Tungsten trixoide/titania (WO3-titania) composite thin films with W/Ti molar ratios of 100/0, 98/2, 96/4, 94/6 92/8 and 90/10 were prepared on fluorine-doped tin oxide conducting glass, and their electrochromic (EC) and photoelectrochromic (PEC) performances were investigated in this study. The composite thin films were synthesized by sol–gel process using peroxotungstic acid and titanium (IV) n-butoxide as the precursors. The surface morphology and composition of the composite thin films were characterized using scanning electron microscope with energy dispersive spectrometer. Electrochemical experiments with in situ spectroscopic measurement were employed to study the EC properties of the composite thin films. It was found that the presence of titania in the WO3 matrix might slightly decreases its EC performance. PEC cells using the composite thin films as the working electrode and a sputtered semitransparent platinum thin film on ITO as the counter electrode were fabricated and their PEC performances were investigated. The device using composite thin film prepared from sol solution with a W/Ti molar ratio of 96/4 exhibited the best PEC performance.

We successfully fabricated a predefined patterned copper (Cu) substrate for thin GaN light-emitting diodes without barriers by the selective electroplating technique. The contours of Cu bumps fabricated using different electroplating modes and parameters were measured. We observed that the average thickness diminished with increasing current density. The current density conditions to obtain the best upright structure in the process were 40 and 80 mA/cm2.

Platinum (Pt) nanoparticles supported on zirconia–carbon black nanocomposites (Zr–C), which annealed at different temperatures, used as Pt/Zr–C electrocatalysts for methanol oxidation reaction (MOR) are prepared and characterized in this study. Transmission electron microscope images and X-ray diffraction analysis showed that the diameters of Pt nanoparticles are around 3–4 nm. Electrocatalytic MOR performances of these Pt/Zr–C electrocatalysts are investigated by cyclic voltammetry, CO-stripping voltammetry, and chronoamperometry. All the Pt/Zr–C electrocatalysts synthesized in this study exhibited higher MOR efficiency than that of the commercial E-TEK Pt/C electrocatalyst, and the electrocatalyst using Zr–C support annealed at 300 °C, achieving the highest MOR efficiency among all the electrocatalysts.