Search

Laser polishing (LP) provides a fast and efficient way of remelting part surfaces manufactured by additive manufacturing to alter both their geometric as well as physical properties. Depending on the laser parameters, remelted surfaces with different properties are achieved, with a majority exhibiting lower surface roughness compared to the original surface. In this study, a high-power continuous fiber laser is used to polish Inconel 718 (IN718) surfaces produced by depositing a single layer of clads on a steel substrate by the powder-blown directed energy deposition (DED) process. Polishing was performed under different sets of parameters, namely, laser power, beam diameter, feed rate or feed, hatch spacing, and the number of polishing passes. Their effects on the surface roughness profiles and the microstructural properties of the sample cross section were analyzed after one and two polishing passes. Optical microscopic images of the sample's cross sections show the presence of supersaturated γ γ' + γ" phase particles, precipitates, Laves phases, and δ phase needles. The combined effect of high-temperature gradients and lower solidification rates in certain regions within the cross section results in undercooled regions and pseudo-heat treatment of unmelted regions close to the undercooled regions. These results are corroborated by indenting the various regions of the IN718 sample cross section with a pyramidal diamond indenter in the form of a grid, resulting in different micro-hardness values due to different densities of precipitate and phase transformed particles. [ABSTRACT FROM AUTHOR]

The process parameters of Directed Energy Deposition (DED) have been widely studied including laser power, powder flow rate, and scanning speed. These parameters affect clad dimension and melt pool temperature, which are directly related to part quality. However, laser/powder profiles and their alignment have obtained less attention due to the cumbersome characterization process, although they can be directly associated with local energy density for melt pool formation. This study examines the impact of the alignment between the laser beam and powder flow distributions in DED on clad dimension and melt pool temperature. The laser beam and powder profiles are characterized by measuring their respective 2D Gaussian profiles for a given standoff distance. Aligned and misaligned laser-powder profiles are then used to build single-clad square geometries. It was found that a 500-µm offset between the centers of the laser and powder profiles causes up to a 20% change in both the width and the height of a single clad as well as an average temperature increase of 100 K. To understand the interaction between powder flow, energy flux, and local temperature, the local specific energy density distribution was plotted in 2D. These results suggest that laser-powder misalignment may significantly alter the thermal history and shape of deposited clads, possibly preventing DED-manufactured parts from meeting design properties and causing build failures. [ABSTRACT FROM AUTHOR]

The process parameters of Directed Energy Deposition (DED) have been widely studied including laser power, powder flow rate, and scanning speed. These parameters affect clad dimension and melt pool temperature, which are directly related to part quality. However, laser/powder profiles and their alignment have obtained less attention due to the cumbersome characterization process, although they can be directly associated with local energy density for melt pool formation. This study examines the impact of the alignment between the laser beam and powder flow distributions in DED on clad dimension and melt pool temperature. The laser beam and powder profiles are characterized by measuring their respective 2D Gaussian profiles for a given standoff distance. Aligned and misaligned laser-powder profiles are then used to build single-clad square geometries. It was found that a 500-µm offset between the centers of the laser and powder profiles causes up to a 20% change in both the width and the height of a single clad as well as an average temperature increase of 100 K. To understand the interaction between powder flow, energy flux, and local temperature, the local specific energy density distribution was plotted in 2D. These results suggest that laser-powder misalignment may significantly alter the thermal history and shape of deposited clads, possibly preventing DED-manufactured parts from meeting design properties and causing build failures. [ABSTRACT FROM AUTHOR]