Search

The long-term operation of motors induces substantial alterations in the surface conductivity and nonlinear coefficient of anti-corona paint, diminishing its efficacy and jeopardizing the longevity of large motors. Hence, the development of high-performance anti-corona paint holds paramount importance in ensuring motor safety. In this study, we integrate two nano-fillers, namely silicon carbide (SiC) and organic montmorillonite (O-MMT), into a composite matrix comprising micron silicon carbide and epoxy resin (SiC/EP). Subsequently, three distinct types of anti-corona paint are formulated: SiC/EP, Nano-SiC/EP, and O-MMT/SiC/EP. Remarkably, O-MMT/SiC/EP exhibits a glass transition temperature about 25 °C higher than that of SiC/EP, underscoring its superior thermal properties. Moreover, the introduction of nano-fillers markedly augments the surface conductivity of the anti-corona paint. Aging tests, conducted across varying temperatures, unveil a notable reduction in the fluctuation range of surface conductivity post-aging. Initially, the nonlinear coefficients exhibit a declining trend, succeeded by an ascending trajectory. The O-MMT/SiC/EP composite displays a maximum nonlinearity coefficient of 1.465 and a minimum of 1.382. Furthermore, the incorporation of nanofillers amplifies the dielectric thermal stability of epoxy resin composites, with O-MMT/SiC/EP showcasing the pinnacle of thermal endurance. Overall, our findings elucidate the efficacy of nano-fillers in enhancing the performance and longevity of anti-corona paint, particularly highlighting the exceptional attributes of the O-MMT/SiC/EP composite in bolstering motor safety through improved thermal stability and electrical properties. [ABSTRACT FROM AUTHOR]

The purpose of this paper is to study the effect of nano-bismuth ferrite (BiFeO3) on the electrical properties of low-density polyethylene (LDPE) under magnetic-field treatment at different temperatures. BiFeO3/LDPE nanocomposites with 2% mass fraction were prepared by the melt-blending method, and their electrical properties were studied. The results showed that compared with LDPE alone, nanocomposites increased the crystal concentration of LDPE and the spherulites of LDPE. Filamentous flake aggregates could be observed. The spherulite change was more obvious under high-temperature magnetization. An agglomerate phenomenon appeared in the composite, and the particle distribution was clear. Under high-temperature magnetization, BiFeO3 particles were increased and showed a certain order, but the change for room-temperature magnetization was not obvious. The addition of BiFeO3 increased the crystallinity of LDPE. Although the crystallinity decreased after magnetization, it was higher than that of LDPE. An AC test showed that the breakdown strength of the composite was higher than that of LDPE. The breakdown strength increased after magnetization. The increase of breakdown strength at high temperature was less, but the breakdown field strength of the composite was higher than that of LDPE. Compared with LDPE, the conductive current of the composite was lower. So, adding BiFeO3 could improve the dielectric properties of LDPE. The current of the composite decayed faster with time. The current decayed slowly after magnetization. [ABSTRACT FROM AUTHOR]

In the course of this study, the dielectric and physicochemical properties of poly(2-oxazoline) (POx) networks from renewable resources were compared with those of fossil-based polyamide 12 (PA 12) networks. POx was synthesized by the energy-efficient, microwave-assisted copolymerization of 2-oxazoline monomers, which were derived from fatty acids of coconut and castor oil. For the preparation of composites, aluminum nitride nanoparticles n-AlN and microparticles μ-AlN as well as hexagonal boron nitride BN submicroparticles were used. Additionally, 0, 15, or 30 wt.% of a spiroorthoester (SOE) were added as an expanding monomer aiming to reduce the formation of shrinkage-related defects. For the crosslinking of the polymers and the SOE as well as the double ring-opening reaction of the SOE, a thermally triggered dual-cure system was developed. The fully-cured blends and composites containing SOEs exhibited lower densities than their fully-cured SOE-free analogues, which was indicative of a lower extent of shrinkage (or even volumetric expansion) during the curing reaction, which is referred to as relative expansion RE. The RE amounted to values in the range of 0.46 to 2.48 for PA 12-based samples and 1.39 to 7.50 vol.% for POx-based samples. At 40 Hz, the "green" POx networks show low loss factors, which are competitive to those of the fossil-based PA 12. [ABSTRACT FROM AUTHOR]