We have performed quantitative analysis of {332}〈113〉 twinning in a β-Ti-15Mo (wt.%) alloy by in situ scanning electron microscopy and electron backscattering diffraction (EBSD). Microstructure-twinning relations were evaluated by statistical analysis of the evolving twin structure upon deformation at room temperature. Our analysis reveals that at the early stages of deformation (ε < 1.5 to 2.0%), primary twinning is mainly determined by the applied macroscopic stress resolved on the twin system. Most of the primary twins (~70–80% of the analyzed twins) follow Schmid’s law with respect to the macroscopic stress, and most of the growth twins (~ 85% of the analyzed twins) correspond to the higher stressed variant. In the grain size range studied here (40–120 μm), we find that several twin parameters such as number of twins per grain and number of twins per grain boundary area exhibit grain size dependence. We ascribe these effects to the grain size dependence of twin nucleation stress and apparent critical resolved shear stress for twinning, respectively.

We have investigated the propagation of {332} twins in a multilayered Ti-10Mo-xFe (x = 1–3) alloy fabricated by multi-pass hot rolling. The material contains a macroscopic Fe-graded structure (about 130 μm width) between 1 and 3 wt% Fe in the direction perpendicular to rolling. We observe strong influence of the Fe-graded structure in the twin propagation behavior. The propagation of {332} twins that are nucleated in Fe-lean regions (~1 wt% Fe) is interrupted in the grain interiors at a specific Fe content, namely, about 2 wt% Fe. We ascribe this effect to the role of Fe content in solid solution on the stress for twin propagation. The interruption of twins in the grain interiors results in the development of characteristic dislocation configurations such as highly dense dislocation walls (HDDWs) associated to strain localization phenomena. The nucleation and propagation of these dislocation configurations is ascribed to the underlying plastic accommodation mechanisms of the stress field at the twin tips. We find that the crystallographic alignment of HDDWs is determined by the stress field at the twin tips and the deformation texture. The excellent plastic accommodation at the interrupted twin tips allows attaining the good ductility of the present material (total elongation of 28%).