Search

The paper investigates the freeze–thaw resistance and sorptivity behavior of fine‐grained alkali‐activated concrete cured at ambient temperature. A blended binder system containing fly ash, ground granulated blast furnace slag, and silica fume was used. A combination of sodium hydroxide and sodium silicate was used as an activator. The freeze–thaw resistance was evaluated based on mass loss (scaling), and the extent of internal damage was assessed by testing the ultrasonic time at different cycles. Initial and secondary sorptivity coefficients were calculated based on the cumulative water absorption values at different time intervals. Alkali content, sodium silicate to sodium hydroxide ratio, and water to binder ratio were investigated. The experimental results showed that water to binder ratio is the most significant parameter for the scaling; higher ratios result in higher scaling. In terms of internal damage, alkali content is the most significant. The increase of alkali increased the amount of internal damage in the concrete. The initial sorptivity coefficient increased with the water and alkali content and decreased with the silicate content. The secondary sorptivity coefficient showed no significant change with the investigated parameters. [ABSTRACT FROM AUTHOR]

The success of ordinary Portland cement (OPC) comes at a risk to the environment because of the large carbon dioxide emissions associated with cement manufacturing. This has led the scientific community to look for alternative cementitious materials with lower environmental impact. Alkali activated cement (AAC) is an excellent alternative to this end. In this study, the effect of binder content, alkaline solid to binder ratio (AS/B), sodium silicate to sodium hydroxide solids ratio (SS/SH), and total water content to total solid binder ratio (TW/TB) on the strength, setting time and flowability of ambient cured AAC mixtures are studied using Taguchi method of experimental design. Binder content was varied from 550 to 750 kg/m3, AS/B ratio from 0.14 to 0.22, SS/SH ratio from 1.5 to 2.5, and TW/TB ratio from 0.29 to 0.39. The study results showed that within the investigated range, an increase in binder content has a minor effect on strength but resulted in a considerable increase in setting time and flowability. An increase in the AS/B ratio resulted in increased flowability and setting time and a decrease in strength. Moreover, the study also investigated the relationship between compressive strength and flexural strength. [ABSTRACT FROM AUTHOR]

Accurate estimation of the in situ strength of concrete at early age is very important as it provides the necessary information required to start subsequent construction operations. Overestimation of the strength may cause serious safety hazards and underestimation may lead to unnecessary costly delays. This study investigates the performance of the maturity method in estimating the strength of in situ concrete subjected to cold weather at early age. Instrumented concrete slabs were subjected to cold weather conditions at early ages and their strengths were measured using drilled core samples from the slab. Sensors embedded in the slabs measured the temperature in the concrete which was used to estimate the strength using the maturity method. The measured core strengths at 24 and 72 h after casting are then compared with the estimated strengths using the maturity method and its performance is evaluated. The core strengths are also compared with the strength of standard cylinders cured at the same condition as the slabs. More than 250 cylinders from two slab thicknesses and four batches of concrete were used in the experiments to obtain statistically significant experimental data. The results show that the maturity method performed much better than the standard cylinder strength. On average the standard cylinder strength underestimated the core strength by more than 40% while the maturity method overestimated the strength by less than 10% with a lower variation. [ABSTRACT FROM AUTHOR]