Search

In this study, the influence of hybridization on the compression response of thermoplastic matrix-based composites under high strain rate loading was investigated. The intra-ply and inter-ply hybrid composites were manufactured with Kevlar/Basalt yarns as the reinforcements with Polypropylene as a matrix. Cylindrical composite specimens were laser cut from the flat compression moulded laminates. The composite specimens were loaded under high strain rate using split-Hopkinson pressure bar setup at strain rates ranging from 2815/s to 5481/s. The study revealed differences in the rate-dependent growth of peak stress, peak strain and toughness with the strain rate. Intra-ply hybrid composites with alternate weaving of Kevlar and basalt yarns exhibited highest peak stress as compared to the Inter-ply hybrid composites (alternate layers of Kevlar and basalt fabrics) and another intra-ply composite containing Kevlar in the warp and basalt in the weft direction. Whereas in inter-ply hybrid composite, with Kevlar as the loading face attained higher stress, while composite with Basalt as the loading face attained higher strain. SEM micrographs revealed that Kevlar on the loading face can bear the impact with lesser delamination as compared to the Basalt on the loading face. Damage studies revealed that Kevlar fiber surface loading results in higher stress as compared to basalt (brittle) surface loading with lower overall damage. • The influence of hybization on the high strain rate resposne of thermoplastic composites. • Intra-ply hybridization excels over inter-ply hybridization. • Placement and direction of yarns is crucial in intra-ply hybridization. • Higher areal density fabrics are replacable with hybrid fabrics of lower areal density. [ABSTRACT FROM AUTHOR]

The present study deals with the quasi-static and high strain rate characterization of Kevlar-129 based thermoplastic composites. Two different thermoplastic matrices, namely, Polypropylene (PP) and Polyetherimide (PEI) were used to manufacture composite laminates. Quasi-static compression tests were performed at strain rates of 0.041 s−1 and 0.045 s−1. High strain rate tests were performed using a split Hopkinson pressure bar apparatus within the strain rates ranging from 2548 s−1 to 4379 s−1. Stress-strain relations reveals the rate-sensitive behaviour of composites. Kevlar/PP (K-PP) showed higher peak stress under quasi-static loading as compared to the high strain rate test. Comparable peak stresses were revealed under quasi-static and high strain rate loading for Kevlar/PEI (K-PEI) composite. Also, high strain rate compression properties such as peak stress, peak strain and toughness of K-PP were 25%, 27% and 6% higher than that of the K-PEI composite. The failure mechanisms of both the composites were characterized through macroscopic and scanning electron microscopy. K-PP failed majorly due to matrix crush and fibre failure while K-PEI failed due to shear cracking. Damage study reveals that a single fibre based composite system can be tailored to act as an energy-absorbing or dissipating material system by varying the thermoplastic matrix materials. • Static and dynamic compressive properties of Kevlar reinforced high-performance polymers. • Kevlar/Polypropylene outperforms over Kevlar/Polyetherimide under both the quasi-static and high strain rate loads. • The quasi-static strength of Kevlar/Polypropylene is 25% higher than its high strain rate strength. • Polypropylene matrix results in ductile failure, while the Polyetherimide matrix results in brittle failure. [ABSTRACT FROM AUTHOR]