The behavior of solute atoms in an undersaturated Fe-3.3 at.%Ni model alloy upon heavy and light particle irradiations was investigated by Atom Probe Tomography. Whereas first irradiations, performed using 27 MeV Fe ions at 400 °C, highlight significant Ni enrichment on point defect clusters, solute-rich features detected after 2.8 MeV H + ion (400 °C) and 1 MeV electron (320 °C) irradiations are only associated with pre-existent microstructural defects. Nanoindentation tests show no hardening in light particle irradiated samples, strongly suggesting that no dislocation loop formed. These observations put forward the importance of point defect clusters resulting from displacement cascades in Ni clusters' formation. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Post irradiation annealing (PIA) clarified the induced versus enhanced controversy regarding nanoscale Mn-Ni-Si precipitate (MNSP) formation in pressure vessel steels. Radiation induced MNSPs would dissolve under high temperature PIA, while radiation enhanced precipitates would be stable above a critical radius (r c). A Cu-free, high Ni steel was irradiated with 2.8MeV Fe2+ ions at two temperatures to generate MNSPs with average radii (r ¯) above and below an estimated r c for PIA at 425°C up to 52 weeks. Atom probe tomography and energy dispersive x-ray spectroscopy showed MNSPs with r < r c dissolved, while those with r > r c slightly coarsened, consistent with thermodynamic predictions. Image, graphical abstract [ABSTRACT FROM AUTHOR]

In this study, APT and TEM analyses were used to characterise two Zr-based alloys neutron-irradiated to 13.7 dpa. The high spatial and chemical resolution of these techniques has enabled the irradiation-induced nanoscale distribution of solute elements to be characterised. The results on both Zircaloy-2 and low-Sn ZIRLO support previous observations of Fe segregation to planar dislocation arrays with enhanced Sn between. In Zircaloy-2, the APT data in this study have also revealed short-range (∼2 nm) clustering of Fe and Sn atoms both within the Fe-enriched planes and in the regions between dislocation arrays. The resultant microstructure is reminiscent of spinodal decomposition. In low-Sn ZIRLO Nb-rich precipitates formed in the Sn-rich planes. The data in this article enhance our understanding of microstructural evolution in Zr alloys under neutron irradiation and are relevant for predicting changes in the properties of Zr alloys in-service in fission reactors. [Display omitted] [ABSTRACT FROM AUTHOR]