TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M (NH4)2SO4 solution in a temperature-controlled bath. The pH values of the suspension were 7, 8 or 9. According to the x-ray diffraction (XRD) analysis the anatase crystallite sizes were about 12 nm, which coincided with the average particle size revealed by scanning electron microscopy (SEM). The Raman scattering measurements have shown the presence of a small amount of highly disordered brookite phase in addition to dominant anatase phase with similar nanostructure in all synthesized powders. BET measurements revealed that all synthesized catalysts were fully mesoporous, except the sample synthesized with 0.07 M (NH4)2SO4 at pH=9, which had small amount of micropores. The photocatalytic degradation of herbicide Clomazone was carried out for both the pure active substance and as the commercial product (GAMIT 4-EC) under UV irradiation. The best photocatalytic efficiency was obtained for the catalyst with the largest specific surface area, confirming this parameter as crucial for enhanced photocatalytic degradation of the pure active substance and commercial product of herbicide Clomazone. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. III45018]

Raman spectroscopy has been used for characterization of commercial nanosized TiO2 powder with declared grain size of 5 nm. The Raman spectra measured in Stokes and anti-Stokes regime confirm the anatase phase of TiO2 powder in temperature range 25-1173K. It is shown that phonon-confinement (due to small grain size) and nonstoichiometry (caused by laser irradiation in vacuum) have a great influence on blueshift and broadening of the main Eg Raman mode at low temperatures, while the influence of the strong anharmonic effect becomes dominant at higher temperatures. The phonon confinement effect decreases due to the crystallite growth at temperatures above 673K.