Search

In the biomedical industry, tricalcium phosphate is a bioceramic substance that is frequently employed in the fabrication of scaffolds and bone structures. Fabrication of porous ceramic structures using conventional manufacturing techniques is very challenging because of the brittle nature of the ceramics, which has led to a newly adapted direct ink writing additive manufacturing method. This work investigates the rheology and extrudability of TCP inks to produce near-net-shape structures. Viscosity and extrudability tests found that stable TCP: Pluronic ink of 50 vol.% was more reliable compared to other tested inks prepared from a functional polymer group polyvinyl alcohol. A line study was carried out to identify the printing parameters suitable for printing structures from the selected ink with lesser dimensional error. Printing speed 5 mm/s and extrusion pressure 3 bar was found suitable to print a scaffold through a nozzle of 0.6 mm, keeping the stand-off distance equal to the nozzle diameter. The printed scaffold was further investigated for its physical and morphological structure of the green body. A suitable drying behavior was studied to remove the green body without cracking and wrapping before the sintering of the scaffold.

In the present study, recyclability of Laser PP CP 75 polypropylene powder from Diamond Plastics GmbH was determined by characterizing and comparing the used powder after each cycle with material from previous cycles and with fresh powder. The melt flow index of Laser PP CP 75 was affected by recycling since it was observed to change by 30.62% after the 8th 100% re-use cycle, a lower value than PA 12 of 66.04%, for the 6th re-use cycle. Parts printed with virgin Laser PP CP 75 had an average dimensional error of 3.02% (virgin material) and 4.06% after the 4th 100% re-use cycle, which raises concerns about the commercial viability of the material. After the 4th re-use cycle, the printed parts had distorted edges and failed to print after the 9th print cycle. Lastly, tensile testing revealed a skewed bell-shaped curve of strength versus the number of recycles with the highest ultimate tensile strength occurring for the second 100% re-use cycle (7.4 MPa). The curves for elastic modulus and percentage elongation were inverted with minimum points for the 2nd 100% re-use cycle. Overall, the experimental work confirmed that the properties of polypropylene powder were affected by recycling in polymer laser sintering, but the powder exhibited superior characteristics upon recycling to those of the predominantly used PA 12 powder.

Extrusion printing processes allow for manufacturing complex shapes in a relatively cheap way with low-cost machines. The present study analyzes the effect of printing parameters on dimensional error, roughness, and porosity of printed PLA parts obtained with grid structure. Parts are obtained by means of the fused filament fabrication (FFF) process. Four variables are chosen: Layer height, temperature, speed, and flow rate. A two-level full factorial design with a central point is used to define the experimental tests. Dimensional error and porosity are measured with a profile projector, while roughness is measured with a contact roughness meter. Mathematical regression models are found for each response, and multi-objective optimization is carried out by means of the desirability function. Dimensional error and roughness depend mainly on layer height and flow rate, while porosity depends on layer height and printing speed. Multi-objective optimization shows that recommended values for the variables are layer height 0.05 mm, temperature 195 ºC, speed 50 mm/min, and flow rate 0.93, when dimensional error and roughness are to be minimized, and porosity requires a target value of 60%. The present study will help to select appropriate printing parameters for printing porous structures such as those found in prostheses, by means of extrusion processes.