Two inorganic scintillator detectors consisting of Yb:YAG scintillators and photomultiplier tubes, and an oscilloscope were used to studied the neutron sensitivities of Yb:YAG scintillators at the China Spallation Neutron Source (CSNS) Back-n white neutron source. The relative neutron sensitivity curves of two Yb:YAG scintillators in the energy region between 0.5 and 20 MeV were obtained for the first time. As the measured relative neutron sensitivity curves of Yb:YAG scintillators cannot be verified by the Monte Carlo method and there was no referable data, the neutron sensitivity curve of a ST401 scintillator was also studied in the same method and a Geant4 simulation of ST401 scintillator was conducted to verify the experiment method in this paper. The result showed that the experimental and simulation results were approximately consistent between 17–20 MeV, and agreed well between 1–17 MeV. A comparison between the experimental result and references of ST401 scintillator was also applied and the result showed that the curve tendency of the experimental result and references was matched. The above results imply that the measured relative neutron sensitivity curves and the experimental method used herein were reliable. It also demonstrated the feasibility of studying the neutron sensitivity of inorganic scintillator based on the white neutron source. [ABSTRACT FROM AUTHOR]

Terbium doped gadolinium oxysulfide (GOS:Tb) ceramics were successfully fabricated by pre-sintering in vacuum and HIP post-treatment in Ar atmosphere. Ceramic densification in vacuum and HIP was discussed in the detail mainly by relative density and FESEM characterizations. The fabricated GOS:Tb ceramics were translucent with 0.5 mm thickness after HIP post-treatment. Optical and scintillation properties of GOS:Tb ceramics were also investigated. Temperature-dependent X-ray excited spectra were recorded using a homemade XEL spectrometer. Neutron scintillation light output was also measured in China Spallation Neutron Source (CSNS). The light output was measured to be about 284 photons per neutron with different thicknesses of GOS:Tb ceramics. • Highly dense GOS:Tb ceramics were prepared by vacuum sintering combined with HIP post-treatment. • The light output of GOS:Tb ceramic scintillator screen is increased by 23% compared with powder form. • The fabricated GOS:Tb ceramic is very promising for using as scintillator in neutron imaging technology. [ABSTRACT FROM AUTHOR]