Poly(phenylene methylene) (PPM) is a multifunctional polymer that is also active as an anticorrosion fluorescent coating material. Although this polymer was synthesized already more than 100 years ago, a versatile synthetic route to obtain soluble high molar mass polymers based on PPM has yet to be achieved. In this article, the influence of bifunctional bis-chloromethyl durene (BCMD) as a branching agent in the synthesis of PPM is reported. The progress of the reaction was followed by gel permeation chromatography (GPC) and NMR analysis. PPM-based copolymers with the highest molar mass reported so far for this class of materials (up to M n of 205,300 g mol -1 ) were isolated. The versatile approach of using BCMD was confirmed by employing different catalysts. Interestingly, thermal and optical characterization established that the branching process does not affect the thermoplastic behavior and the fluorescence of the material, thus opening up PPM-based compounds with high molar mass for applications.

Poly(phenylene methylene)s (PPMs) with high molar masses were isolated by polymerization of benzyl chloride catalyzed with tungsten(II) compounds and subsequent fractionation. Four different tungsten(II) catalysts were successfully exploited for the polymerization, for which a strict temperature profile was developed. The PPMs possessed roughly a trimodal molar mass distribution. Simple fractionation by phase separation of 2-butanone solutions allowed to effectively segregate the products primarily into PPM of low molar mass ( M n = 1600 g mol -1 ) and high molar mass ( M n = 167,900 g mol -1 ); the latter can be obtained in large quantities up to 50 g. The evolution of the trimodal distribution and the monomer conversion was monitored by gel permeation chromatography (GPC) and ¹H NMR spectroscopy, respectively, over the course of the polymerization. The results revealed that polymerization proceeded via a chain-growth mechanism. This study illustrates a new approach to synthesize PPM with hitherto unknown high molar masses which opens the possibility to explore new applications, e.g., for temperature-resistant coatings, fluorescent coatings, barrier materials or optical materials.