Search

[Display omitted] • High P-doped (9.24 at%) thick carbon electrodes (CW-P) by phytic acid treatment. • SSC exhibits high capacitance of 4.7F cm−2/206.5F g−1 at 1.0 mA cm−2. • Excellent capacitance retention of 90.5% after 20 000 cycles (@20 mA cm−2). • High energy density up to 0.94 mW h cm−2 (41.2 Wh kg−1). • High power density up to 0.6 mW cm−2 (26.3 W kg−1). Keeping outstanding electrochemical performance under high mass loading is critical to develop functional thick electrodes. Here, we report a high phosphorus-doped wood-derived carbon thick electrode for supercapacitor via phytic acid treatment, which can form hydrogen bonds with cellulose molecules in the wood. The content of phosphorus reaches up to 9.24 at% in carbonized wood with P-doping (CW-P-9.24), higher than most previously reported P-doped carbonaceous materials. CW-P-9.24 electrode (800 μm, 17.17 mg cm−2) exhibits greatly improved electrochemical performance, especially in energy density and cyclic stability. Significantly, the symmetrical supercapacitor device exhibits high areal and specific capacitance of 4.7 F cm−2 and 206.5 F g−1 at 1.0 mA cm−2 with prominent retention of 90.5% through the long-term cycling at 20 mA cm−2 for 20,000 cycles, and 0.94 mW h cm−2 (41.2 Wh kg−1) at power density of 0.6 mW cm−2 (26.3 W kg−1), and possesses excellent volumetric capacitance and energy density of 29.3 F cm−3 and 5.8 Wh cm−3, respectively. The outstanding performance can be attributed to the excellent hierarchical structure, low tortuosity, and high phosphorus doping with fast accessible channels at high current density. The extraordinary performance of CW-P has been elucidated by density functional theory calculations, which confirm the enhanced activity by P-doping. These results demonstrate that the CW-P electrode is promising for practical application in energy storage devices and encourage more investigations for thick electrode. [ABSTRACT FROM AUTHOR]

[Display omitted] • The effect of electrode thickness on the supercapacitance performance is studied. • Bass wood with hierarchical pores is easy processed to thick electrode. • The thick electrodes have high specific/areal/volumetric energy/power densities. • The SSC shows excellent cycling performance of 81% (20 mA cm−2, 15 000 cycles). The practical application of energy storage device requires high areal/volumetric energy density. One of the strategies is to design bulk electrode with hierarchical porous structure for the application of supercapacitor. Significantly, the energy storage electrochemical performance of the bulk electrode is highly influenced by the pore structure regulation and electrolyte infiltration. Therefore, it is necessary to design thick electrodes with proper pore structures and investigate the effect of thickness on the supercapacitance performance. In this work, bass wood is selected as the carbon source of electrode because of its hierarchical porous structure and easy processing into different thicknesses. The wood-derived carbon thick electrode with a thickness of 1.532 mm (CWT1.532) presents the best supercapacitance performance. Such electrode possesses a high active material loading of 54.75 mg cm−2. The symmetrical supercapacitor from CWT1.532 electrode displays remarkable specific capacitance of 65 F g−1 and areal/volumetric capacitance of 0.846 F cm−2 and 2.67 F cm−3 at 1.0 mA cm−2, respectively. It also exhibits mass/areal/volumetric power densities of 38.47 W kg−1, 500 mW cm2 and 1580 mW cm−3 as well as the corresponding energy densities of 9.04 Wh kg−1, 117.5 mWh cm−2 and 0.374 mWh cm−3, respectively. Moreover, the symmetrical supercapacitor shows an attractive cycling stability with a supercapacitance retention of 81.48% at 20 mA cm−2 even after 15 000 long-term cycles. This work provides an essential understanding about the effect of different thicknesses on the thick electrode-assembled supercapacitance and inspires future practical application in other energy storage areas. [ABSTRACT FROM AUTHOR]