Membrane distillation (MD) is an emerging technology for water recovery from hypersaline wastewater. Membrane scaling and wetting are the drawbacks that prevent the widespread implementation of the MD process. In this study, coaxially electrospun polyvinylidene fluoride-co-hexafluoropropylene (PVDF-co-HFP) nanofibrous membranes were fabricated with re-entrant architecture and enhanced hydrophobicity/omniphobicity. The multiscale roughness was constructed by incorporating Al2O3 nanoparticles and 1H, 1H, 2H, 2H Perfluorodecyltriethoxysilane in the sheath solution. High resolution transmission electron microscopy (HR-TEM) could confirm the formation of the core-sheath nanofibrous membranes, which exhibited a water contact angle of ~142.5° and enhanced surface roughness. The membrane displayed a stable vapor flux of 12 L.m−2.h−1 (LMH) for a 7.0 wt.% NaCl feed solution and no loss in permeate quality or quantity. Long-term water recovery from 10.5 wt.% NaCl feed solution was determined to be 8–10 LMH with >99.9% NaCl rejection for up to 5 cycles of operation (60 h). The membranes exhibited excellent resistance to wetting even above the critical micelle concentration (CMC) for surfactants in the order sodium dodecyl sulphate (SDS) (16 mM) > cetyltrimethylammonium bromide (CTAB) (1.5 mM) > Tween 80 (0.10 mM). The presence of salts further deteriorated membrane performance for SDS (12 mM) and Tween-80 (0.05 mM). These coaxial electrospun nanofibrous membranes are robust and can be explored for long-term applications. [ABSTRACT FROM AUTHOR]

A novel, modified polypyrrole/m-phenylediamine (PPy–mPD) composite, decorated with magnetite (Fe3O4) nanoparticles, and prepared via an in-situ oxidative polymerisation, was investigated. The PPy–mPD/Fe3O4 nanocomposite was employed for the removal of highly toxic oxyanion hexavalent chromium Cr(VI) from an aqueous solution. The structure and successful formation of the PPy–mPD/Fe3O4 nanocomposite was confirmed and investigated using various techniques. The presence of Fe3O4 was confirmed by high resolution transmission electron microscopy, with an appearance of Fe lattice fringes. The estimation of the saturation magnetisation of the nanocomposite, using a vibrating sample magnetometer, was observed to be 6.6 emu/g. In batch adsorption experiments, PPy–mPD/Fe3O4 nanocomposite (25 mg) was able to remove 99.6% of 100 mg/L of Cr(VI) at pH 2 and 25 °C. Adsorption isotherms were investigated at different Cr(VI) concentration (100–600 mg/L) and temperature (15–45 °C). It was deduced that adsorption follows the Langmuir model, with a maximum adsorption capacity of 555.6 mg/g for Cr(VI) removal. Furthermore, isotherm data were used to calculate thermodynamic values for Gibbs free energy, enthalpy change and entropy change, which indicated that Cr(VI) adsorption was spontaneous and endothermic in nature. Adsorption–desorption experiments revealed that the nanocomposite was usable for two consecutive cycles with no significant loss of adsorption capacity. This research demonstrates the application potential for the fascinating properties of PPy–mPD/Fe3O4 nanocomposite as a highly efficient adsorbent for the removal of heavy metal ions from industrial wastewater. [ABSTRACT FROM AUTHOR]