Search

Abstract: Titanium-based materials have been used for dental implants due to their excellent biological compatibility, superior mechanical strength and high corrosion resistance. The osseointegration of titanium dental implants is related to their composition and surface treatment. A better anti-bacterial performance of the abutment seated in the prosthetic crown is beneficial for the osseointegration and for avoiding the infection after implantation surgery. In this study, TaN-Ag coatings with different Ag contents were deposited on a bio-grade pure Ti dental implant material. A twin-gun magnetron sputtering system was used for the deposition of TaN-Ag coatings. The Ag content in the deposited coatings was controlled by the magnetron power ratio of Ag/(Ta+Ag) targets. To verify the susceptibility of implant surface to bacterial adhesion, Staphylococcus aureus, one of the major pathogen frequently found in the implant-associated infections, was chosen for in vitro anti-bacterial analyses. In addition, the biocompatibility of human gingival fibroblast (HGF) cells on coatings was also evaluated. A composite structure of crystalline TaN and Ag nanoparticles was identified. The TaN-Ag coating with the highest Ag content of 21.4at.% possessed the lowest bacterial retention and viability of S. aureus. From the MTT assay test, the mean optical density values for the TaN and TaN-Ag coated samples after 72h of HGF adhesion were greater than the value obtained from the uncoated Ti. The results suggested that the TaN-Ag coatings improve antibacterial performance with compatible biological response. [ABSTRACT FROM AUTHOR]

Development of oxide films on metallic implants with a desirable combination of mechanical properties and biocompatibility can greatly improve its functionality and application to the medical implant field. The present work is aimed to fabricate titanium (Ti) or zirconium (Zr) oxide films with porous structures onto Ti substrates by micro-arc oxidation (MAO) procedure. Before the MAO treatment, a series of Ti Zr alloy films were deposited on polished pure Ti substrates using a cathodic arc deposition system with different deposition cathode current ratios of Zr/Ti. The post-MAO-treated surface layers were characterized for its composition, crystalline structure, bonding states, surface morphology, and wettability. The results showed that porous crystalline titanium and zirconium oxides were formed using the MAO treatment for the Ti Zr films. To evaluate the bioactivity, cell viability and gene expression of human osteosarcoma cell line (MG-63) and human skin fibroblast cell line (SKF) cultured on different Ti Zr oxide films were determined. The results of MTT tests showed that the higher cell viability of MG-63 and SKF cells was found in MAO-treated Ti Zr films with higher Zr content. Gene expression data by RT-PCR and agarose gel electrophoresis showed that MG-63 cells and SKF cells exhibited notable osteogenic gene expression, such as Runx2, ALP, Dlx-5, OCN, BMP-2 and BMPR1A. The cell adhesion-related genes, such as fibronectin, collagen types I and III, and laminin were also remarkably expressed in the gel imaging. It suggested that the MAO-treated Ti Zr films were suitable for bone tissue- or soft tissue-derived cell growth and differentiation. The design and fabrication of Ti Zr oxide films with specific composition and porous surface layer with MAO treatment may provide a better material environment for cell bonding, living, and differentiation in dental and orthopedic implants. [ABSTRACT FROM AUTHOR]