Dy 3+ and Sm 3+ doped Li 4 CaB 2 O 6 materials were prepared by the solid state reaction. The phase analysis of all phosphors were determined using the X- Ray Powder Diffraction Analysis. The photoluminescence (PL) properties of both phosphors were investigated using spectrofluorometer at room temperature. The first luminescent material, Li 4 CaB 2 O 6 : Dy 3+ emits 489, 577 and 674 nm upon excitation with 345 nm. The second luminescent material, Li 4 CaB 2 O 6 : Sm 3+ , emits (565–570), (602–609), 650 and 712 nm upon excitation with 404 nm. Also, the dependence of the emission intensity on the activator ions (Dy 3+ and Sm 3+ ) concentration for the Li 4 CaB 2 O 6 were studied in detail. It was observed that the concentration quenching of Dy 3+ and Sm 3+ in Li 4 CaB 2 O 6 are 0.05 and 0.06 mol, respectively. [ABSTRACT FROM AUTHOR]

MSr 4 (BO 3 ) 3 :Sm 3+ (M = Li, Na) materials were synthesized a solution combustion synthesis method followed by heating of the precursor combustion ash at 800 and 750 °C, respectively. The synthesized phosphors were characterized by using the powder XRD. The excitation and emission spectra of these materials were measured at room temperature with a spectrofluorometer. The photoluminescence properties of MSr 4 (BO 3 ) 3 :Sm 3+ (M = Li, Na) materials with different mol ratios of Sm 3+ were analyzed in detail. Both LiSr 4 (BO 3 ) 3 :Sm 3+ and NaSr 4 (BO 3 ) 3 :Sm 3+ phosphors emit a strong in orange–red region. It was observed that the optimum concentration of Sm 3+ in LiSr 4 (BO 3 ) 3 and NaSr 4 (BO 3 ) 3 are 0.04 and 0.03 mol, respectively. Finally, The relation between the photoluminescence properties of Sm 3+ and host compositions was discussed in detail. [ABSTRACT FROM AUTHOR]

Pure and Pb 2+ doped Ba 2 Be 2 B 2 O 7 materials were prepared by a solution combustion synthesis method. The phase analysis of all synthesized materials was carried out using the powder XRD. The synthesized phosphors were investigated using spectrofluorometer at room temperature. The excitation and emission bands of Ba 2 Be 2 B 2 O 7 :Pb 2+ were observed at 284 and 396 nm, respectively. The dependence of the emission intensity on the Pb 2+ concentration for the Ba 2 Be 2 B 2 O 7 was studied in detail. It was observed that the concentration quenching of Pb 2+ in Ba 2 Be 2 B 2 O 7 is 0.04 mol. The Stokes shifts of Ba 2 Be 2 B 2 O 7 :Pb 2+ phosphor were calculated to be 9959 cm −1 . [ABSTRACT FROM AUTHOR]

Pure and Pb 2+ doped Li 4 CaB 2 O 6 materials were prepared by the solid state reaction. The phase analysis of all synthesized materials were determined using the powder XRD. The synthesized materials were investigated using spectrofluorometer at room temperature. The excitation and emission bands of Li 4 CaB 2 O 6 :Pb 2+ were observed at 263 and 298 nm, respectively. The dependence of the emission intensity on the Pb 2+ concentration for the Li 4 CaB 2 O 6 were studied in detail. It was observed that the concentration quenching of Pb 2+ in Li 4 CaB 2 O 6 is 0.01 mol. The Stokes shifts of Li 4 CaB 2 O 6 :Pb 2+ phosphor was calculated to be 4466 cm −1 . Also, the photoluminescence properties of Pb 2+ in various lithium calcium borates (LCB) with different structure was discussed. [ABSTRACT FROM AUTHOR]