Search

This paper presents a study of the flammability and thermal decomposition products of glass fiber-reinforced epoxy resin (GFRER) with the addition of cardanol-based phosphorus-containing benzoxazine monomer (CBz) and graphene and their combinations in different proportions (up to 20 wt.%). The addition of CBz alone or in combination with graphene resulted in an increase in the limiting oxygen index (LOI) and self-extinguishing in the UL-94 HB test. The flame-retardant samples had better tensile mechanical properties than the sample without additives. The differential mass-spectrometric thermal analysis (DMSTA) of the thermal decomposition products of GFRER without additives and with the addition of CBz and graphene was carried out. CBz addition promoted the thermal decomposition of high-molecular-weight products of epoxy resin decomposition in the condensed phase and at the same time decreased the time of release of low-molecular-weight thermal decomposition products into the gas phase. Graphene addition resulted in an increase in the relative intensities of high-molecular-mass peaks compared to GFRER without additives. [ABSTRACT FROM AUTHOR]

In this study, two types of composites, polybutylene terephthalate (PBT) and epoxy resin (ER), reinforced with 20% of glass fiber (GF) are used as the comparative research objects. Their mechanical properties after thermal aging at 85~145 °C are evaluated by tensile strength and fracture morphology analysis. The results show that the composites have similar aging laws. The tensile strength of GF/PBT and GF/ER decrease gradually with the increase of aging temperature, while their elastic moduli are independent of the thermal treatment temperature. Scanning electron microscopy study of the fracture surface shows that separation of glass fiber from PBT and ER matrix becomes more obvious at higher aging temperature. The fibers on the matrix surface appear clear and smooth, and the whole pulled out GFs can be observed. As a main mechanical strength degradation mechanism, the deterioration of interface adhesion between the matrix and GF is discussed. A large difference in coefficients of thermal expansion of the matrix and GF is a main factor of the mechanical degradation. [ABSTRACT FROM AUTHOR]

The pull-out method was used to study the adhesive strength τ of "fiber–thermoset" systems with wide variations in area. Studied binders were based on resins that had different chemical natures (epoxy, epoxy phenol, orthophthalic, polyphenylsiloxane, and phenol–formaldehyde). Shear adhesive strength was determined for systems with two fiber types (glass and steel fibers). It was shown that strength τ depended on scale (area). Formation of τ occurred during the curing process and the system's subsequent cooling to the measurement temperature T. It was found that interface strength depended on measurement temperature across a wide temperature range that covered the highly elastic and the glassy state of the adhesive. The influence of residual stresses τres, acting at the "binder–fiber" interface, on the nature of the curves describing the dependence of the adhesive strength on the studied factor was experimentally shown. A qualitative explanation of the observed regularities is proposed. [ABSTRACT FROM AUTHOR]

Although epoxy resin has been extensively used in the field of wind turbine blades, polyurethane has attracted much attention in recent years, due to its potential value of better fatigue resistance, lower processing viscosity and higher strength than epoxy resin blades. Herein, we construct a dense cross-linking structure in polyurethane (PU) based on different amounts of hydroxypropyl methacrylate (HPMA) with low processing viscosity and excellent mechanical properties. By increasing the content of HPMA, the thermal stability of PU is enhanced, but the micro-morphology does not change significantly. When the content of HPMA is 50 g (in 200 g copolymer), the PU sample PH-50 exhibits a viscosity of 70 MPa·s and a gelation time of 120 min at 25 °C, which is sufficient to complete processes like pouring and filling. By post-curing the PH-50 at 80 °C for 2 h, the heat distortion temperature can reach 72 °C, indicating the increase of temperature resistance. The PU copolymers also have excellent mechanical and dynamic thermo-mechanical properties due to the cross-linking structure between PU chains and poly-HPMA chains. Additionally, the PU copolymer has excellent compatibility with various glass fiber fabrics (GFF), showing a good match in the vacuum infusion experiment and great properties in the mechanical test. By compounding PH-50 with GFF, the composite with high strength is easily prepared for a wind turbine blade in various positions. The tensile strengths of the composites are all over 1000 MPa in the 0° direction. Such composites are promising for the future development of wind turbine blades that meet the stringent requirements for outstanding processing and mechanical properties. [ABSTRACT FROM AUTHOR]