Abstract: Magneto-impedance (MI) of a double-barrier MgO magnetic tunnel junction (DMTJ) is measured as a function of frequency (20 Hz–3 MHz) and DC bias (−1 to 1 V) under magnetic parallel and antiparallel states. A strong nonlinear effect is observed at all frequencies and the MI changes from positive to negative at the relaxation frequency ∼1/RC. A frequency–dc bias () “phase diagram” is mapped out to describe the combination effects of the magneto-impedance response. The decay of the tunnel magneto-resistance (TMR) and tunnel magneto-capacitance (TMC) at high voltage is sufficiently reduced by the double-MgO barrier. The V1 / 2 (the voltage that magnetic response drops to 1/2 of its maximum) of TMC reaches an average value of ∼1.35 V, which is larger than the V1 / 2 of TMR ∼0.95 V, suggesting that the response of TMC is more stable than TMR for high frequency application. [ABSTRACT FROM AUTHOR]

We report on the preparation and characterization of the variation of B′-site transition metal in Sr2CrMO6 (M=Mo, W) with double perovskites structure. The magnetic susceptibility shows that Sr2CrMoO6 and Sr2CrWO6 are antiferromagnets with TN=40 and 30 K at H=1 T, respectively. In addition, a large magnetoresistance ratio (MR) of ∼38% (H=3 T) at 5 K was observed in the Sr2CrWO6 compound. However, the Sr2CrMoO6 compound does not show any significant MR even at high fields (MR∼4%; H=3 T and 5 K). The measured O K-edge X-ray absorption is in agreement with the calculated O p-density of states for both compounds. [Copyright &y& Elsevier]