Macro-size regenerated cellulose fibres (RCFs) with embedded graphene oxide (GO) were fabricated by dissolving cellulose in a pre-cooled sodium hydroxide (NaOH)/urea solution and regenerated in sulphuric acid (H2SO4) coagulant. Initially, GO was found to disperse well in the cellulose solution due to intercalation with the cellulose; however, this cellulose–GO intercalation was disturbed during the regeneration process, causing agglomeration of GO in the RCF mixture. Agglomerated GO was confirmed at a higher GO content under a Dino-Lite microscope. The crystallinity index (CrI) and thermal properties of the RCFs increased with increasing GO loadings, up to 2 wt.%, and reduced thereafter. Cellulose–GO intercalation was observed at lower GO concentrations, which enhanced the crystallinity and thermal properties of the RCF–GO composite. It was shown that the GO exhibited antibacterial properties in the RCF–GO composite, with the highest bacterial inhibition against E. coli and S. aureus. [ABSTRACT FROM AUTHOR]

This study aimed to develop a safe and advanced antibacterial material of electrospun microfiber membranes (MFMs) for wound dressings. Combinations of several materials were investigated; thermal treatment and electrospinning techniques were used to form the best quality of MFMs to suit its end applications. By comparing the fiber morphology, diameter changes, and fracture strength, the suitable ratio of raw materials and thermal treatment were obtained before and after adding Trition X-100 as a surfactant for MFMs of sodium alginate/polyvinyl alcohol/polyethylene oxide (SA/PVA/PEO). The electrospinning solution was mixed with berberine as an antibacterial substance; meanwhile, calcium chloride (CaCl2) was used as the crosslinking agent. The antibacterial properties, water dissolution resistance, water content, and fracture strength were thoroughly investigated. The results showed that the antibacterial rates of MFMs with different mass fractions of berberine (0, 3, and 5 wt.%) to Escherichia coli (E. coli) were 14.7, 92.9, and 97.2%, respectively. The moisture content and fracture strength of MFMs containing 5 wt.% berberine were 72.0% and 7.8 MPa, respectively. In addition, the produced MFMs embodied great water dissolution resistance. Berberine-loaded SA/PVA/PEO MFMs could potentially serve as an antibacterial wound dressing substrate with low cost and small side effects. [ABSTRACT FROM AUTHOR]