Search

In this study, we described the preparation of sponge-like porous scaffolds that are feasible for medical applications. A porous structure provides a good microenvironment for cell attachment and proliferation. In this study, a biocompatible PHA, poly(3-hydroxybutyrate-co-4-hydroxybutyrate) was blended with gelatine to improve the copolymer's hydrophilicity, while structural porosity was introduced into the scaffold via a combination of solvent casting and freeze-drying techniques. Scanning electron microscopy results revealed that the blended scaffolds exhibited higher porosity when the 4HB compositions of P(3HB

The microbond test of natural fibers tends to produce scattered interfacial shear stress (IFSS) values. The sources of this scattering are known, but the roles they play in producing high IFSS scattering remain to be investigated. In this study, a numerical method was used to simulate microbond testing and to examine the experimental parameters in a microbond test of

Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] is a bacterial derived biopolymer widely known for its unique physical and mechanical properties to be used in biomedical application. In this study, antimicrobial agent silver sulfadiazine (SSD) coat/collagen peptide coat-P(3HB-co-4HB) (SCCC) and SSD blend/collagen peptide coat-P(3HB-co-4HB) scaffolds (SBCC) were fabricated using a green salt leaching technique combined with freeze-drying. This was then followed by the incorporation of collagen peptides at various concentrations (2.5–12.5 wt.%) to P(3HB-co-4HB) using collagen-coating. As a result, two types of P(3HB-co-4HB) scaffolds were fabricated, including SCCC and SBCC scaffolds. The increasing concentrations of collagen peptides from 2.5 wt.% to 12.5 wt.% exhibited a decline in their porosity. The wettability and hydrophilicity increased as the concentration of collagen peptides in the scaffolds increased. In terms of the cytotoxic results, MTS assay demonstrated the L929 fibroblast scaffolds adhered well to the fabricated scaffolds. The 10 wt.% collagen peptides coated SCCC and SBCC scaffolds displayed highest cell proliferation rate. The antimicrobial analysis of the fabricated scaffolds exhibited 100% inhibition towards various pathogenic microorganisms. However, the SCCC scaffold exhibited 100% inhibition between 12 and 24 h, but the SBCC scaffolds with SSD impregnated in the scaffold had controlled release of the antimicrobial agent. Thus, this study will elucidate the surface interface-cell interactions of the SSD-P(3HB-co-4HB)-collagen peptide scaffolds and controlled release of SSD, antimicrobial agent.

The microbond test of natural fibers tends to produce scattered interfacial shear stress (IFSS) values. The sources of this scattering are known, but the roles they play in producing high IFSS scattering remain to be investigated. In this study, a numerical method was used to simulate microbond testing and to examine the experimental parameters in a microbond test of Typha angustifolia fiber/epoxy. Three parameters were considered: fiber diameter, fiber length embedded in the epoxy, and the distance between the vise and the specimen. The geometries were modeled and analyzed by ABAQUS software using its cohesive zone model features. There were two types of contact used in this analysis: tie constraint and surface-to-surface. The results showcased the roles of the following experimental parameters: a larger fiber diameter from a sample increased the IFSS value, a longer embedded length reduced the IFSS value, and a shorter vise–specimen distance increased the IFSS value. The IFSS scattering in the microbond test could have originated from the interaction between these parameters. Of the three parameters, only the vise–specimen distance was found to be able to be reasonably controlled. When the IFSS value was atypically large, fiber diameter and/or embedded length potentially drove the scattering. This study advises further compilation and classification of the role of each experimental parameter in modulating the IFSS value.