Search

The effect of the chemical treatment of paper mill sludge fibers and polypropylene molecular weight were studied relative to the physical, mechanical, and morphological properties of a novel cellulosic biocomposite. Paper mill sludge fibers were treated with acetic anhydride, and succinic anhydride was mixed with maleic anhydride polypropylene (MAPP) and coupling agent (0 and 3%). The ratio of fibers and polymer materials was considered 30 to 70, which was manufactured by the hotpressing method at 180 °C. Water absorption, volume swelling, and contact angle were examined on each specimen according to ASTM standards, while Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) explored the efficiency of chemical modification of fibers and the morphology of biocomposites, respectively. The results showed that chemical treatment of fibers reduced the water absorption and volumetric swelling. Both tensile and flexural strength were increased with chemical treatment using the coupling agent. Comparison of fibers treated with succinic acid and acetic acid showed that the succinic acid enhanced the mechanical properties better than the acetic acid treatment. Finally, FTIR analysis showed that the hydroxyl groups decreased, and SEM images indicated the interface between fibers and polypropylene improved via chemical treatment of sludge fibers. [ABSTRACT FROM AUTHOR]

To efficiently and economically utilize a wood-plastic biocomposite, an eco-friendly biocomposite was prepared using modified poplar fiber and polylactic acid (PLA) via 3D printing technology for the first time. First, the effects of poplar fiber (0, 1, 3, 5, 7, and 9%) on the mechanical and rheological properties of the printed biocomposites were investigated. Subsequently, the printing parameters, including printing temperature, speed, and layer thickness, were optimized to obtain the biocomposite with superior properties. Finally, four printing orientations were applied to the biocomposite based on the optimized printing parameters to study the effect of filament orientation on the properties of the biocomposite. Favorable printability and mechanical properties of the biocomposite were obtained at 5% poplar fiber. The optimal printing temperature of 220 °C, speed of 40 mm/s, and layer thickness of 0.2 mm were obtained to produce the desired mechanical properties of the biocomposite with the printing orientation in a longitudinal stripe. However, the printing parameters should be chosen according to the applications, where different physical and mechanical properties are needed to achieve efficient and economical utilization of the biocomposites. [ABSTRACT FROM AUTHOR]

Consecutive superheated steam-alkali treatment was introduced to modify oil palm mesocarp fiber (OPMF) prior to biocomposite fabrication. The biocomposite made up of 70 wt.% modified OPMF (SNOPMF) and 30 wt.% poly(butylene succinate) (PBS) was prepared by melt blending followed by compression molding. A silane coupling agent of 3- aminopropyltrimethoxysilane (APTMS) was also incorporated into the SNOPMF/PBS biocomposite during the compounding process to impart better adhesion at the SNOPMF-PBS interface. The experimental results revealed that the tensile, flexural, and impact strengths were enhanced by 16, 30, and 15%, respectively, after the introduction of 2 wt.% APTMS to the SNOPMF/PBS biocomposite. Similarly, the resistance to water uptake and thickness swelling of this biocomposite was improved by 34 and 49%, respectively, relative to SNOPMF/PBS biocomposite. The SEM observation of the tensile fracture surface showed that APTMS improved the interfacial adhesion between SNOPMF and PBS. Based on the results, it can be deduced that APTMS could be a good coupling agent for improving the SNOPMF-PBS adhesion and, thereby, lead to a water resistant biocomposite of enhanced mechanical properties. [ABSTRACT FROM AUTHOR]