In this study, a single-step combustion process for the synthesis 1-D, 2-D, and 3-D micro and nanostructures of AlN was developed. The structures were grown by combustion of Al+ k AlF 3 (or ZnF 2 )+ m NH 4 Cl reaction mixture under 4.0 MPa nitrogen atmosphere. Based on experimental data, the growth conditions, morphology, and composition, optical, and thermal properties of AlN micro and nanostructures were determined. The formation of structures was associated with the combustion temperature, liquid and gas-phase reactions, and the type of additives used in the experiments. The new insight, we gleaned from this study may help in the selective growth of AlN micro and nanostructures of different morphology, enhancing their functionality. [ABSTRACT FROM AUTHOR]

In this study, a combustion process for a TiO 2 + 0.12Al + (2.5 + 6 k )Mg + 0.021V 2 O 5 + k MgCl 2 ·6H 2 O mixture was studied to fabricate Ti-6Al-4V alloy spherical particles. From the temperature-time profiles, the average value of the synthesis temperature was estimated to be 1650 ± 20 °C. Based on FESEM observations, spherical shape particles were obtained when 0.05–0.1 mol MgCl 2 ·6H 2 O was added to the initial reaction mixture. Therefore, spherical alloy particles were achieved by consecutive processes of cooling and acid purification of the burned down sample. According to laser particle size analysis, the average diameter of the spheres was between 5 and 25 μm. A selective laser melting process was applied to build dense Ti-6Al-4V alloy samples. The tensile properties and the microhardness were evaluated and compared to those characteristics of a reference sample prepared from commercial Ti-6Al-4V alloy spherical powder. [ABSTRACT FROM AUTHOR]