Humidity sensitivity is evaluated for chemically synthesized ZnAl2O4/Al devices. We succeeded in synthesizing the ZnAl2O4/Al device by applying chemical techniques only. Hydrothermal treatment for the anodized aluminum (AlOx/Al) gives us the device of the ZnAl2O4/Al structure. All fabrication processes were conducted under 400 °C. The key was focusing on ZnAl2O4 as the sensing material instead of MgAl2O4, which is generally investigated as the humidity sensor. The evaluation of this ZnAl2O4/Al device clarified its effectiveness as a sensor. Both electrical capacitance, Cp, and the resistivity, Rp, measured by an LCR meter, obviously responded to the humidity with good sensitivity and appreciable repeatability. Our synthesis technique is possible in principle to improve on the process for the device with a complex structure providing a large surface area. These characteristics are believed to expand the application study of spinel aluminate devices as the sensor. [ABSTRACT FROM AUTHOR]

ZnAl2O4 nanoparticles were synthesized employing a colloidal method. The oxide powders were obtained at 300 °C, and their crystalline phase was corroborated by X-ray diffraction. The composition and chemical structure of the ZnAl2O4 was carried out by X-ray and photoelectron spectroscopy (XPS). The optical properties were studied by UV-vis spectroscopy, confirming that the ZnAl2O4 nanoparticles had a direct transition with bandgap energy of 3.2 eV. The oxide's microstructures were microbars of ~18.2 nm in size (on average), as analyzed by scanning (SEM) and transmission (TEM) electron microscopies. Dynamic and stationary gas detection tests were performed in controlled propane atmospheres, obtaining variations concerning the concentration of the test gas and the operating temperature. The optimum temperatures for detecting propane concentrations were 200 and 300 °C. In the static test results, the ZnAl2O4 showed increases in propane response since changes in the material's electrical conductance were recorded (conductance = 1/electrical resistance, Ω). The increases were ~2.8 at 200 °C and ~7.8 at 300 °C. The yield shown by the ZnAl2O4 nanoparticles for detecting propane concentrations was optimal compared to other similar oxides categorized as potential gas sensors. [ABSTRACT FROM AUTHOR]