Search

The study of damage processes in concrete and their effects on the residual properties represents a key point related to the service life of reinforced concrete (RC) structures. The use of steel fibers in RC beams mainly improves the cracking control and the shear bearing capacity. Considering the shear behavior, the presence of fibers not only leads to partial or total substitution of secondary reinforcement, but they can also result in a modification of the failure behavior from a shear failure (brittle) to a bending (ductile) one. The contribution of fibers on flexural and shear behavior of sound and damaged RC beams was investigated using alkali‐silica reaction as a damaging tool. First, the evolution of deformations and cracks were measured on creep tests of RC beams with and without fibers and reactive aggregates. Second, the flexural and shear behavior of damaged and undamaged beams incorporating steel fibers were compared. Results showed that alkali‐silica reaction damage can provoke a reduction of RC beam ductility, while the flexural strength is preserved. Regarding shear, it was observed that even in damaged concrete, fibers were able to control the crack propagation and increase the bearing capacity. [ABSTRACT FROM AUTHOR]

The use of fibers in Reinforced Concrete (RC) elements changes their cracking pattern, leading to narrower and more closely spaced cracks. In addition, the presence of fibers can improve the steel‐to‐concrete bond behavior reducing the steel‐to‐concrete interface damage after cracking. Cracks and steel‐to‐concrete interface damage work like paths, for aggressive agents, to reach the rebar in cracking elements, reducing the initiation period of the corrosion process, and favoring the corrosion at the intersection between cracks and reinforcement. In this context, this article discusses an experimental program on tension ties mechanically cracked and exposed to a chloride‐rich environment with the purpose to check and eventually adequate the typical electrochemical measurements, used in the case of RC elements, for Steel Fiber Reinforced Concrete (SFRC). Adjustments related to degradation morphology and interference of steel fibers are proposed and used on Fiber Reinforced Concrete (FRC) elements for monitoring the influence of cracks and fibers on corrosion propagation. Finally, these proposed modifications were checked and validated against the results obtained by monitoring SFRC beams in the cracked stage. [ABSTRACT FROM AUTHOR]

The use of fibers in reinforced concrete (RC) beams mainly improves both the bearing capacity and the cracking control. In this way, positive effects on the service life of RC structures can be expected. In this paper, the fiber influence on the flexural behavior of RC beams with different longitudinal reinforcement ratios (0.5% ≤ ρs ≤ 1.2%) is analyzed by testing small‐scale RC beams. Concretes incorporating 0, 25 and 50 kg/m3 of steel, 6 and 12 kg/m3 of glass macrofibers, and 5 and 10 kg/m3 of polymer macrofibers were studied. Crack and deflection control, as well as bearing capacity and crack localization were evaluated for a broad range of fiber‐reinforced concrete (FRC) toughness. It is verified that fibers, in the longitudinal reinforcement ratio considered, improve the bending behavior at serviceability limit state (SLS) and ultimate limit state (ULS) of RC beams, without limiting the structure ductility. It was also confirmed the philosophy of the fib Model Code 2010, such that FRC can be considered as a composite material where performance parameters govern its mechanical behavior. Finally, the several data available allowed to deeply analyze fib Model Code 2010 formulations (mean crack spacing and flexural bearing capacity) and to propose modifications where needed. [ABSTRACT FROM AUTHOR]

The use of fibers can improve the behavior at serviceability limit states (crack and deflection control) and ultimate limit states (bearing capacity) of reinforced concrete (RC) elements under flexure. Fibers reinforcement provides a postcracking resistance, leading RC element to have a more diffused crack patterns characterized by narrower and more closely spaced cracks. Some doubts are instead related to RC element ductility, which can be affected by crack localization after rebar yielding. However, most of experiments present in literature relate only to elements in steel fiber reinforced concrete with significant residual strengths (fR,1 and fR,3 greater than 3.5–4.0 MPa). This paper aims to evaluate the influence of different fiber type (steel, glass, or polymer macrofibers) on the cracking and strength capacity of RC beams under flexure by using a broad range of Fiber Reinforced Concrete (FRC) toughness (1.6 ≤ fR,1 ≤ 5.1 MPa and 0.8 ≤ fR,3 ≤ 4.5 MPa). Twenty‐one small scale RC beams with a typical value of longitudinal reinforcement ratio (0.87%) were tested under flexure. Crack and deflection control, as well as bearing capacity and crack localization were evaluated as a function of FRC toughness. Finally, results were compared against mean crack spacing and strength capacity predictions of fib Model Code 2010. [ABSTRACT FROM AUTHOR]

Different tests are proposed by international standards for the evaluation of the mechanical properties of fiber reinforced concrete (FRC); among them, either beams or round determinate panels are generally used. However, different tests are accepted by design codes if reliable correlation factors between standard parameters are provided (fib Model Code 2010). Within this context, a broad experimental program on both beams and round determinate panels was carried out in order to provide a critical discussion on material characterization and to evaluate possible correlation factors. Beam tests according to European (EN 14651), American (ASTM 1609), and Japanese (JCI‐SF4) standard, as well as small round panels and large round panels (according to ASTM 1550) were studied within an experimental program comprising 189 beams and 90 round panels. Unlike previous researches, mainly focused on steel fibers, two types of macro‐synthetic fibers were considered. Based on these experimental results, a comparison between test methods is presented, along with correlation approaches are proposed and critically discussed. [ABSTRACT FROM AUTHOR]