Search

Abstract: This article reports the effect of mixed alkalis on the optical absorption and emission spectra of Sm3+ and Dy3+ doped chloroborate glass matrices of the compositions 69.5B2O3 xLiCl(30− x)NaCl0.5R2O3 and 69.5B2O3 xLiCl(30− x)KCl0.5R2O3 (where R=Sm and Dy and x =5, 10, 15, 20 and 25). Using Judd–Ofelt theory, the spectral intensities and Judd–Ofelt intensity parameters (Ω 2, Ω 4 and Ω 6) were obtained from the measured absorption bands of the spectra. Using these intensity parameters, total radiative transition probabilities (A T), radiative lifetimes (τ R), branching ratios (β) and peak emission cross-sections (σ P) were obtained for the two rare earth ions in these two glass matrices. Variation of these parameters with x in the glass matrix has been discussed. It is found that for Sm3+ ion, the transition, 4G5/2 → 6H9/2 shows highest emission cross-section and is maximum at x =10mol% in lithium–sodium and at x =20mol% in lithium–potassium glass matrices. For Dy3+ ion, the transition, 4F9/2 → 6H13/2 shows highest emission cross-section and is maximum at x =20mol% in lithium–sodium and at x =10mol% in lithium–potassium glass matrix. [Copyright &y& Elsevier]

Multi-component phosphate glasses with various Nd 2 O 3 content have been prepared using conventional melt-quenching technique. X-ray diffraction was carried out to study the structure of the prepared samples and it was found that all the obtained samples are amorphous. Electrostatic F (2) , F (4) , F (6) , and spin–orbit parameters have been determined from the absorption spectra. Judd-Ofelt theory has been used to analyze and evaluate the radiative transition probability, branching ratio, and radiative lifetime for the metastable level 4 F 3/2. Luminescence spectra and experimental lifetimes give information regarding the absence of chemical clustering and suggest that the physical clustering is negligible making the glass a suitable candidate for photonic applications. Image 1 [ABSTRACT FROM AUTHOR]