Whether the performance of carbon fiber‐reinforced polymer (CFRP)‐strengthened concrete structure is affected by chloride penetration is the key to the application under chloride environments. In this paper, the effect of chloride penetration on tensile properties of CFRP sheet, bond behavior of CFRP‐concrete, and flexural performance of CFRP‐strengthened concrete beams were studied. Results show that chloride penetration has no effect on the elastic modulus of the CFRP sheet. The tensile strength and elongation of the CFRP sheet decrease with the exposure time increase, reducing by 10% and 12.7% after 240 days. The interface failure of CFRP‐concrete is likely to occur on the concrete surface. As the exposure time increases, the interface failure develops toward the epoxy resin layer; the sliding stiffness and end slip of the interface decrease. However, the ultimate bearing capacity of the interface first increases and then decreases. As the exposure time increase, the effective bonding length gradually increases, and the failure mode of CFRP‐strengthened beams changes from bending failure to shear failure. After 120 days, the ultimate bearing capacity of the beams is significantly reduced. From three parts of materials, interfaces, and components to provide an evaluation basis for the use, regular detection, and life prediction of CFRP‐strengthened reinforced concrete beams under chloride environments. [ABSTRACT FROM AUTHOR]

This paper investigates the influence of cyclic preloading on the fatigue behavior of reinforced concrete (RC) beams rehabilitated with near surface mounted (NSM) carbon fiber reinforced polymer (CFRP) reinforcement. The study includes eight RC beams with dimensions of 152.4 × 152.4 × 1,521 mm. Strengthened and nonstrengthened specimens were tested under monotonic loading to obtain the flexural static capacity. Two strengthened specimens were tested as a reference under constant amplitude cyclic stress without prefatiguing. Four nonrehabilitated RC beams were prefatigued to simulate service loading conditions. Later, these RC beams were rehabilitated with NSM CFRP reinforcement and tested under the same cyclic stress range of the reference specimens. Mid‐span deflection, strain of tension steel rebars and CFRP rods, stiffness degradation, and energy dissipation were analyzed and evaluated. Experimental results show that the rehabilitated prefatigued RC beams had similar stiffness degradation and failure modes to the reference strengthened RC beams. The rehabilitated RC beams had an improvement in the fatigue responses when compared to the reference strengthened RC beams. Moreover, the postfatigue monotonic behavior of the rehabilitated RC beams showed an increase in the elastic modulus and a decrease in ductility. [ABSTRACT FROM AUTHOR]