Nanocomposites of isotactic polypropylene with 1–5 wt.% of fibrillated PTFE (PP/T) were prepared, and their crystallization during cooling under elevated pressure, in a wide pressure range, up to 300 MPa, as well as the resulting structure, were examined. The crystallization peak temperatures of PP/T, especially with 3 and 5 wt.% of PTFE, exceeded by up to 13 °C those of neat PP. Moreover, a fine-grain structure was formed in PP/T in the entire pressure range, which proved the ability of the fibrillated PTFE to nucleate crystallization of PP in the γ-form under elevated pressure. This also resulted in a higher crystallinity level developed in the γ-domain, before the temperature range of the α-domain was reached during cooling. Hence, the γ-content increased in comparison to that in neat PP, under the pressure up to 200 MPa, especially under 50–100 MPa.

Ternary blends of polylactide (PLA, 90 wt.%) and poly(methyl methacrylate) (PMMA, 10 wt.%) with functionalized polysilsesquioxanes (LPSQ-R) were obtained by solution blending. R groups in LPSQ containing hydroxyethyl (LPSQ-OH), methylglycolic (LPSQ-COOMe) and pentafluorophenyl (LPSQ-F5) moieties of different chemical properties were designed to modify PLA blends with PMMA. The effect of the type of LPSQ-R and their content, 1–3 wt.%, on the structure of the blends was studied with scanning electron microscopy (SEM) combined with energy dispersive spectroscopy (SEM-EDS), dynamic mechanical thermal analysis (DMTA) and Raman spectroscopy. Differential scanning calorimetry (DSC) and tensile tests also showed various effects of LPSQ-R on the thermal and mechanical properties of the blends. Depth-sensing indentation was used to resolve spatially the micro- and nano-scale mechanical properties (hardness and elastic behaviour) of the blends. The results showed clearly that LPSQ-R modulate the structure and properties of the blends.

1,3:2,4-bis(3,4-dimethylbenzylidene)sorbitol (DMDBS) is highly effective in nucleation of the α- form of isotactic polypropylene (iPP). However, its role in high-pressure crystallization of iPP, facilitating the formation of the γ- polymorph, has not been explored. The present paper focuses on the influence of DMDBS on nucleation of high-pressure crystallization of iPP. iPP with 0.2–1.0 wt.% of the DMDBS was crystallized under elevated pressure, up to 300 MPa, in various thermal conditions, and then analyzed by PLM, WAXD, SEM, and DSC. During cooling, crystallization temperatures (Tc) were determined. It was found that under high-pressure DMDBS nucleated crystallization of iPP in the orthorhombic γ- form. As a consequence, Tc and the γ- form content increased for the nucleated iPP, while the size of polycrystalline aggregates decreased, although the effects depended on DMDBS content. The significant increase of Tc and the decrease of grain size under high pressure of 200–300 MPa required higher content of DMDBS than the nucleation of the α-form under lower pressure, possibly due to the effect of pressure on crystallization of DMDBS itself, which is a prerequisite for its nucleating activity.