The behavior of solute atoms in an undersaturated Fe-3.3 at.%Ni model alloy upon heavy and light particle irradiations was investigated by Atom Probe Tomography. Whereas first irradiations, performed using 27 MeV Fe ions at 400 °C, highlight significant Ni enrichment on point defect clusters, solute-rich features detected after 2.8 MeV H + ion (400 °C) and 1 MeV electron (320 °C) irradiations are only associated with pre-existent microstructural defects. Nanoindentation tests show no hardening in light particle irradiated samples, strongly suggesting that no dislocation loop formed. These observations put forward the importance of point defect clusters resulting from displacement cascades in Ni clusters' formation. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Post irradiation annealing (PIA) clarified the induced versus enhanced controversy regarding nanoscale Mn-Ni-Si precipitate (MNSP) formation in pressure vessel steels. Radiation induced MNSPs would dissolve under high temperature PIA, while radiation enhanced precipitates would be stable above a critical radius (r c). A Cu-free, high Ni steel was irradiated with 2.8MeV Fe2+ ions at two temperatures to generate MNSPs with average radii (r ¯) above and below an estimated r c for PIA at 425°C up to 52 weeks. Atom probe tomography and energy dispersive x-ray spectroscopy showed MNSPs with r < r c dissolved, while those with r > r c slightly coarsened, consistent with thermodynamic predictions. Image, graphical abstract [ABSTRACT FROM AUTHOR]