Search

Polymer blends based on plastic waste and natural biodegradable polymers is an interesting strategy in view of environmental and technical concerns. This article investigates the structure, thermal and physical properties of virgin and post‐industrial polymethyl methacrylate (PMMA) waste/pristine chitosan (Cs) bio‐blends. Waste PMMA was generated by an extrusion process for the manufacturing of sheets. The results of gel permeation chromatography analysis (GPC) show a slight decrease (about 8%) in the average molecular weight of PMMA after extrusion. Fourier transform infrared spectroscopy in attenuated total reflectance mode (FTIR‐ATR) spectra do not reveal changes in the chemical structure of post‐industrial PMMA/Cs blends compared to virgin PMMA/Cs samples, indicating that chain scission reactions are the dominant degradation mechanism of PMMA during processing. Dynamic mechanical analysis (DMA) results reveal a single glass transition temperature (Tg) for the blends, implying miscibility of the components. Post‐industrial PMMA/Cs samples exhibit slightly lower values of Tg compared to virgin PMMA/Cs blends. The post‐industrial PMMA waste slightly reduces nano‐mechanical properties and thermal stability of the blends relative to those from virgin PMMA. In contrast, it increases the water uptake of the bio‐blends compared with virgin PMMA. Highlights: Chain scission is the dominant degradation mechanism of PMMA during extrusion.Miscibility between the homopolymers within the blends.PMMA waste slightly reduced the nano‐mechanical properties of the bio‐blends.Post‐industrial PMMA waste increased the water uptake of the bio‐blends.Possibility of using post‐industrial PMMA waste by blending with chitosan. [ABSTRACT FROM AUTHOR]

Halloysite nanotubes (HNTs) were successfully incorporated as flame retardants in polyamide‐11 (PA11) after their modification with methyl phosphonic acid. Fourier transform infrared spectroscopy, thermal gravimetric analysis (TGA) and pyrolysis–gas chromatography–mass spectrometry were used to evidence the functionalization of the clay. Raw and modified HNTs were then incorporated by melt mixing in PA11 at 20 wt%. Compositions containing both ammonium polyphosphate (APP) and HNTs were also prepared. TGA and pyrolysis combustion flow calorimeter exhibited enhancement in thermal stability upon incorporation of both raw and modified halloysite nanotubes while APP causes degradation at lower temperature. Cone calorimeter data showed that modified halloysite acts by forming an insulating barrier during the combustion, which limits heat and mass transfers. Moreover, elemental analysis of sample residues after cone test evidenced that a part of the phosphorus of the modified halloysite was transferred to the gaseous phase. These results suggest the full potential of halloysite as fire retardant agent for polyamides. POLYM. ENG. SCI., 59:526–534, 2019. © 2018 Society of Plastics Engineers [ABSTRACT FROM AUTHOR]

Polyamide 11‐based bionanocomposites were prepared by melt compounding with 10 wt% clays of different chemistry and morphology. This included vermiculite nanoflakes obtained by consecutive thermal and ultrasonic exfoliation in both neat and organo‐modified form. The mechanical reinforcement‐ and flame‐retardant performance of the vermiculite clays were compared to organo‐modified montmorillonite (Cloisite 30B) and needle‐shaped sepiolite (Pangel S9). Electron microscope investigations revealed different structures and dispersion levels of the clay nanoparticles in the polymer matrix. Tensile tests showed that the addition of clays led to considerable improvements in Young's modulus without compromising the elongation at break. Compared to the neat polymer, all clays reduced the peak heat release rate and the smoke production rate in cone calorimeter testing. Surprisingly, the needle‐shaped sepiolite clay and the two vermiculites outperformed the montmorillonite organoclay in the fire testing even though it featured the highest degree of exfoliation in the polymer matrix. POLYM. ENG. SCI., 58:1746–1755, 2018. © 2017 Society of Plastics Engineers [ABSTRACT FROM AUTHOR]

Blends of poly(3-hydroxybutyrate- co-3-hydroxyvalerate) (PHBV) and polylactide (PLA) with different PHBV/PLA weight ratios (100/0, 75/25, 50/50, 25/75, 0/100) were prepared by melt compounding. To improve the miscibility between the two components of the blend, low amount of compatibilizing agent (5 wt%), obtained by grafting maleic anhydride onto PHBV, was used. When compared with the uncompatibilized blends, the compatibilizer presence induces a greater interfacial adhesion. The effect of Cloisite 30B (C30B) on the blend morphology and the blend properties was also investigated. The morphology of the different blends as well as the evolution of their material properties were discussed in terms of the nanoclay and compatibilizing agent contents. A synergistic effect of compatibilizer and C30B was highlighted leading to an improved miscibility of the two blend components. The resulting properties were correlated with the morphology observed for the different blends. POLYM. ENG. SCI., 54:2239-2251, 2014. © 2013 Society of Plastics Engineers [ABSTRACT FROM AUTHOR]