack, the content of gypsum decreased and the content of ettringite increased. Ettringite was the main reason for the expansion damage of concrete. Additionally, the fracture mode of internal sulfate attack on concrete was the crack extension from gypsum to paste; finally, the aggregate separated from the paste. [ABSTRACT FROM AUTHOR]