Search

Objectives To evaluate knot security for 3 knot types created in 3 commonly used 5 metric suture materials incubated in physiological and pathological fluids. Study Design In vitro mechanical study. Sample Population Knotted suture loops (n = 5/group). Methods Loops of 3 different suture materials (glycolide/lactide copolymer; polyglactin 910; polydioxanone) were created around a 20 mm rod using 3 knot types (square [SQ], surgeon's [SK], and triple knot [TK]) and were tested to failure in distraction (6 mm/min) after tying (day 0) and after being incubated for 14 and 28 days in phosphate buffered saline (PBS) or inflamed peritoneal fluid. Failure load (N) and mode were recorded and compared. Results For polydioxanone, significant differences in force to knot failure were found between SQ and SK/TK but not between SK and TK. The force required to break all constructs increased after incubation in phosphate buffered saline (PBS). With glycolide/lactide copolymer no differences in force to knot failure were observed. With polyglactin 910, a significant difference between SQ and TK was observed, which was not seen between the other knot types. Incubation in inflamed peritoneal fluid caused a larger and more rapid decrease in force required to cause knot failure than incubation in PBS. Conclusions Mechanical properties of suture materials have significant effects on knot security. For polydioxanone, SQ is insufficient to create a secure knot. Additional wraps above a SK confer extra stability in some materials, but this increase may not be clinically relevant or justifiable. Glycolide/lactide copolymer had excellent knot security.

Objective: To determine the physiologic response of the equine navicular bone to core decompression surgery in healthy horses. Study Design: Experimental in vivo study. Materials: Healthy adult horses (n=6). Methods: Core decompression was completed by creating three 2.5-mm-diameter drill channels into the navicular bone under arthroscopic control. The venous (PV), arterial (PA), articular (PDIPJ), and intraosseous pressures (IOP) were recorded before and after decompression drilling. Each IOP measurement consisted of a baseline (IOPB) and a stress test (intramedullary injection of saline solution, IOPS) recording. Lameness was assessed subjectively and using force plate gait analysis. Fluorochrome bone labeling was performed. Horses were euthanatized at 12 weeks. Navicular bone mineral density (BMD) was measured, and bone histology evaluated. Results: Peak IOP (IOPmax) after stress testing was significantly (P

Objective: To determine the effect of core decompression surgery and bone mineral density (BMD) on the mechanical properties of equine navicular bones. Study Design: Experimental, in vitro study. Sample Population: Fore limb navicular bones (n=36 pairs) from sound 2–5-year-old horses with no radiographic abnormalities of the distal aspect of the forelimbs. Methods: Navicular BMD was measured using dual energy X-ray absorptiometry. One randomly assigned navicular bone from each pair served as control. The contralateral test specimen was allocated to 1 of 6 treatment groups defined by drill bit size (3.2 versus 2.5 mm diameter) and by the number of drill channels (1, 2, or 3) created in the proximal border of the bone. Bones were then tested until failure in 3-point bending. Data were statistically analyzed using ANOVA and regression analysis. Results: There were significant (P .05) influence the extent of the reduction in mechanical strength. Conclusion: In vitro core decompression significantly decreases the breaking strength of the equine navicular bone.